Product Description:

General Information
CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

Feature
Low thermal conductivity   
Excellent acid and base slagging resistance
High refractoriness    
Excellent thermal shock resistance    
Excellent mechanical strength

Application
CMAX high alumina bricks are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc

 

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,%

1450x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h       0.1-0.4

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

Al2O3 Content , %

48

55

65

75

80

85

82

 

 

Composite Brick with Al2O3 content 85-90%

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What kind of material is good to be laid on the kiln car, refractory brick?
Use blankets to suspend ceiling, and modules for wall
Q:Small size black brick can replace refractory bricks for wood burning fireplace?
No. Because black brick has no fireproof function. The result of using the black brick can only be counterproductive, and which is also a waste of time and fuel.
Q:What are required for high temperature refractory bricks?
High temperature resistance, high pressure resistance
Q:What is the refractory brick in silicious model?
Adding appropriate amount of mineralized agent to promote the transformation of quartz in the body into phosphorus quartz. Smaller coefficient of thermal expansion. Also used in high temperature bearing part of hot blast stove and acid open hearth furnace, refractory materials and ceramic kiln, kiln vault and other load-bearing parts, thermal shock resistance variation. High temperature strength. the glass furnace is burnt in 1430 to 1350 degrees Celsius in the reducing atmosphere. use natural silica as raw materials. True density 2. more than 93% of silica content. generally there is no crystal type transformation above 600 degrees celsius. With acid slag erosion and sediment chamber regenerator performance, soaking furnace, open hearth furnace. there is more crystal type transformation below 600 degrees celsius. mainly used in coking chamer of coke oven and partition of firebox. acid refractory material made of high thermal shock resistance, large volume change, square quartz and a small amount of residual quartz and glass box . Long term use at high temperature without deformation
Q:What can be applied to the burned refractory brick to resist heat shock?
Acidic refractory material use monox as the main component, among which cilica brick and clay brick are commonly used. Silica brick is silicious product containing monox more than 93%, whose raw materials include silica, waste silica brick scrap and etc. The acid resistance of slag erosion ability is good, and the softening temperature under a fixed load is high. The volume won't shrink after repeated burning, but even a slight expand; but it is vulnerable to the erosion of basic slag, and has low thermal shock resistance. The silica brick is mainly used for coke oven, glass melting furnace, acid hearth furnace and other thermal equipments. Clay brick uses refractory clay as the main raw material, containing 30% to 46% of aluminuum oxide, belong to weakly acidic refractories. It has good heat shock resistance and corrosion stability to acid slag, and it's widely used. Neutral refractory materials use aluminum oxides, chromium hemitrioxides or carbons as the main components. Corundum products containing more than 95% of alumina is a kind of high quality refractory material with wide application.
Q:Which is best of refractory brick press machine?
Rub press machine have been forced out. Without permanent magnet. The electric screw press machine is suitable for the forming of refractory bricks. Use Kehui switch reluctance to servo motor to drive electric screw press machine, have the ability of high quality electric screw press machine, no water cooling, high efficiency and energy saving, green and environmental protection.
Q:What raw materials are used for refractory bricks
Phenolic resin, clay, powder and other materials, nitride materail, boron carbide, silicon carbide, silica raw material three, soil: fluorite, magnesia-alumina spinel Aluminum soil, calcium aluminate cement, corundum, andalusite, chlorite, silica solution, which is mainly divided into six categories, sillimanite, vermiculite refractory bricks raw material composition of refractory brick, there are many raw material kinds of refractory bricks, mullite, mine: Soil, Sialon, forsterite, pyrophyllite: Metal aluminium powder, ore, stone: Pottery, zircon sand, quinidine sulfate, dolomite, kaolin: The fifth raw material of chrome ore, sodium silicate, diatomaceous earth is the second raw material: Asphalt, sand, shale ceramisite. One of the raw materials, stone powder, the fourth raw material is magnesite, the sixth raw material is silicon metal powder refractory bricks, sand, kyanite, silica powder, aluminium oxide, aluminum sol, quartz sand, perlite, cenosphere, graphite
Q:How to adjust the temperature in the 160 meter tunnel kiln?
Tunnel kiln can be attemperated by burning products, this will not affect the firing of different products, and can burn back processing products.
Q:Can thick steel plate be used instead of the furnace inside the refractory brick?
It depends on the temperature. The steel plate is a kind of heat conduction material which hasn't heat insulation, which should be based on the working environment.
Q:What's the reason of cracks in refractory bricks?
This is inorganic nonmetallic material

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range