Fireclay Brick Alumina Conten from 36% to 48%

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
1 m.t.
Supply Capability:
20000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Description of fireclay bricks

CMAX fireclay bricks are made from clinker clay. The alumina content ranges from 36% to 48%.

 

Features of fireclay bricks

Low thermal conductivity       
High refractoriness  
High mechanical strength      
Excellent thermal shock resistance

 

Applications of fireclay bricks

CMAX fireclay bricks are commonly applied in blast furnace, hot blast furnace, teeming ladle, glass furnace, etc.

Specifications of Insulating Firebricks

 

 

fireclay bricks

NG-0.5

NG-0. 6

NG-0. 8

NG-1.0

NG-1.3

NG-1.5

USA Brand

ISO125-0.5

ISO125-0.6

ISO135-0.8

ISO135-1.0

ISO140-1.2

ISO140-1.5

Max Service Temperature (°C)

1150

1200

1280

1300

1350

1400

Bulk Density (g/cm3)

0.55

0.6

0.8

1.0

1.3

1.5

Apparent Porosity %

80

70

60

55

50

40

Cold Crushing Strength

 (Mpa) ≥

1.5

2.0

2.5

3.0

4.0

6.0

Reheating Linear Change (%)   °CX 12H ≤

1250°C

-0.5

1300°C

-0.5

1350°C 

-0.5

1350°C

-0.9

1350°C

-0.9

1350°C

-0.9

Thermal conductivity(W/m.k) 

400°C

0.14

0.25

0.35

0.41

0.51

0.6

600°C

0.16

0.29

0.45

0.43

0.61

0.71

800°C

0.18

0.31

0.50

0.44

0.67

0.77

1000°C

0.20

0.33

0.60

0.45

0.8

0.9

Al2O3 (%)

37

40

40

40

40

42

Fe2O3 (%)

1.0

1.5

1.5

1.5

2

2

SiO2

44

55

55

55

55

55

 

  

Images of fireclay bricks

 

 

Fireclay Brick Alumina Conten from 36% to 48%

Fireclay Brick Alumina Conten from 36% to 48%

Fireclay Brick Alumina Conten from 36% to 48%

Fireclay Brick Alumina Conten from 36% to 48%

 

FAQ of fireclay bricks

 

1. Which products do you have?

We have all kinds of refractory brick, castable, mortar, cement, ceramic fiber products, etc.
Or you could browse our products to choose what you need.

 

 

2. Can you give me a general idea of the specification and technical data of your products?

CNBM offer a range of refractory and insulation products. We provide refractory bricks, monolithic refractories as well as ceramic fiber products. And On your given shapes, drawings or description, we are producing refractories with all sizes and shapes, resistant to temperature from 800 °C till 1800 °C, using various machines and equipments for cutting, grinding, drilling, polishing, shaping processes.
Every refractory product by CNBM is of superior quality. Lesser refractory products can not approach. CNBM utilizes proprietary testing methods, testing for chemical content, density, apparent porosity, cold crush strength and modulus of rapture. With stringent quality control, you can count on CNBM products to exceed refractory industry standards and your expectations.

 

3. Can you give me a brief introduction of the application of your products?

We are mainly specializing in the refractory materials in iron and steel, cement, glass, ceramics, petrochemical, electric power Industry, etc.

 

4. If I need your offer, what information do you need?

In order to choose suitable products, it will be appreciated to provide us the information, such us specification, technical data, order quantity, products application etc.
If any question, please contact us freely.

 

