Fireclay Insulation Bricks for Electric Power Industry

Fireclay Insulation Bricks for Electric Power Industry System 1

Fireclay Insulation Bricks for Electric Power Industry System 2

Fireclay Insulation Bricks for Electric Power Industry System 3

Fireclay Insulation Bricks for Electric Power Industry

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 2 m.t

Supply Capability:: 5000 m.t/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Fireclay Brick RN40

Fireclay Brick for Hot Blast Stove

$Fireclay Brick for Coke Oven Refractory$

Fireclay Brick for Coke Oven Refractory

Fireclay Brick RN40 for Hot Blast Furnace

Fireclay Brick (Al2O3 58-60) for Glass Furnace

$Fireclay Brick Corundum Brick of Refractory Brick for Steel Industry$

Fireclay Brick Corundum Brick of Refractory Brick for Steel Industry

$Fireclay Brick - Low Porosity Refractory Clay Brick$

Fireclay Brick - Low Porosity Refractory Clay Brick

Fireclay Brick (230*114*65mm)

Brief discription for Insulation bricks for Electric Power industy

CMAX Insulation bricks for Electric Power industy are classified according to alumina content ranging from 48% to 90%.

CMAX Insulation bricks for Electric Power industy are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln,regenerator, etc.

Brief features for Insulation bricks for Electric Power industy

◆Low thermal conductivity

◆Excellent acid and base slagging resistance

◆High refractoriness

◆Excellent thermal shock resistance

◆Excellent mechanical strength

◆Good spalling resistance and wear resistance.

◆Good corrosion resistance.

◆High-temperature creep rate is quite low.

◆Good volume stability at high temperature.

◆Low bulk density, low thermal conductivity, good thermal insulation performance.

Technical data for Insulation bricks for Electric Power industy

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories,at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time,seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:After an order is confirmed,when to deliver?

A:15-25days after deposit.

Q6:Is your company accept customization?

A:We have own factory and excellent technical team,and we accept OEM service.

Q7:How about your company's certification?

A:ISO9001 and Test Report,also we could apply other necessary certification.

Q8:How to slove the quality problems?

A:If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.

Q: is it correct that the higher the refractoriness is, the better refractory bricks are?: Not completely correct. Refractory bricks need to be strong in addition to the fire resistance.

Q: when to replace the worn refractory bricks in rotary?kiln?: Wear out at least 23.

Q: The furnace refractory bricks are burnt into ash, what material can resist higher temperature than the refractory brick: steel plate is ok

Q: how much is the content of the high alumina of refractory brick?: linear?change?on?reheating is small and Slag resistance is good, matte smelting, good thermal shock resistance used refractory materials should be resistant to high temperature: In front of the furnace, the temperature can reach 1800, copper blowing. The maximum temperature in the smelting furnace area is on the top, pyro-refining and electrorefining, magnesia chrome brick, magnesia chrome castable, magnesia alumina brick. The commonly used refractory materials is direct-bonded?magnesia-chrome?bricks, which has large volume density. manufacturing technique of copper smelting consists of five parts, Clay brick

Q: What are 85 bricks, 95 bricks and standard bricks? What are the specifications?: Chinese in the spring and Autumn period has created a square and brick, Qin and Han Dynasties brick technology and production scale, quality and variety have significant development, known as "Qin Zhuanhan tile".

Q: How aluminium oxide becomes a entity from the the form of powder (such as a ball, a stone, or a refractory brick)?: Just like the process of making steamed bun from flour. Ball milling ---in the auxiliary material to make the slurry --- suppress the body --- high temperature calcination

Q: What are the reasons for the production of waste in the formation of fireclay bricks?: The reasons for the production of waste when form fireclay bricks: Tile size is unqualified. This is due to the mold installation is not firm, the template transfers when molding; if the amount of material being added fluctuates largely, also can cause the body size changing. Ji Yangon Chi lie charge generation layer containing decyl poke pull and crack. The molding operation does not according to the principle of the light first and the thick later. At the initial pressure, the air doesn't releases, which causes the elastic aftereffect by repressing. Too much mud water, uneven mixture and inequal template all can make the body produce layer crack or crack. Twist. The template is used for too long, the template deforms, so raw brick deforms, the amount of water is too large, brick naturally deforms, causing the body twist. Miss edge and angle. Because of poor plasticity of mud, particles segregate, feeding back corner is not real, the body will appear side missing and angle modulation phenomenon. Bias voltage. Due to the deflection of the die head or the uneveness of mold bottom. Loose。 Due to insufficient feeding amount or insufficient pressure times.

Q: 1200 degrees inside the furnace, lay a layer of refractory brick, what is the temperature outside?: except refractory brick, refractories include refractory concrete (refractory cement+aggregate), fire-resistant insulating layer (refractory cement+vermiculite powder or refractory cement + diatomaceous earth) and so on.

Q: What is the life of an old fashioned refractory brick kiln transformed into a flat topped tunnel kiln? what material should be used to transform the old fashioned refractory bricks vault kiln to flat tunnel kiln, and how long is the service life?: use castable refractory

Q: How to use the winding packaging machine to pack refractory bricks: Over 150KG the most common winding machine can pack, if it is light or the goods scatter, then add capping or pre-drawn device is all right.

Send your message to us

*Email

*TEL

*Quantity

*Unit