white fused alumina for refractory 99%

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-
Inquire Now Customer Service

Contact us by

(1) WeChat
(2) Whatsapp: +8617190086776

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Packaging & Delivery

Packaging Detail:25kg bag or ton bag or as your requirement.
Delivery Detail:within 20 days delivery after receipt of advance payment.

Specifications

99% high purity abrasive White fused alumina for refractory
1.White fused alumina99%
2.Refractory: 0-1mm, 1-3mm, 3-5mm, 5-8mm

Products discription

1.Introduction

The main raw material of white fused alumina is high grade processed alumina, which is fused with the carbon material and scrap iron in the electic furnace under the high temperature of above 2200°C.The product is characterized by low expansion coefficient, high refractoriness, good thermal and chemical stability.

2. Grain size commonly used

  • Refractory: 0-1mm, 1-3mm, 3-5mm, 5-8mm ,200#-0, 325#-0.

  • Abrasives: F24-F60.

  • Sandblasting abrasive:F10-F240.

  • Precision casting: F80-100, F100-F120.

  • Ceramic & electronic polishing:F240-800.

    3.Physical properties of White Fused Alumina

Item

Color

Color System

Mohs Hardness

Melting Temperature(°C)

Refractory Temperature(°C)

True Density( g/cm3)

Magnetic Material

Specification

white

trigonal system

min10

2250°C

1900°C

min3.50

max0.003%

4.Chemical index of White Fused Alumina

Purpose

Specification

Chemical composition(%)

Magnetic material content(%)

