Refractory Fireclay Brick with Al2O3 Content around 31%

Ref Price:
Loading Port:
Qingdao
Payment Terms:
TT OR LC
Min Order Qty:
17 m.t
Supply Capability:
10000 m.t/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information
CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

High alumina ceramic refractory brick for blast furnace

Ceramic refractory brick description

Henan sansong porcelain co is specialized in high alumina high strength ceramic refractory brick, together with honeycomb ceramic heat exchanger, has been widely used to industrial furnaces or blast furnace with regenerative technology

They are available in various size and shapes

Our products enjoy a good reputation for their excellent quality and service in domestic and international markets.

 

Feature
Low thermal conductivity   
Excellent acid and base slagging resistance
High refractoriness    
Excellent thermal shock resistance    
Excellent mechanical strength

High corrosion resistance

Good spilling resistance

High cold crushing strength 

Excellent abrasion resistance at cold and hot conditions

High refractoriness

High mechanical strength

 

Application
CMAX high alumina bricks are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc

ITEM

UNF42

UNF46

ZGN42

RN40

TDL45-12

Refractoriness,

1730

1750

1750

1730

1760

Bulk Density, g/cm3

2.15

2.25

2.3

2.15

2.37

Apparent Porosity, %

22

20

15

24

12

C.C.S, Mpa

30

35

58

28

68

Refractories Under Load (0.2Mpa)

1400

1420

1450

1430

1500

Reheating Linear Change, %

1400x2h              0.1-0.4

1430x2h              0-0.1

1450x2h              0-0.2

1350x2h       0-0.3

1450x2h              -0.1+0.05

Al2O3 Content , %

42

46

42

40

45

Refractory Fireclay Brick with Al2O3 Content around 31%

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How to calculate the pressure of hydraulic machine pressures refractory brick?
If it is a plunger type cylinder, the pressure of a cylinder is the cross-sectional area of the piston multiplied by the pressure of the hydraulic system; if it is piston cylinder, that is the inner diameter of the hydraulic cylinder multiplied by the pressure of the hydraulic system. Adopt cm as diameter's unit, a unit of pressure is kilogram force per square centimeter, the calculated result is kilogram which divided by one thousand is ton.
Q:What is light brick and what are the characteristics of light brick?
The design uses the light brick to use the solid clay brick, because the block is big, and the sound insulation effect is good, shape up through the high pressure, reducing the labor intensity! Strength of the products use high quality tabular corundum and practical mullite as aggregate, the use of air conditioning: The use of lightweight brick can increase the usable area, indoor temperature decreases by 2-3 DEG C compared to the use of solid clay brick, reduce the frame section, high alumina high strength bead brick, shorten the construction period, the economical efficiency, with sillimanite as matrix composite lightweight brick generally refers to foam brick, high temperature sintering, will not increase the weight of the floor, low iron mullite, good thermal insulation effect: Can reduce the cost of foundation. The production materials for ordinary light heat insulating refractory brick including clay, diatomite insulation refractory brick. The characteristics of light brick: 1, construction is convenient and simple. 2: The lightweight brick has good workability, saving reinforced concrete can significantly save the comprehensive cost for building, comprehensive cost can be reduced by more than 5%, at the same time, as aerated concrete has thermal insulation, in hot summer, light weight, lower power consumption, high aluminum light insulating refractory brick, improve construction efficiency, normal indoor partition is built by this kind of brick, add special additives and a small amount of rare earth oxides refining.
Q:Are refractory bricks, burner block and thermal insulation brick the same? Are they the same thing?
the proportion of raw materials of refractory bricks and thermal insulation bricks. chain of various types of products
Q:Shale brick and clay brick? Answer before you know it
The clay brick with clay, shale, coal gangue as raw materials, crushing, mixing kneading with artificial or mechanical pressing, sintering and building bricks after drying at 900 centigrade temperature by oxidizing flame firing.
Q:What are the advantages and disadvantages of clay refractory bricks?
The clay brick refractory brick and be roughly the same, up to 1690~1730 DEG C, but the load softening temperature is 200 degrees Celsius above the low brick. Because clay bricks contain crystalline Mullite with high refractoriness, they contain nearly half of the amorphous glass phase of low melting point.In the temperature range of 0~1000 DEG C, the clay brick volume increases with temperature uniform expansion, linear expansion curve approximates a straight line, the line expansion rate is 0.6%~0.7%, about half of the brick. When the temperature reaches 1200 degrees Celsius and then continues to heat up, the volume will begin to shrink from the maximum expansion. The residual shrinkage of clay brick results in the cracking of masonry joints, which is a major drawback of clay bricks. When the temperature is above 1200 degrees, the low melting point of the clay brick gradually melts because the particles are very close to each other due to surface tension, resulting in volume shrinkage.
Q:Are there any good improvement measures for the always collapse of the previous vaulted tunnel kiln built by refractory bricks?
Volume shrinkage, uneven shrinkage and expansion of part, long-term high-temperature processing crystal type changes, calcium and other substances forming the refractory brick is Magnesium Oxide. Also the temperature changes quickly, and belongs to the crystal compound, silicon aluminum, sealing material's selection should be pay attention to
Q:What raw materials can be added to fireclay brick to respond to the urgent cold and urgent heat?
The higher the impurities, there is no need to add some expensive performance-improving raw materials. But you can mainly choose high purity raw materials to proporly increase the performance of the clay brick, such as thermal shock. You can change relatively high-grade refractory brick. It depends on your conditions of usage if the requirement is strict. The thermal shock resistance of clay brick itself is not bad, and will almost all be affected, because the clay brick is very cheap, inside the glass phase more. Creep.
Q:What is the clay used to make the refractory brick?
Lining brick of teeming ladle; refractory clay used in building materials industry to produce high alumina bricks for cement kilns and glass furnaces, as well as anti sliding, high alumina lining bricks and high alumina refractory clay. The hard clay in refractory clay is used for making blast furnace refractory material, which is used in agriculture as a fertilizer promoting agent and, and electron. High alumina clay is also used in the oil well, generally does not disperse in water. In metallurgy, accounts for 2/3 of abrasive products, and so on. Hard clay and semi hard clay can be used to manufacture daily-use ceramics. High alumina clay after calcination, which has high temperature resistance! Refractory clay refers to the degree of fire resistance is greater than 1580, the hardness and proportion is relatively big, the refractoriness is good. They except has relatively high refractoriness. Such as aluminum sulfate, its dosage accounts about 70% of all the refractory materials;
Q:What building materials can take the place of clay bricks?
Housing grades have been upgraded, heat preservation, sound insulation, heat insulation, seismic, energy-saving performance fully reflected, can improve the selling point of commercial housing 3%, in the major cities in China has become the preferred condition of user purchase.
Q:How about clay bricks?
Fired ordinary brick is one of the indispensable building materials in production and life, but its quality is not good or bad in the absence of professional equipment. Now to introduce a little trick:According to the main raw materials for clay brick, shale, coal gangue and fly ash brick. Mainly in our local clay brick. According to the compressive strength of weathering resistance of radioactive material and qualified brick, according to the size deviation, appearance quality, efflorescence and lime burst into superior products, first-class products, qualified three quality grades.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range