Synthetic Magnesite Refractory Products

Ref Price:
Loading Port:
China Main Port
Payment Terms:
Min Order Qty:
Supply Capability:

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

High iron synthetic magnesite, high iron & high CaO magnesite,magnesite alumina spinel, magnesite chrome spinel. All the kinds of synthetic magnesite and spinel are made from high quality magnesite ore and dolomite ore, by requiting and sintering them at high temperatures together with iron powder, chrome powder, and bauxite as an additive.


Chemical Compostion /%

Physical Index







































































Synthetic Magnesite is a kind of  industry raw materials with properties of moderate basicity and chemical activity, widely used in the fields of national defense, medical, chemical, paper-making, shipbuilding and environment protection etc.

l Its primary technology application contain the areas as following: cellulose acetate, drilling mud, fire retardance filling, flue gas desulfurization, leather-making, oil refining additive, medical industry, rubber and plastics industry, sugar industry and wastewater treatment etc.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Does the aluminum silicate fiber can be used outdoors? If not, what other refractories can be used outdoors?
Q:what's the classification of fireproof materials?
Fireproof materials are used in construction, in various forms and it has played an absolute role in modern fireproofing, common fireproofing materials include fireproof panel, fire door, fireproofing glass, fire retardant coating, fireproof bag,etc Or the material itself has a high temperature resistance, heat-resistant, flame-retardant properties. Most of them are used for the construction industry.
Q:Who knows how many fire heat preservation material are there?
Fire proof board is a fire refractory building material for surface decoration, widely used in interior decoration, furniture, kitchen cabinets, laboratories mesa, walls and other fields. Fire board is base paper (titanium powder paper, kraft paper) processed by melamine and phenolic resin, high temperature and high pressure. 1 mineral wool board, glass wool board: mineral wool, glass wool insulation. It does not burn itself, have good performance such as high temperature resistance, light quality. Such plate have evolved into plate with inorganic adhesive material as base material, mineral wool, glass wool as reinforcing material plate. 2 cement board: High strength, wide source. In the past, it is used to make fire prevention ceiling and partition wall, but its fire resistance is poor. Cement concrete component has good heat insulation and sound insulation performance. It can be used as the partition wall and the roof panel.
Q:What type of firebrick does TZ-3 represent?
It is the standard brick.
Q:How should refractory cement be used?
How to use refractory cement? How to use refractory cement? Thank you.
Q:What are the materials of white firebricks?
They are made of baked refractory materials with pale yellow and a little brown on the surface and very cheap. They are mainly used to pile up smelting furnace and can withstand high temperature from 580 degrees Celsius to 770 degrees Celsius. While the firebricks, also called refractory bricks by others, have a certain size and shape. They can be classified according to manufacturing process, namely, the unburned bricks, burnt bricks and electrically fused bricks. Also they can be divided into common bricks, standard bricks and specific bricks according to different size and shape.
Q:What needs to be paid attention to in the construction of high- temperature refractory mortar?
In the construction of high-temperature refractory mortar, the following matters should be noted: 1. Take out the organic fire blocking material and knead it into tha shape of a ball. If the temperature is too low, the blocking material along with the package can be put into 40-70℃ warm water and heated before any other operation. 2. During the use of high-temperature daub masonry stove, the minimum mortar joint should be 0.5mm and general mortar joint should be 3-5mm, which can solve the processing and fine grinding of refractory brick on the brick grinder. Besides, it is conducive to the health of workers, and can reduce the masonry effort, ensure the quality and speed up the construction progress. 3. When making urgent repair on the stove, if the joint is much too large, 2-3mm refractory pieces can be appropriately added into the high- temperature refractory mortar, and stirred to fill the joint so as to shorten the repair time and ensure normal production. 4. High- temperature refractory mortar can be painted inside various furnace body, and it should be guaranteed that the surface of the furnace body has no dust or debris before painting. The holes should be cleaned up before plugging. Lay, embed, and fill the blocking material into the gap of holes evenly. For larger holes, flame screen can be used as the framework to increase strength.
Q:how about the performance of aluminum silicate fire proof thermal insulation?
aluminum silicate fire proof thermal insulation board has a good performance. it is a artificial board that separates the wood and plant fiber by mechanical and chemical methods and mixed the adhesion agent and water-proofing agent, molding by high temperature and high press. the density of fiber. tha above information is coming from the Internet and it is just for reference.
Q:How to distinguish the fire resistant level of construction materials?
There are 3 conditions for building components to reach fire endurance, namely: Loss of ability to support; loss of integrity; loss of fire insulation function. As long as one condition occurs, fire endurance is reached and the time before it is called fire endurance. 1), loss of ability to support: If the specimen bearing capacity and rigidity reduce, section area shrink, collapses or deformation exceeds specified numerical value because it cannot bear the load of original design under flame or high temperature, it loses the ability to support. 2), loss of integrity: It mainly refers to the thin wall separating component(such as stairs, windows,partitions, ceiling, etc.) burst or partially collapse under flame or high temperature, and penetrating fracture or opening appears, and the reverse side even burn. For example, when the floor is under flame or at high temperature, the flame spread to the upper room, which indicates that the integrity has been damaged. 3), loss of fire insulation function: It mainly refers to that seperating components loses thermal insulation and excessive heat conduction. In experiment, if the average temperature of component unexposed surface exceeds 140 ℃, or if any spot at the unexposed surface exceed the initial temperature of 180 ℃, the component loses fire insulation function.
Q:What a blast furnace refractories generally?
Common refractories often use silica brick, semi-silica brick, fireclay brick, high alumina brick, magnesia brick, etc. special materials often used are AZS brick, corundum brick, directly bonded magnesia-chrome brick, carborundum brick, silicon nitride bonded silicon carbide bricks, nitrides, silicides, sulfides, borides, carbides and other non-oxide refractory materials; calcium oxide, chromium oxide, aluminum oxide, magnesium oxide, beryllium oxide refractory insulating refractory frequently used. material diatomite products, asbestos products, insulation boards. monolithic refractories have fettling frequently used, refractory ramming mixes, refractory castable, fire-resistant plastic, refractory clay, refractory gunning refractory projection material, refractory coatings, lightweight refractory castable, stemming etc.

1. Manufacturer Overview

Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range