Al2O3

Na2O

SIO2

CaO

For abrasive

F

12#—80#

min99

max0.6


max0.4

max0.003

90#—150#

min98.5

max0.003

180#—240#

min98.2

max0.7


max0.4

max0.002

For refractory

Size sand

0—1mm

min99

max0.5


max0.4

max0.003

1—3mm

3—5mm

5—8mm

Fine powder

200#—0

min98.5

max0.5


max0.5

max0.003

325#—0

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What can red stone refractory do?
In severe cases, the resistance to high temperature without softening down the Celsius temperature. Refractory materials are widely used in metallurgy, chemical, petroleum, machinery manufacturing, silicate, power and other industrial fields, the largest amount of metallurgical industry, accounting for 50% ~ 60% of the total output. Chinese use less impurity clay in more than 4000 years ago, firing pottery, and have been able to cast bronze. In the Eastern Han Dynasty (AD 25 ~ 220) have been used to make clay refractory kiln firing porcelain material and sagger. At the beginning of twentieth Century, the development of refractories to high purity, high density and ultra high temperature products, while developing completely without firing, small consumption of unshaped refractory materials and high refractory fiber (160 for industrial furnace refractories above 0 DEG C). The former, such as alumina refractory concrete, is often used in large chemical plants, ammonia synthesis plant, two - stage reformer furnace wall, the effect is good. Since 50s, the rapid development of atomic energy and space technology, the development of new energy technology, requires the use of special refractory material of high temperature resistance, corrosion resistance, thermal shock resistance, erosion has excellent properties, such as melting point above 2000 DEG C, oxide refractory compounds and high temperature composite refractory materials.
Q:what are the types of piping insulation material fire rating?
according to China's national standard GB8624-97, the combustion performance of construction materials can be divided into several grades grade A: Incombustible building material: Almost no burning material. Class B1: nonflammable building material: nonflammable material has a good flame resistance effect. when it meet the open fire in the air or burnd at high temperature, it is difficult to spread quickly, and when the fire source is removed, the combustion stop immediately. Class B2: flammable building material: flammable material has a good flame resistance effect. when it meets open fire in the air or at high temperature, it will immediately burst into flames and easily cause fire spread, such as wooden column, timber roof truss, timber beam, and wooden stairs,ect.. Class B3: inflammable building material: No flame resisting effects, highly flammable, high fire risk. 2, external wall thermal insulation materials, in accordance with fire rating, can be divided into1) grade A combustion performance thermal insulation material: Rock wool, glass wool, foam glass, foamed ceramics, foam cement, hole-closed perlite ect.. 2) class B1 combustion performance insulation materials: Extruded polystyrene board (XPS) after special treatment / Special treatment of polyurethane (PU), phenolic aldehyde, gelatine powder polyphenyl granule, etc. 3) combustion performance of class B2 insulation material: molding polystyrene board(EPS), extruded polystyrene board (XPS), polyurethane (PU), polyethylene (PE), etc.
Q:What are the construction measures of refractory material in winter? Please descriptive briefly.
Binding agent should be attaced great importance to when construction is conducted in winter. Generally if the bingding agent is water or cement, antifreezing measures should be taken.
Q:Graphite and other carbon materials may be oxidized to CO or CO2 at high temperatures. But why can they be refractories?
There is no contradiction for this. Any substance can be combustible, but different materials have different ignition points.There are many types of graphite. Pyrolytic graphite has a much lower ignition point. Therefore, as long as it reaches at a certain temperature, it can convert into graphite. Mostly, in practical applications (such as brake pads will add a certain amount of graphite), graphite is required to have refractoriness of below 1000 ℃. Graphite can serves as both the combustible and refractory material. So, it can be used as a fire-resistant and high-temperature-resisrant material because graphite (lamellar graphite) has a ignition point of at least 3000 degrees in an oxygen free condition. The above information is for reference only and is offered by Xin Ruida Graphite Company.
Q:What materials are needed to make the amorphous refractory bricks?
Amorphous refractory bricks have good quality, good reputation, complete in specifications,high refractoriness, strong resistance to slag, and long service life. It’s worthwhile.
Q:Firing high temperature kiln of refractory and internal temperature being as high as 1600 ℃, metal heat exchanger can't use, how to do?
Directly using silicon molybdenum kiln, the temperature is better. Now using the electricity is cheaper than the price of other fuels.
Q:What's the maximum temperature that the high-temperature resistant refractory ceramic fiber cotton can endure?
It depends on what material the ceramic fiber gasket uses. It’s usually referred to high temperature gasket made from ceramic fiber paper. It is generally classified into normalized form and high alumina type, of which the former can resist the maximum temperature of 1260℃ and its continuous use temperature is 1000℃, and the latter can be used for a long period at the temperature of 1200℃. Nichrome wire, stainless steel wire and glass fiber are reinforced. Ceramic fiber coating cloth and slag cloth, sintering ceramic fiber cloth and ceramic fiber fumigation cloth) Characteristics of the ceramic fiber cloth: It has high temperature resistance, low heat conductivity, thermal shock resistance, low thermal capacity; superior insulating property at high temperature, long service life; resistance to nonferrous metals like molten aluminum and zinc erosion; low and high temperature strength; innocuity with no adverse effect on the environment.
Q:It the Special Fire-Proof Material belonged to ceramics? Is there a national standard of the Special Fire-Proof Material?
The fiber and reinforcing material of the metal ceramic is also belonged to the Special Fire-Proof Material. ~~~~GB is too much trouble, GB online should ~~~ Lei Bao Refractories for you. The high temperature inorganic coating. 5. The refractory compound. 3. The high melting point oxide. You can search it on the internet according to the classification~~~~ The special refractories can be divided into five categories: 1. metal ceramic
Q:What things and cement mixed can act as refractory?
Cement acts as cementing material. Itself works by refractory aggregate and stir the refractory material for its gelling refractory aggregate both should be fire-resistant.
Q:How to count the construction costs of refractories?
In winter, the temperature of the the fire-resistant masonry, fire-resistant plastic, sodium silicate, phosphoric acid castable should be maintained above 5 ℃. Usually greenhouses in which heating facilities are installed to maintain the appropriate temperaturere for the construction environment should be erected in refractory masonry. The temperature around the construction site of the industrial furnace and refractory masonry shall not be lower than 5 ℃.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range