Gas Shielded Welding Wire ER70S-6 from China

Gas Shielded Welding Wire ER70S-6 from China

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t.

Supply Capability:: 10000000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

1.Detailed introduction to Gas shielded welding wire ER70S-6:

General Description: the welding wires has the characteristics of excellent technical performance,fast melting speed, high efficient fusion, stable electric arc, less welding splash,favorable wetness performance,average & beautiful welding seam,good anti-oxygenic & anti-corrasive property, less sensitive to the atmosphere holes. It can be shielded by means of DC(±), CO2 or the combination of Ar+CO2 5-10%. Easy to operate and is suitable for the automatic and semi-automatic omnibearing welding. Applications: Mainly used in welding of carban steel, low alloy steel & 500MPa grade low alloy high intensity steel,Widely used in vehicle, building, bridge, shipbuilding & pressure vessel industry,it can also be used in the high speed welding of thin stell plate and pipeline.

2.Features of Gas shielded welding wire ER70S-6:

CO2 Gas-sheilded welding wires have excellent mechanical performance such as fast depositing speed,high depositing effciency,stable arc,little splash,good welding seam.
suitale for all-position welding work.
widely used to welding low carbon steel and low alloy steel structure,such as ships,vehicles,bridges,boils and buildings etc

3.Photo of Gas shielded welding wire ER70S-6:

4.Chemical Composition of Welding Wire (%):

C	Mn	Si	S	P	Ni	Cr
≤0.10	0.3~0.55	≤0.03	≤0.030	≤0.030	≤0.30	≤0.20

Examples of Chemical Composition of Deposited Metal (%)

C	Mn	Si	S	P	Ni	Cr
0.060	0.45	0.012	0.014	0.020	0.022	0.017

Mechanical Properties of Deposited Metal

Test Items	Rm	ReL/Rp0.2	A	KV2(J)
Flux Used Together	(Mpa)	(Mpa)	(%)	0°C	-20°C
SJ301	415-550	≥330	≥22	—	≥27
HJ431	415-550	≥330	≥22	≥27	—

5.FAQ

We have organized several common questions for our clients，may help you sincerely：

①How about your Warranty？

Warranty: 1Year for the whole light. Warranty is based on correct storage, installation, using and maintenanc

②How to guarantee the quality of the products？

We have established the international advanced quality management system，every link from raw material to final product we have strict quality test；We resolutely put an end to unqualified products flowing into the market. At the same time, we will provide necessary follow-up service assurance.

③How long can we receive the product after purchase?

In the purchase of product within three working days, We will arrange the factory delivery as soon as possible. The pecific time of receiving is related to the state and position of customers.Commonly 7 to 10 working days can be served.

Q: What kind of steel bars are used for the two electrodes?: Their strength is different, J422 is 42 kg class, J502 is 50 kg class, steel model I don't understand. J502 welding thread steel is appropriate.

Q: 3.2 how much is a package of bridge electrode: This depends on what kind of electrode, such as J422 welding rod, 3.2mm package is five kg, the price is about twenty yuan. If it is J507 electrode and so on, the price will be higher, such as A132 and other stainless steel prices will be much higher.The electrode (coveredelectrode), is the metal coating in the welding core (coating), uniform centripetal pressure applied to core. The core metal cored electrode, in order to ensure the quality and performance of the weld, there are strict rules on the contents of metal elements in the core, especially for harmful impurities (such as sulfur, phosphorus content, etc.) should be strictly restricted, better than the base metal. The electrode consists of two cores and coating composition. The different cores are also different. The core components directly affect the composition and properties of the weld metal, so the harmful elements in the welding core to as little as possible.For welding of carbon steel and low alloy steel welding core, are mostly made of low carbon steel as the core, and adding manganese, silicon, chromium, nickel and other components (see wire national standard GB1300 - 77). The reason of low carbon is a low carbon steel wire plastic, wire drawing is relatively easy, on the other hand can reduce the CO content of reducing gas, reduce spatter or porosity and increased weld metal solidification temperature, favorable for overhead welding. The addition of other alloy elements mainly guarantees the comprehensive mechanical properties of the weld, and also has some effect on the welding process performance and the removal of impurities.