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:is it good to use firebricks to preserve the heat of rto furnace? Is there any other good ideas?
1. what variety and grade of refractory materials should be chosen to build all parts of the industrial furnace?; 2. is the origin of these materials be assured? mesothern resistance furnace, lightweight refractory brick, refractory fiber, bead brick of 1000 degrees; fuel heating furnace, refractory clay brick, high alumina brick, silica brick, carborundum brick, refractory castable, the plastic refractory of 1300 degrees; heat treatment furnace, refractory clay brick, refractory fiber of 1100 degrees; high temperature salt bath furnace, refractory clay brick, high alumina brick, zircon brick, refractory castable of 1300 degrees; high temperature resistance furnace, lightweight refractory brick, high aluminum bricks, lightweight alumina brick, lightweight refractory clay brick of 1400 degrees; molybdenum wire furnace, alumina brick, corundum brick, carborundum brick, finished alumina hollow ball product of 1650 degrees; cupola, refractory clay brick, carborundum brick, dolomite Brick, carbon brick, graphite brick of 1650 degrees; arc furnac, high alumina brick, silica brick, magnesia brick, magnesia brick, magnesia chrome... Corundum brick, carbon brick, magnesia chrome brick, magnesia brick, high aluminum brick, silica brick, finished alumina hollow ball product of 1700 degrees; cupola, refractory clay brick of 1650 degrees;
Q:What is the name of the white clay refractory brick
There are several kinds of white clay, Guangxi clay, Suzhou clay, kaolin
Q:How much is the silica powder in refractory bricks.
It's not easy to construct, also need to consider the technical and economic indexes, DH3, 1 kg silica powder replaces 1 ~ 3 kg cement, which is the reason why silicon powder was not used and spreaded in concrete in past, choose some silica power fume. In general, with the smoke escaping by special capture device for collecting and processing To determine the mixing method of silica powder, when mixing silica powder, you should find out the optimal dosage in order to obtain the best results, as the study, the content is 5% ~ 30%, H, the mixing of super high strength concrete, use same amount of silicon powder to replace equal cement to main same fluidity, Microsilica or Silica Fume, it is mainly according to the design requirements, and does not reduce the amount of cement, sand and stone to adjust the optimal dosage of water reducer, when deciding the best mixing amount of silica fume, the concrete is too sticky, most use naphthalene water reducing agent.
Q:What is the raw material for the production of refractory bricks?
Refractory raw material, sodium silicate as a binder, and lightweight aggregate, magnesium sand, magnesia calcium. Magnesium Oxide, bauxite, and then lightly burn: Hard refractory clinker
Q:What are the factors that determine the weight of the refractory bricks?
(5) Under high temperature, the volume is stable, the inner part of brick will produce unrecoverable volume shrinkage or expansion because of the internal transformation. Therefore, masonry inner will produce stress to make the material break and peel off, and the weight of a ton of bricks is determined by the bulk density and quantity, how much is the weight of refractory bricks, refractory bricks should have the ability to resist the damage, the weight of a piece of brick is determined by the bulk density: Refractory bricks are used under high temperature for a long term: Refractory bricks in the use of the process. Cooltech refractory brick used in various high-temperature equipment: The temperature of some parts of metallurgical furnace and other industrial furnace is uneven due to rapid temperature change during operation. (3) good thermal stability: Refractory bricks should not only have a high fusion temperature, no softening deformation and collapse, causing damage to the masonry. (4) strong resistance to slag: Modern metallurgy and the other industrial furnace heating temperature is generally between l000~1800. Refractory bricks should have the performance that is not easy to melt under high temperature. Therefore. Therefore, it is subject to high temperature conditions of physical and chemical corrosion and mechanical damage, the refractory brick must have the ability to resist high temperature chemical corrosion, the volume of refractory brick is required to be stable under high temperature. (2) High-temperature structural strength, chemical corrosion of metal, but also should have been built in the stove brickwork load or other mechanical vibration, often has the high temperature slag, so the refractory materials performance should meet the following requirements: (1) high refractoriness
Q:Can refractory bricks be used to pave roads or build a wall?
Complete refractory brick has standard size and it is heavier than ordinary red brick. the volume ratio is shrinking with change of temperature to crack and strength of brick with brick walls down enough for new
Q:What bricks are used for constructting refractory bricks tunnel kiln what is the material of each burning zone brick
Exterior wall uses red brick, preheating zone uses lightweight high aluminum bricks, burning zone uses mullite, cooling zone uses ordinary refractory bricks
Q:is there any requirement for radioactive materials in refractory materials.
they all do not cause radiological hazards to the environment, so no requirements! analyze rom the element , magnesia. Do not know if it is useful, but material used by refractory materials, firstly any chemical elements are radioactive, human beings can not close, then, such as silicon dioxide: If it is radioactive. analyze from use, such as bauxite, does not have the use value
Q:Why are the refractory bricks near to rotary kiln tyre easy to be short lives?
Q:Classification of refractory bricks

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range