Q:How to remove the bottom of coke steel

Finally, wash the rice cooker, stove, as well as your tired hands, thoroughly washed several times. Here, everything is back to normal, as if nothing had happened.After such a toss, the coke pot was removed, but the bottom layer of the so-called "nonstick layer" are often the early damage (normally always destroyed), it is impossible to. It's like trying to get rid of terrorists.If the bottom of the layer of carbon black is not easy to erase, even if, even with good. Some people may worry about eating into the carbon poisoning, I think there is no need to worry about this. Wenchuan earthquake hero, Mr. Zhu Jianqiang, light to eat charcoal for 36 days, you can see the toxicity of carbon nothing. Moreover, after cleaning the rice cooker in the layer of carbon black has very little

Q:What is the difference between metallurgical coke and chemical coke

The chemical composition of coke including fixed carbon, ash, sulfur, volatile matter and moisture. Except moisture, other ingredients in dry coke, is an important raw material of cupola smelting, casting of the components of specific inspection requirements.

Q:How much coke is needed for a ton of iron

Iron ore in blast furnace, mainly iron and oxygen compound. At high temperature, the carbon monoxide produced in the coke and the carbon dioxide in the injection and the carbon monoxide generated by the carbon capture the oxygen in the iron ore, which is called the reduction. The iron ore is used to produce pig iron by reduction reaction. The gangue in the iron ore, the ash in the coke and the spraying material and the flux of the limestone in the furnace are combined to generate the slag, and the slag is discharged from the taphole and the slag outlet respectively. The gas is derived from the top of the furnace, which is used as industrial gas after dust removal. Modern blast furnace can also use the top of the high pressure, with the export part of the gas power generation.

Q:I see that there are metallurgical coke and coke on the Internet, what is the difference between them (I hope to be able to say in detail) and a level of two points, how is this going on?.. Where is the quality of coke in China? Hunan good coke plant which? Although the problem is a little bit more, I hope that insiders can give some useful information. Extremely grateful.

The following indexes: Metallurgical Coke metallurgical coke: fixed carbon, 86%; calorific value 7300cal/kg; ash < 12%; volatile < 1.9%; all 5% "0.6%" water; sulfur; two metallurgical coke: fixed carbon 84.5-85%; calorific value 7000cal/kg; ash < 13.5%; volatile "1.9% full" water; 6%; "three sulfur 0.7%; metallurgical coke: fixed carbon 83-84.5%; calorific value 6500cal/kg; ash < 15%; volatile < 1.9%; all 6%" 1% "water; sulfur;

Q:In the coke analysis index, M40% and M25% respectively mean what?

(1) crushing strength (shatter strength): the ability of a certain particle size coal sample to fall under the condition of free fall.

Q:What is coke and how is coke classified?

Coke definitionBituminous coal in the absence of air is heated to 950-1050 DEG C, after drying, pyrolysis, melting, bonding, curing and contraction of the final stage of this process is made of coke, coking high temperature (high temperature carbonization). By high temperature coking coke for blast furnace smelting, casting and gas generated in the process of coking. After the recovery and after the purification of coke oven gas is not only a high calorific value of fuel, and is an important raw material for organic synthesis industry. Metallurgical coke is coke, coke, iron alloy coke and non-ferrous metal smelting coke for metallurgical coke collectively. More than 90% were used for blast furnace ironmaking blast furnace coke, so often referred to as metallurgical coke is coke. The special cupola molten iron and coke. Coke is the main fuel cupola molten iron. It is melting charge and molten steel overheating, the support column to maintain its good permeability. Therefore, coke should have Large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough.

Q:Effect of coal fineness on coke

From the point of view of the uniformity of coal material, the more finely pulverized coal. But if the coal fineness is small, because of the presence of a larger particle weakly caking coal and ash and coke cracks increased, the uniformity of deterioration. If the particle size of coal is not uniform, it is easy to produce segregation phenomenon in the transportation process, the grain size of different size will be gradually stratified by size. Due to the different coal hardness of the coal blending, large particles of coal is often a greater hardness of coal, so the segregation phenomenon, will make the different coal species gradually separated, so that the uniformity of coal deterioration.

Q:What is the use of coke

Finally made coke, this process is called high temperature coking (high temperature carbonization). Coke obtained from high temperature coking for blast furnace smelting, casting and gasification. Coke oven gas produced in the process of coking and recovery is not only a high calorific value of fuel, but also an important industrial raw material for organic synthesis

Q:Types of coke and use of coke

China's coking industry has been formed with conventional machine coke oven blast furnace ironmaking production of metallurgical coke, with heat recovery coke oven production machinery foundry and foundry

Q:Why is coke used in blast furnace steelmaking?Why not use coal?

(2) reduction: high temperature gas generated in coke combustion in the raceway, passed to the material in the process of heat rising, the endothermic reaction and coke formation, CO and H2, then CO and iron oxide in iron ore reduction reaction is transformed into metallic iron.(3) the role of the skeleton: the blast furnace smelting process occurs in the movement and interaction between the rising of the gas and the falling of the charge. The pellets, coke, iron ore, ore and other materials according to a certain proportion, and batch sequence into a blast furnace, blast furnace smelting in reducing atmosphere under the hot metal, after providing to the steelmaking plant of the steel-making.