Stainless Steel Mig Wire

Hot Products

15Kgs/Spool ER70S-6 Solid Mig welding Wire Rissian Standard sv08g2s

Mig Welding Wire ER70S-6

Welding Wire AWS 5.18 ER70S-6 Copper Coated High Quality

Factory Supply Mig co2 Welding Wire AWS ER70s-6

MIG Welding Wire ER70S-6/DIN SG2/BS A5.18 High Quality Factory

Welding Wire Factory Hot Selling ER70S-6 Co2 Welding Wire Manufacturer

High End Solid MIG Welding Wire ER70S-6 Factory Competitive Price

Mild Steel Welding Rod AWS E6013 Weding Rods Factory

Welding Wire with AWS A5.18 ER 70S-6 Welding Wire High Quality

AWS ER 70S-6 Welded Wire AWS A5.18 ER 70S-6 0.8mm/0.9mm/1.0mm

FAQ

What are the welding metallurgical characteristics of flux cored wire?

I suggest you go to see the welding metallurgy

The difference between Jinqiao welding wire 50-6 and 70S-6

Similarly, ER70S-6 is the American Standard, 70 of which means tensile strength, expressed in PSI, while 50S-6 is the domestic standard, and 50 represents tensile strength, expressed in MPA.

Argon arc welding how to continuously feed wire, the head of the welding wire will not sway.

Isn't there an automatic wire feed?

2.4, arc welding of stainless steel wire 308 and 308L difference between large? Can I change it between you and me?!

308 and 308L wire, in theory, the strength of 308L is slightly lower. But the actual test is not low. Simple structural connections can be interchanged. The difference between 308 and 308L is the amount of carbon contained. The rest are the same. The carbon content of 308L is less than 0.03.308, and the content of carbon is less than 0.08.308L can instead of 308, but not recommended (special weld not allowed)

What is the relation between Jing Lei welding wire and Beijing group welding wire?

One family. Beijing group is the name of the company, Jing Lei Shijing group company product trademarks.

Is the ER50-6 good solder wire?

Still can burn, still very tired, solid, again to see what people use

What kind of welding wire is used for 310S stainless steel plate?

310S stainless steel plates shall be welded with ER-310 wire or A132 and 137 electrodes.ER310 stainless steel welding wire, molten gold containing 25Cr-20Ni, used for welding 310S stainless steel, suitable for welding of dissimilar metals and welding of alloy steel and high carbon steel.A132 welding electrodes are used to weld important corrosion resistant, Ti stabilized 0Cr19Ni10Ti stainless steels.A137 is an Cr19Ni10Nb stainless steel electrode with an alkaline coating and a low carbon content containing Nb stabilizer. It is used for welding important corrosion resistant Ti stabilized stainless steel 0Cr19Ni11Ti.310S stainless steel is austenitic chromium nickel stainless steel, with good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance. Mainly used in petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries.

What is the difference between ER70-G welding wire and ER100S-G welding wire?

Generally there are three kinds of welding wire:(1) MGS-70 ER100S-G is used for welding 690Mpa high strength steel(two) MG-80 ER110S-G is used for welding 780Mpa high strength steel(three) MGS-88A ER120S-G is used for welding 780Mpa grade high strength steel at low temperatureMG70-G conforms to GB ER70-G, equivalent to AWS ER100S-G1. note: JQ.MG70-G is NiMo type 700MPa high toughness low alloy steel gas shielded welding wire, with good welding performance in all position. Arc stable, small splash.2. uses: suitable for welding 700MPa grade high strength steel structure, such as construction machinery, lifting machinery, bridges, pipelines, ships and pressure vessels and other structures welding.3. wire chemical composition (%):C = 0.10, Mn1.40~1.80, Si 0.50~0.80, S = 0.025, P = 0.025, Cu = 0.50, Ni1.20~1.60, Mo0.30~0.60, Cr, 0.15~0.25, Ti = 0.10.