Raw Materials for Refractory:Black Silicon Carbide 0-1/1-3/3-5mm and Powder at Low Prices

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Place of Origin:	China (Mainland)	Brand Name:	CNBM	Model Number:	CF180# 240# 320# 800# 1200#
Material:	SIC	Usage:	Lapping, Polishing,Blasting, Refractories	Abrasive Grain Sizes:	46#..1200#...2000#..2500#
color:	black and green	hardness:	9.15 mosh	melting point:	2250

Packaging Details:	bags, cartons
Delivery Detail:	15-20 days

silicon carbide Size Available:
F10-F220,F240-F1200
Other special size could be supplied as required.

1.used for made abrasive products 2.professional manufacture 3.prompt reply-within 24hours 4.prompt delivery-within 15days.





Grit	SiC	F.C.	Fe2O3
F12-F90	98.50%min	0.20%max	0.60%max
F100-F150	98.00%min	0.30%max	0.80%max
F180-F220	97.00%min	0.30%max	1.20%max
F230-F400	96.00%min	0.40%max	1.20%max
F500-F800	95.00%min	0.40%max	1.20%max
F1000-F1200	93.00%min	0.50%max	1.20%max
P12-P90	98.50%min	0.20%max	0.60%max
P100-P150	98.00%min	0.30%max	0.80%max
P180-P220	97.00%min	0.30%max	1.20%max
P230-P500	96.00%min	0.40%max	1.20%max
P600-P15000	95.00%min	0.30%max	1.20%max
P2000-P2500	93.00%min	0.50%max	1.20%max
Black Silicon Carbide is brittle and sharp and has electrical and heat conductivity in some degree. Aplications : Black Silicon Carbide is suitable for make grinding wheels, cutting wheels, mounted wheels, oil stone, abrasive media, and also suitable for surface grinding, lapping or polishing. The abrasive products made of it are suitable for working on Cast Iron, Non-ferrous Metal, Rock, Leather, Rubber, Wood, Ceramic, etc. Black Silicon Carbide is also broadly used as high-grade refractory material and metallurgical additive.

Black silicon carbide 0-1/1-3/3-5mm and powder with low price

Q: what kind of refractories is used to make the industrial silicon furnace mouth long life?: Fused zirconia corundum brick, the smelter of the glassworks is used this kind of lining, and you can contact by private letter.

Q: How long is the duration of fire resistance of autoclaved flyash-lime bricks?: The fly ash effect will continue to play a role in a considerable period of time, so the long-term strength keeps strengthening, the average age of 90 days of strength will grow 80%-100% more than the 28 days.

Q: What requirements should refractory materials meet?: The operating temperature of forging furnace is above 1000, which can ensure the normal operation of the furnace, prolong the life of the furnace and save energy. General requirements for refractories are as follows. 1 They should deform at a sufficient temperature without melting. 2, They should have necessary structural strength without softening and deforming. The volume should be stable at high temperature without expansion, contraction or cracking. 4, They can resist erosion of molten metal, slag, gas and other chemicals.

Q: What's the fire endurance of hollow brick?: This question is really very simple. It is better no to exceed 1050℃, or it will be easily burnt. I think 980℃ is ok actually. Around 950℃, no more than 1100℃, or brick will be burnt and melted easily.

Q: What's the definition of fire endurance of the fire-resistant coating for steel structure?: 1. Fire endurance. Conduct fire resistance test of any building component according to the standard time-temperature curve, and the time when it is subjected to the fire to the time when it loses support capability or fire insulation function or its integrality is destroyed is referred to fire endurance. 2. Steel has relatively low fire endurance which is usually 0.25h only, namely 15 minutes; 3. Of steel structure buildings, steel can be used as beams, pillars, etc. but its fire endurance is not enough (usually these components have higher requirement on fire endurance, and take pillar as an example, it is usually demanded that the fire endurance should be 2-3h), and under this condition, it needs to brush fire retardant coating so as to raise the fire endurance. As to the specific quantity or types of the fire retardant coating, it is decided upon the actual conditions. In short, the building material needs to meet the required fire endurance of the buildings.

Q: what kind of fireproof materials is used for high rise buildings?: Recommended thickness of 1mm or more # 304 stainless steel, refractory, corrosion-resistant, easy to clean. closed balcony of high rise buildings use thickened manganese, aluminum profiles. You can also use plastic steel window, solid wooden windows. Mg-Mn alloys have excellent weldability and corrosion resistance, unstressed corrosion tendency. Mechanical properties are not good enough, the ultimate strength of 210 ~ 280MPa.

Q: How long is the fire resistance time of the AAAfire resistance rolling shutter door?: How long is the fire resistance time of the AAA fire resistance rolling shutter door?

Q: Is the refractory reached British BS standard and used for cables in China at present ceramic silicone rubber?: The texture should be designed according to the British relevant BS standard; crosslinked polyethylene or ethylene propylene rubber under 6600V to 19000 / 33000V is not necessarily ceramic silicone. The rated voltages of a small amount of smoke and corrosive gases from 3800 & # 47 when the BS 7835-2000 is affected by fire.

Q: For refractory, why is it necessary to store the first mixing materials for some time under proper moisture and temperature?: It is mainly to remove gas form chemical reactions in the pug, give full play to plasticity and binding properties of combined, and store unburned?brick whose cememting agent is phosphoric?acid or aluminium?phosphate for some time under proper moisture and temperature. For example, to avoid the formed bricks in the initial stage of drying and firing form cracking due to hydration of calcium oxide. Mixing materials is to store the first mixing materials for some time under proper moisture and temperature in order to improve the evenness and moldability of pud, such as making the distribution of combined clay and water more even. The length of storing chiefly depends on the process requirements and the characteristics of blanks. For the producing pug of high temperature kiln furnitures, the storing time is longer. The function of storing mxing materials varies with different natures of blanks. For honeycomb ceramics, it is to fully digest calcium oxide in blanks. For storing magnesia brick blanks containing much calcium oxide, it should be stored for some time in proper humidity and temperature.

Q: how to classify the fireproofing material levels A1 A2 B1?: their classification is shown specifically in Fireproof? Specification of Building Interior Decoration?Design GB 50222-95 appendix A, flammability,inflammability materials, flame retardency, noninflammability: combustion performance of A, B3, B2, B1 materials are divided into