Product Description:



1 % Silver Brazing Rod

 

Brazing Rings are the cleanest and brightest, free of oxide and surfaceimpurities.  

 

Ag%

P%

Cu%

Solidus

Flow Point

Liquidus

AWS A5.8

1

6

Balance

1190º F

1325º F

1495º F

---

2

7

Balance

1190º F

1300º F

1450º F

BCup-6

2

6.5

Balance

1190º F

1350º F

1460º F

---

5

6

Balance

1190º F

1325º F

1495º F

BCup-3

5

6.75

Balance

1190º F

1300º F

1420º F

BCup-7

6

6

Balance

1190º F

1325º F

1480º F

---

6

7.25

Balance

1190º F

1275º F

1325º F

BCup-4

15

5

Balance

1190º F

1300º F

1475º F

BCup-5

18

6.25

Balance

1190º F

1220º F

1220º F

---

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is the J422 electrode core material
The J421Z electrode is composed of two parts, core and coating composition. The electrode is coating in metal welding core (coating), uniform centripetal pressure applied to core.The electrode of different types, different cores. The core metal cored electrode, in order to ensure the quality and performance of the weld, there are strict rules on the contents of metal elements in the core, especially for harmful impurities (such as sulfur, phosphorus content, etc.) should be strictly restricted, better than the base metal. The core components directly affect the composition and properties of the weld metal, so the harmful elements in the welding core to as little as possible. For welding of carbon steel and low alloy steel welding core, are mostly made of low carbon steel as the core, and adding manganese, silicon, chromium, nickel and other components (see wire national standard GB1300 - 77). The reason of low carbon is a low carbon steel wire plastic, wire drawing is relatively easy, on the other hand can reduce the CO content of reducing gas, reduce spatter or porosity and increased weld metal solidification temperature, favorable for overhead welding. The addition of other alloy elements mainly guarantees the comprehensive mechanical properties of the weld, and also has some effect on the welding process performance and the removal of impurities.
Q:What kind of welding rod is used for No. 55 steel?
To choose J506 or J507 welding rod, preheat 150~200 degrees before welding, heat preservation after welding. Or choose the electrode with higher strength grade
Q:Why stainless steel electrode is relatively short?
The reason is that the stainless steel electrode relative to the general structure of the electrode, the resistance is relatively large, if it is too long, lead to resistance heat is too large, welding electrode to the final red too much, the performance can not be guaranteed!
Q:What kind of welding rod is used for Q345R steel plate welding?
Vessel steel, with wide application range of J506R (E5016) welding, the weather is not good now, less than 15 degrees should pay attention to insulation, preheating, don't let the weld cold air humidity is greater than 70% or no end of trouble for the future, is to do the drying (electrode, weld must be cleaned before welding, final note)
Q:Is it possible to use an AC welder for 506 electrodes?
AC and DC can be, a large current bar on the line
Q:What is the welding process of duplex stainless steel 2507? What electrode?
standardAWS 5.4, E2594CharacteristicThe 2507 electrode /P100 high alloy dual phase steel welding, SAF2205 welding, ASTM S32750, ASTM S32760 dual phase steel, 2507 electrode /P100 heat input is lower than 2205, the permeability and fluidity of welding (considered relatively ordinary austenitic stainless steel welding). Avoid rapid and repeated quenching to form excessive ferrite or crystalline phase.Typical values of deposited metal (%)C, Si, Mn, Cr, Ni, Mo, N0.03, 0.5, 1.3, 25.5, 10.1, 3.6, 0.23Typical values of mechanical properties of deposited metalPerformance typical value minimumYield strength RP0.2, 695N/mm2, 550N/mm2Tensile strength RM, 895N/mm2, 6320/mm2Elongation rate A5 27% 25%
Q:Does the welding rod have a shelf life?
Must have ah, Pro is generally two or three years, but save the good words, do not let him wet, you can put many years of welding rod, afraid of moisture, and what problems can ask me again
Q:What kind of welding rod is Mt -12?
MT-12 is J421 (E4313) - type carbon steel welding rod.Carbon steel electrode (its tensile strength of deposited metal is less than or equal to 500MPa or 50kgf/mm2), suitable for welding carbon steel and low strength low alloy steel.The electrode of low hydrogen type, powder type, welding electrode must be baked above 350 DEG C, as far as possible to do with baking with, how much the drying principle, otherwise it will result in welding defects (such as porosity, cracks, slag, clamping process performance deterioration etc.). The cellulose type welding rod should be baked strictly according to the baking temperature stipulated in the instruction. When the temperature is too high, the cellulose in the coating will be burned and the inherent technological property of the welding rod will be destroyed.When using the low hydrogen electrode, the welder shall be in the upper wind position, strengthen the exhaust air, and prevent the welding fume from damaging the body.For the low hydrogen type welding rod, the number of baking can be less than two times as much as possible, so as to prevent the medicine skin from becoming brittle and falling off.
Q:What welding rod should be used for welding between No. 20 and No. 45 steel?
J427When welding, pay attention to the small current at the bottom, and the weldability of No. 45 steel is poor
Q:What kind of welding rod does aluminum alloy use?
Specific to see what aluminum alloy, different aluminum alloy may use different welding rod.Turn left and turn right |Turn left and turn right |Turn left and turn right |Aluminum and Aluminum Alloy wire can be used for welding processing spool or longitudinal incision of MIG or TIG, according to its composition can be divided into pure aluminum, aluminum silicon and aluminum magnesium wire into a disc through certain processing methods (coils) or rod (bar) supply, widely used in construction, decoration and equipment, metallurgy and spinning apparatus, pipelines, ships, drilling equipment, train, car, storage tanks and pressure vessels welding processing industry and other industries. Precautions for product use:1, the package after the warranty period you can directly connect the welding, welding without any pretreatment. The product can be stored for more than two years under the condition of packing and sealed. After packing, it can be guaranteed for three months in the normal atmospheric environment;2, the product should be placed on ventilation, dry and with acid and alkali, oil and other local storage medium isolation;3, the product should avoid bumping and damp during transportation, in order to avoid damaging the wire tray and affecting the quality of wire;4, after the wire is removed and packed, it is recommended to apply proper dust cover over the welding wire;5. The wire surface cleaning is recommended before welding;6, welding process of the arc will stimulate your eyes, please pay attention to protection.
Our main products are made in accordance with state and industry standards as well as being able to meet our customers' requirements. We have a certified quality management system that meets with ISO9001:2000 approval, which we gained in 2002. We believe in placing equal emphasis on quality, the end user and on the building of our reputation, and have personnel who are ready to do to their utmost to provide you with the best products and service.

1. Manufacturer Overview

Location Zhejiang, China
Year Established 2001
Annual Output Value US$50 Million - US$100 Million
Main Markets North America 0.24%
South America 0.16%
Southeast Asia 3.15%
Africa 0.08%
Oceania 0.79%
Mid East 0.08%
Western Europe 1.58%
Northern Europe 1.34%
Southern Europe 0.40%
South Asia 0.08%
Domestic Market 92.10%
Company Certifications ISO 9001:2000 ;ISO 14001:2004

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port Ningbo,Shanghai
Export Percentage 31% - 40%
No.of Employees in Trade Department 6-10 People
Language Spoken: English, Chinese, Japanese, German
b)Factory Information  
Factory Size: 10,000-30,000 square meters
No. of Production Lines 5
Contract Manufacturing OEM Service Offered Design Service Offered Buyer Label Offered
Product Price Range Low and/or Average