Cast Stainless Steel

Hot Products

FAQ

Why do casting parts have air holes?
There are many reasons for casting porosity, mainly due to:1. smelting process is unreasonable, metal liquid absorbs more gas;2. the gas in the mold invades the metal liquid;3. from the mold is more water brush, core dry;4. the casting has poor ventilation;5. ladle tools are not dry.Wait。
Question, such as title, I hope I don't copy the definition of rolling and casting in Baidu encyclopedia, thank you
Service performance: heat conductivity, friction reduction, shock absorption, heat resistance and corrosion resistanceTo compare these properties, it depends on the specific material, structure, and use of the parts. Otherwise, there is no comparisonS
What is the difference between forging parts and casting parts?
No, it's called die castingDifference: the die casting parts are simple in structure and large in batch sizeCasting: the use of a wide range of structures without restrictions
How to cast iron and wrought iron collocation
2, listen: Pig beating sound boring, wrought iron beating sound loud.
The casting sand is going on
3, prevention measures(1) to improve the strength of sand mold (core), especially surface strength, high temperature strength, refractoriness, compact, better coating, good core coating and parting surface coating.(2) mould and box can prevent damage;(3) the core should have clearance.
What is the reason for 304 stainless steel precision casting parts to be changed?
Mainly because of the cooling shrinkage caused by internal stress caused. There is the change of temperature distribution in materials element imbalance, is typical of surface and internal, thin wall and thick wall, bottom and top.
How can the casting be quenched and tempered?
Another is the result of pre heat treatment (quenching or annealing) after quenching and tempering treatment, suitable for ZG35SiMNMo, ZG35CrMo and so on. Please tell the casting process is your product and material and then set tempered.: shutup:
I often see Waixiejiagong drawings, casting, how to distinguish the latheman.
What you say is the difference between rough drawing and processing drawingThere must be a difference between the rough drawings and the rough ones