99.95% high purity weld molybdenum wire System 1

99.95% high purity weld molybdenum wire System 2

99.95% high purity weld molybdenum wire System 3

99.95% high purity weld molybdenum wire System 4

99.95% high purity weld molybdenum wire

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 100 m.t.

Supply Capability:: 100000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Quick Details

Place of Origin:	Hebei, China (Mainland)	Brand Name:	cnbm	Model Number:	er70s-6
Material:	CO2	Diameter:	0.8 1.0 1.2mm	Melting Point:	2700
Weight:	5kg 10kg 15kg	Application:	for welding low carbon steel,light gauge sheet,structures	Flux Content:	0.03
AWS:	ER70S-6	GB:	ER50-6	color:	golden

Packaging & Delivery

Packaging Details:	black plastic spool+layer winding welding wire+tarnish paper+plastic packing+carton 15kg:72cartons on a pallet,one 20FT container can loading 20-25tons
Delivery Detail:	with15-20 days

MS flux cored welding wrie for boiler welding :

The series of welding wries can be used to welding low carbon steel and low alloyed steel structure, such as ships, vehicles, bridges, boilers and buildings etc.

package:5kg,15kg,20kg

have excellent mechanical performance such as fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam. Suitable for all-position welding work.

Specifications of welding wire:

1) Sizes: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm

2) Applications: Widely used as welding carbon steel wires in shipbuilding,

Bridge building, machinery manufacturing and general welding purposes

Mechanical properties of deposited metal

C	Si	Mn	P	S	Cr
≤0.10	0.80~1.15	1.40~1.85	≤0.02	≤0.02	≤0.10
Ni	Cu	Al	Co	Ti	V
≤0.10	≤0.30	≤0.01	≤0.01	≤0.01	≤0.02

Mechanical properties of deposited metal
Yield stregth(Mpa)	Tensile strength(Mpa)	Elogtions(%)	Impact value (J)
≥400	≥480	≥22	≥27

picture

99.95% high purity weld molybdenum wire

Q: Is there a welding wire for gas shielded welding of stainless steel? What brands do you have?: Having such a welding wire.For example, AT-Y316L, is the Aetna 316L stainless steel CO2 gas shielded flux cored wire.308309309L has flux cored wire.I guess you'd like to ask about the flux cored wire. The upstairs are talking about argon arc welding wires.Argon arc welding wire is the beginning of ER.

Q: Which subjects should be included in the purchase of welding wires (auxiliary materials) in industrial enterprises?: Industrial enterprises to buy wire (auxiliary materials), not necessarily auxiliary workshop. This point must pay attention to, auxiliary materials can be used in the basic production vehicle. The main material is sometimes used in the auxiliary workshop.Purchasing wire (auxiliary material) in industrial enterprises shall be included in raw material subjects. Because both the main material and the auxiliary material are raw materials.Borrow: raw materialTax payable - VAT should be paid - the input taxCredit: bank deposits (accounts payable, etc.)Then, in accordance with the use of departments to confirm, recorded in the relevant cost subjects.

Q: Does argon arc welding thick material need no welding wire?: Argon arc welding is not like welding, welding electrode itself is filling material, argon arc welding is no filling material. Argon arc welding stainless steel without welding wire is formed by melting the base metal. Such as two stainless steel butt welding wire, in no case, two pieces of plate must be no gap, when the tungsten needle alignment weld produced high current that produce high temperature, the two panels are also melting, loosen the gun switch after the melting of stainless steel water condenses together welded together, if we must have with the wire.Summary: no welding wire welding workpiece can solder together must leave, if even only 0.5mm are difficult to weld, first after welding, the welding, the welding speed should be uniform, without wires, not large current about 20A, from the middle to both sides welding. After welding, the main point of non deformation is that the plate should be docked and added at least 1 centimeters a point. The copper lining under the condition plate is best, and the weldment can be placed on the platform or made as a fixture. Speed must be fast, the more slowly, the more deformation.

Q: Q235 plate thickness 4mm-5mm what is the diameter of the wire to be selected by submerged arc welding what is the flux?: In fact, 4-5MM has a special submerged arc welding 1.6 wire, that is automatic two welding machine, remove gas and welding flux. Or use 2.5 of the wire,

Q: Carbon steel, with two, welding current, voltage, welding speed, wire diameter, thank you: The following welding parameters are usually used: 100-200A, 18-25V, 1.2-1.6mm

Q: What welding wire should be used when welding between 0cr18Ni9 and 0cr18Ni9?: Base metal 0Cr18Ni9 welding rod A137 argon arc welding wire H0Cr20Ni10

Q: What is the difference between Q235B welding with H08mnA and H08A submerged arc welding wire? Which match is better? Ask professional personage to analyse for me: Nothing different.Better with H08A. It does not contain Mn

Q: What kinds of brands are there for gas shielded welding wire?: The domestic, the Atlantic, bridge, bridge, Tiantai, Kam, Shanghai electric power, Kunshan Beijing group, these are relatively large, a little more of the other brands, Hodge, many are home to open a small workshop will be able to do, not a example.

Q: Can gas shielded welding welding aluminum welding wire?: Gas shielded welding for welding aluminium welding wire.The method is put into a U shape wheel rotation wire, wire feeding hose for Chengtefurong, gun into the water.Gas shielded welding refers to the welding method of carbon dioxide or argon gas, without welding wire. CO2 welding efficiency is high, argon welding mainly welding aluminum, titanium, stainless steel and other materials.The use of welding torch must first check the performance and gas tightness, welding torch of the connecting parts, gas, road and control valve, etc., shall not be stained with grease.When welding torch ignition, should first open acetylene valve ignition, after opening oxygen valve to adjust the flame; turn off the fire, should first off acetylene, and then shut off oxygen. When stopping the use, it is strictly forbidden to permanently connect the welding torch, hose and gas source.The use of the torch, clean work surface paint, rust layer, and can not work on the concrete, to prevent water and cement in high temperature blasting splashing wounding.In the cutting torch ignition, the first ignition test, check the cutting nozzle is installed. When the ceasefire is committed, acetylene should be first turned off and then oxygen closed.

Q: CO2 protection wire, which brand of domestic quality is good?!In addition to the Atlantic and the Golden Bridge, and the brand of excellent quality?: If you want to talk about the quality, it's the Atlantic, the bird's nest, the space project, and the Three Gorges dam!

Send your message to us

*Email

*TEL

*Quantity

*Unit