Low Porosity Fireclay Brick hot sale

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
500000 pc/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information of Fireclay brick

Our corporation produces a comprehensive range of Fireclay bricks, with 30% to 55% alumina content, allof these bricks exhibit excellent performance.

Our Fireclaybricks are the final result of blending excellent fused alumina and silicon asthe main raw materials with cutting-edge technology, adding superfine powder,after mixing, drying, forming, in the high temperature shuttle kiln. We ensureyou that the Fireclay Bricks made by us possess high quality standard and havegone through all the complicated quality control parameters. Their durabilityand strength adds life to the structure and they have the capacity of bearinghigh temperature.

Feature of Fireclay Brick

Resistant tothermal shock, abrasion, chemical attack

High ability foranti-abrasion during work

Low shrinkagedegree under high temperature so as to maintaining integrity of the furnacelining

Low apparentporosity, and low Fe2O3 content to reduce the carbondeposit in the blowhole and avoid the bricks broken in case of expansion

Applications of Fireclay Brick

Fireclay brick is mainlyused in the part of throat, stack, hearth, bottom for blast furnace and thestack for a big blast furnace.

1. Carbon bakedfurnaces in the alumina industry

2. Preheat zonesand cyclones of rotary cement kilns

3. Insulation forglass tanks

4. Coke ovens

5. Blast furnaces

6. Reheatingfurnaces

7. Suspended roofs

8. Lime kilns

9. Chimney

 

       Technical Data of Low Porosity Fireclay Brick

Physical Properties:

Refractoriness

1750

Permanent Linear Change(1450℃×2h)%

%

-0.4~0

Apparent Porosity, %

%

≤18

Cold Crushing Strength

Mpa

≥48

Refractoriness Under Load (T0.6)

1400

Thermal Expansion at 1000℃,  

%

-

Density

g/cm3

≥2.25

Chemical Analysis:

 

 

Al2O3  

%

≥42

Fe2O3

%

1.8

Note:
 Technical Data are typical average results from test pieces. The technical  data is offered solely for your consideration. And we reserve the right to  modify the technical data without any prior notice. Users of our products  should make their own tests to determine the suitability of each product for  their particular purposes.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Are refractory bricks poisonous?
Zirconium minerals are often associated with other minerals in the mining, because the bricks are basically burned under more than 1 thousand degree. But some of the bricks contain heavy metal elements chromium. Some of the brick contains zirconium, the vast majority are very safe, and heavy metal elements have a certain toxicity, there are many kinds of refractory bricks that the nature is very stable, and the associated minerals are generally radioactive
Q:What is the density of the high alumina refractory brick?
it depends on the aluminum content, the higher it contains, the larger the density is. the hjghest is 3, the lowest is 2.
Q:What are the differences between fireclay brick and high alumina refractory brick?
One is the high alumina, solid and hollow respectively, fused mullite as main raw material made of high-grade refractory materials, strong corrosion resistance, has the advantages of through mud treatment, good thermal shock stability. Good resistance to slag, used to build steel making furnace and glass furnace. High alumina brick is a kind of refractory material. Clay brick is also known as sintered brick, electric smelting corundum and low creep high alumina brick [1] with high grade bauxite, this kind of refractory brick's main component is AL2O3, which is suitable for large and small buildings with artificial bulk. High thermal stability. A neutral refractory material with more than 48% of alumina oxide content, clay brick has clay (including shale, molding, coal gangue and other powder) as the main raw materials, cement rotary furnace lining. The product has a small high-temperature creep, one is clay. From bauxite or other high content of aluminium oxide raw materials' forming and firing, refractoriness is above 1770 deg. High R.U.L and medium-sized hot-blast furnace is different firstly in the material, forming from drying and roasting
Q:several refractory brick of rotary kiln several is damaged, how many refractory bricks should be replaced?
The life of refractory bricks in rotary kiln is generally short.
Q:is refractory brick used around the mechanism flue?
Q:How to choose refractory brick
First of all, design the refractory brick size or select the standard size of refractory bricks directly, resist high temperature, and convenient. There are many types of refractory bricks produced by refractory material factory, has heat insulation, so needless to say the country, this work is done by a furnace company . The qualified rate of loading and firing brick and other major production on the process and the final product rate is high, and the brick molding. Too much types of the refractory brick is not easy: is a refractory material factory to accept and use the same brick production models will be more to the degree of refractory brick amazing wide. Whether the furnace design companies or construction companies design certain size refractory bricks, in addition to satisfying the furnace operation and service life.Hiphotos, wear resistance. management and calculation have brought great difficulties, it must also be taken into account that whether refractory bricks produced by the refractory material factory is convenient, low temperature But for intermodulation between refractory bricks factory, redundancy of refractory factories prepare lots of brick mould, this is convenient for operation and construction. A large number of furnace design anticorrosion company design brasque, sometimes work is done by furnace construction company or furnace repair company. if each company that has its own furnace and thermal equipment designs refractory bricks suitable for themselved, it should take into account the general systematic and standard
Q:What is the refractory brick in silicious model?
Adding appropriate amount of mineralized agent to promote the transformation of quartz in the body into phosphorus quartz. Smaller coefficient of thermal expansion. Also used in high temperature bearing part of hot blast stove and acid open hearth furnace, refractory materials and ceramic kiln, kiln vault and other load-bearing parts, thermal shock resistance variation. High temperature strength. the glass furnace is burnt in 1430 to 1350 degrees Celsius in the reducing atmosphere. use natural silica as raw materials. True density 2. more than 93% of silica content. generally there is no crystal type transformation above 600 degrees celsius. With acid slag erosion and sediment chamber regenerator performance, soaking furnace, open hearth furnace. there is more crystal type transformation below 600 degrees celsius. mainly used in coking chamer of coke oven and partition of firebox. acid refractory material made of high thermal shock resistance, large volume change, square quartz and a small amount of residual quartz and glass box . Long term use at high temperature without deformation
Q:What material does tile tunnel kiln use to replace the refractory brick to have better insulation effect and save the maintenance and prolong the service life?
Yes, but the cost is high, refractory material should be the most affordable at present.
Q:Is fireclay brick acidproof? Does clay brick anti corrosion when it's used to build chimney lining?
Refractory bricks anti acid and alkali after high-temperature calcination, and anti-corrosion won't be a problem
Q:Why should the clay bricks be watered first when they are building masonry walls?
And because a portion of the water in the mortar brick absorb, can lead to early dehydration, but are not very good on the hydration of the brick and mortar bond strength weakened, greatly reduce mortar and masonry compressive strength, shear strength, affecting the integrity and seismic performance of masonry.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range