Q: How do you know it's a white steel electrode?: White steel electrode, stainless steel electrode is generally refers to many kinds of stainless steel, such as 30403-30408, 32310S, 31603, 31608, 1CR13 and so on, using different types of electrode, stainless steel electrode used in general are: 102, 022, 132, 042, 002, 132 different types of.

Q: Does the welding rod have a shelf life?: Welding rod has shelf life,The quality index of storage time exceeds a certain time limit, changes in different degree of quality (metamorphic). Various types of electrodes are stored for a long time, and sometimes white crystals are found on the surface of the electrode. This is usually caused by water glass. Packing should be improved to prevent moisture absorption of welding rod and must be properly kept in storage. All kinds of welding rod are seriously deteriorated, and the batch of medicine is seriously falling off. The welding rod should be scrapped.

Q: What is the J422 electrode core material: The J421Z electrode is composed of two parts, core and coating composition. The electrode is coating in metal welding core (coating), uniform centripetal pressure applied to core.The electrode of different types, different cores. The core metal cored electrode, in order to ensure the quality and performance of the weld, there are strict rules on the contents of metal elements in the core, especially for harmful impurities (such as sulfur, phosphorus content, etc.) should be strictly restricted, better than the base metal. The core components directly affect the composition and properties of the weld metal, so the harmful elements in the welding core to as little as possible. For welding of carbon steel and low alloy steel welding core, are mostly made of low carbon steel as the core, and adding manganese, silicon, chromium, nickel and other components (see wire national standard GB1300 - 77). The reason of low carbon is a low carbon steel wire plastic, wire drawing is relatively easy, on the other hand can reduce the CO content of reducing gas, reduce spatter or porosity and increased weld metal solidification temperature, favorable for overhead welding. The addition of other alloy elements mainly guarantees the comprehensive mechanical properties of the weld, and also has some effect on the welding process performance and the removal of impurities.

Q: Method for using welding rod heat preservation barrel: Put in the electrode and plug into the power supply,Reach a certain time

Q: J422 electrodes are marked with "THJ422". What does TH represent?: J422 is the brand of welding rod GB. As for the TH is the enterprise stipulated grades, the first letter T should be on behalf of the welding electrode (strip of the first letter); second letters H, should be related to the electrode trademark or manufacturer's name.

Q: What are the technological parameters of E5015 welding rod?: Answer: is the ordinary alkaline welding rod, welding, welding rod connected to the positive electrode, the workpiece connected to the negative electrode. Different electrode diameter, welding current is not the same. This is marked on the package of the electrode!

Q: Can 50Mn2 casting be welded with 507 electrodes?: 50Mn2 is medium carbon steel, while J507 electrode is a low carbon component. If 507 electrodes are used to weld, the carbon content of the weld seam is lower, which will reduce the joint strength. Therefore, the welding of 50Mn2 steel with J507 welding rod can not guarantee the strength of the weld seam. It only applies to the welding of the weld when the strength of the joint is not high.

Q: What are the functions of E506 structural steel welding rod, which material is suitable for processing?: You say E506 structural steel welding rod, the correct welding rod brand should be written in E5016 or J506, the former model, and the latter is the brand.E5016 welding rod is a kind of alkali and direct current welding electrode. It is mainly used for basic welding rod which is not used by DC welding machine and welding with AC welder. The material used is the same as J507, and is used for 16Mn (Q345) grade steel.When welding the electrode, the process performance is worse than that of the acid welding rod, that is, spatter is bigger and weld formation is poor. But the metallurgical properties are better, that is, the anti - parathion of welding rod is harmful, and the welding seam has strong anti - crack ability, so it is used in welding of important welding seam. However, this kind of electrode tends to be larger than the direct current alkaline electrode (E5015 or J507), so it is seldom used in welding seams (e.g. pressure vessels) that require inspection.

Send your message to us

*Email

*TEL

*Quantity

*Unit