​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
1 m.t.
Supply Capability:
1044 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

High Alumina High Strength for Glass Kiln Thermal Insulating Brick

Product Description


The phosphate bonded high aluminum bricks are with high strength, low bulk density, low thermal, conductivity, high thermal shock resistance and the anti-spalling is good. Widely used in cement kiln,hot blast stove/furnace,EAF(electric arc furnace),coke oven door...

Structure& Advantage

for Our High Aluminum/Alumina Refractory Brick, Fireclay Bricks

1)    Good thermal shock resistance 

2)    High-temperature endurable 

3)    Good thermal insulation 

4)    The using temperature is 1600 c

5)    Phosphate high alumina bricks,iso

6)    High strength

7)    Low thermal conductivity

8)    Widely used in cement kiln.

9)    Low creeping rate

10)  High pressure

11)  Excellent thermal shock resistance

12)  High quality fireclay clinker

We Are Suppiler for

Below are some of our customers

 Allied Mineral Products,inc

Refractories Incorporated

Srs Sorg Refractory Systems GmbH,

Sunward Refractories Co.,Ltd

Lilama69-1 Joint Stock Company etc.

Major Images

Refractory High Alumium and Fireclay Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

​High Alumina High Strength for Glass Kiln Thermal Insulating Brick

Specification for High Aluminum Refractory Brick  

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,%

1450x2h           

  0.1~-0.4

1500x2h             0.1~-0.4

1500x2h             0.1~-0.4

1500x2h       0.1~-0.4

1550x2h             -0.5~+0.5

1550x2h             -0.5~+0.5

1550x2h             -0.5~+0.5

Al2O3 Content , %

48

55

65

75

80

85

82







FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories, at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time, seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:After an order is confirmed, when to deliver?

A:15-25days after deposit.

Q6:Is your company accept customization?

A:We have own factory and excellent technical team,and we accept OEM service.

Q7:How about your company's certification?

A:ISO9001 and Test Report,also we could apply other necessary certification.

Q8:How to slove the quality problems?

A:If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.

Q9:Can you offers samples?

A:Of coures,samples are free but freight paid by the buyers.

Q10:What is the service life of your bricks?

A:The service life of different bricks is unlike.It also depends on your using condition and method.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How high can aluminum bricks expand at 80O degrees of heat?
When an object is heated, the particle moves faster and thus occupies additional space. This phenomenon is called dilation.
Q:Aluminum content 38. silicon content 55 What refractory bricks?
High alumina brick:The mineral composition of the high alumina brick is determined by the bauxite used. The mineral composition of the clinker is usually mullite, corundum and glass. The theoretical composition of mullite is Al2O371.8%, SiO2 28.2%, and its melting decomposition temperature is 1840 DEG C. With acicular crystal, network cross structure, high temperature state showed better strength. Corundum in the form of alpha -Al2O3, melting point of 2050 degrees, hardness of Mohs 9, showing a granular and columnar crystal, has good chemical stability, acid, alkaline slag have a certain resistance. Based on the composition of mullite minerals, the phase composition of high alumina brick can be judged according to the content of Al2O3. When the bricks are below Al2O3 71.8%, the base of the composition is mullite and SiO2, such as grade LZ-48 bricks. Because it contains a large number of SiO2 formed in the liquid phase under high temperature is 20% ~ 30%; brick in Al2O3 more than 71.8%, the excess Al2O3 formed corundum crystal under high temperature, while generating 2 high temperature phase, eutectic temperature rise by the low content of Al2O3 brick 1595 C to 1840 C, such as grade LZ-75 brick. In fact, it is impossible to produce a complete phase equilibrium in the process of production, but the glass phase is very small, and there is no more than 10% in the partial gap of the Yu Jing phase
Q:What is the difference between fireclay bricks and high alumina refractory bricks?
High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3.
Q:The cloth blowing is not uniform on the lime kiln refractory brick is damaged it
Lining 1 yuan to prevent direct damage to the Sindh kiln high temperature flame or air, to protect the kiln carcass; 2, to prevent harmful substances (CO, SO2) erosion of the kiln body; 3, to prevent corrosion, material flow on the kiln body; 4, reduce the kiln temperature, kiln body to prevent oxidation 5, has the function of corrosion; thermal insulation; 6, to improve the coating performance.
Q:How to reduce porosity of high alumina brick
In order to reduce the porosity of high alumina brick, the corresponding measures should be taken from the selection of raw materials, batching, mixing, molding and firing.The water absorption rate of the first grade high alumina bauxite clinker should be less than 5%, and the water absorption rate of two grade high alumina material should be less than 7%. Fine grinding of soft clay and bauxite clinker with less than 4% water content. Mixed fine milling ingredients with this, can reduce the porosity of bricks.
Q:What is the standard size of high alumina brick?
Standard brick: 230 x 115 x 65; four points: 230 x 115 x 40; three points: 230 x 115 x 30; 150 x 120: Brick gable. Light weight brick 1 to 1.7 kilograms; heavy clay superscript brick weighs 3.75 kilograms; light 30 plates 0.79 kilograms; light 40 plates, 1.05 kilograms.
Q:What are the specifications for bricks?
Thecompressive node as a new type of building energy-saving wall materials, which can be used for masonry walls, but also has good thermal properties, in line with the construction of the building module, reduce the loss in the process of construction, improve work efficiency; the hole rate reached more than 35%, can reduce the weight of the wall, save the foundation engineering cost. Compared with common sintered porous brick, it has the characteristics of heat preservation, heat insulation, light weight, high strength and high construction efficiency. The product is made of shale as raw material. It is produced by high vacuum extrusion molding machine and one yard firing process
Q:Which is faster for heat transfer between corundum bricks or high alumina bricks?
There must be a difference. They vary in color from the amount of aluminum, the weight, the temperature, and the color.
Q:How many cubic bricks does a high alumina brick have?
Different content of aluminum, different proportion, weight is not the same. General grade T3 standard brick, 4.3~4.5kg, aluminium content 75. T3 size 230*114*65mm.
Q:What are the categories of bricks?
Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range