DEAD BURNT MAGNESITE MGO87%

Ref Price:

Loading Port:: Dalian

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 2000 m.t./month

Inquire Now

Chat Online

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Item	MgO	SiO₂	CaO	LOI	B.D.(g/cm³)
DBM-97	97	0.7	1.4	0.2	3.2
DBM-96	96	1.5	1.5	0.2	3.2
DBM-95	95	2.2	1.6	0.3	3.2
DBM-94	94	3	1.6	0.3	3.2
DBM-93	93	3.5	1.6	0.3	3.2
DBM-92	92	4	1.6	0.3	3.18
DBM-92	92	4	1.6	0.3	3.18
DBM-91	91	4.5	1.6	0.3	3.18
DBM-90	90	4.8	2	0.3	3.18
DBM-87	87	7	2.2	0.3	3.2

Our factory produce the products of the Dead-burned magnesite are selected natural magnesite, it is produced by mine-selecting, purifying, calcimine in shaft kiln. It is an ideal material for unshaped refractory material, the final products are used in open hearth furnace, electric furnace bottom and furnace's lining tamping.

Q:What is the material of fire resistant glass reinforced plastics grating?: What is the material of fire resistant glass reinforced plastics grating?

Q:What is fireproofing material? Are fireproof materials the same thing with thermal insulation materials and refractories?: The refractory material is capable of withstanding high temperature burning, while fireproofing material is to prevent burning. They are different from each other

Q:how to divided the external wall thermal insulation materials fire rating: Level A: Incombustible building material: It is a kind of material that almost does not occur burning. Level B1: Nonflammable building material: Non-flame material has good flame resistance. It is difficult to fire under the condition of open fire in the air or high temperature, and it is not easy to quickly spread, and when the combustion?source is removed, the combustion will stop immediately. Level B2: Combustible?building?materials: Flame material has a good flame resistance. In case of fire in the air or at high temperature, it will immediately burst into flames, and easily lead to the spread of fire, such as wooden column, timber roof truss, timber beam and wooden stairs. Level B3: Combustible?building?materials: It has no any flame resisting effects, and is easy to burn, so the fire risk is high.

Q:What is the fireproofing requirements of external wall thermal insulation materials?: External wall thermal insulation materials fire rating regulations, 1, the height of a building is greater than or equal to 100m , the combustion performance of insulation materials should be level A; 2, the height of a building is greater than or equal to 60m but less than 100m, the combustion performance of insulation materials should not be less than the level B2. When using level B2 thermal insulation material, every layer should set horizontal fire barrier zone 3,The height of building is be equal or greater than 24m but less than 60m, the combustion performance of thermal insulation material should not be less than the level B2. When using level B2 insulation material, each two-layer should set fire barrier zone ; 4, the height of building is less than 24m, the combustion performance of insulation materials should not be less than the level B2. Besides, when using level B2 thermal insulation material, each three-layer should set a horizontal fire barrier zone.

Q:who knows how to classify the fire resistant levels of fireproofing material?: Materials used in construction are called construction materials. The combustion performance of construction materials refers to all physic and chemical changes happened when burning or contacting fire, the properity is measured by combustibility of material surface and flame transmission, heating, smoke,charring, weightlessness, and the producing of toxicity resultant. Our national standard GB8624-97 classifies the combustion performance of construction materials into following several levels. Class A: Incombustible building material, class B1: Nonflammable building material, class B2: Combustible?building?materials, class B3: Inflammability construction materials, generally speaking: first fire resistant level construction is the mixed construction of reinforced concrete structure or brick wall and steel concrete structure; second fire resistant level construction is the steel structure roof truss, reinforced concrete column or mixed structure made by brick wall; third fire resistant level construction is the wood and brick made by wooden roof and brick wall; fourth fire resistant level one is the combustible?structure made by wooden roof, hard-comnustible component wall.

Q:Which kind of furnace hearth refractory is better?: hearth selected material] hearth material must be durable, high temperature resistant, general selecting masnory made of refractory cement, silicon carbide refractory products, mullite or multicrystal mullite (which is the general term of minerals composed of a series of aluminum silicate, mullite is only stable binary compound in the Al2O3-SiO2 system) etc.. [hearth] is a three-dimensional space surrounded by furnace walls for combustion of the fuel. The funtion of hearth is to ensure the fuel to burn as far as possible, and to cool the gas temperature of the hearth exit to the allowed temperature of convection heating surface safe operation . Therefore, the hearth should have sufficient space and adequate heating surface. In addition, there should be reasonable shape and size in order to fit the burner and the organize aerodynamic field inside the furnace to prevent the flame from adherence, dashing walls and have high fullness and eve wall thermal load.

Q:How many refractory materials does the annual output of 1 million tons of coke oven require?: The production of dense synthetic Magnesium Oxide requires many steps, briefly summarized as follows:(1) Mgcl2+Ca, Mg (OH) 2, =Mg (OH) 2+CaCl2Sea salt or brine, dolomite, magnesium hydroxide, residual salt(2) Mg (OH) 2 Mg0 (low density);(3) MgO, Mgo (compact)The resulting compact Magnesium Oxide generally has a purity of up to 95%-99%, depending on the manufacturing process and the final application requirements. As shown above, Magnesium Oxide can be obtained from sea water and slaked lime. The density of the final product is through the high temperature roasting in shaft furnace and the large area obtained by calcination, and the mechanical compaction. Through the pre sintered refractory material to fundamentally eliminate the permanent contraction or extension is extremely important, it is obviously, because we cannot expect excessive contraction or extension in the use of the materials can be used to store the proper degree of molten metal or slag. The production of magnesium oxygen throughout the world (Fang Meishi) large factories in the United States, Michigan by brine well production, and by the sea water production Magnesium Oxide factory is located in Florida, Texas, California and Maryland.

Q:Is there anyone who can explain how to grade the level of fire insulation board?: The classification of fire proof level for thermal insulating material 1, Burning performance of building material can be classified into the following several grade according to national standard GB8624-97: Non combustible building materials: Non-conbustible material. Class B1: Refractory building materials: Flame retardant materials have good flame retardant effect.

Q:What are the characteristics of magnesium fireproof plate: Fire Excellence: Glass magnesium plate is non combustible plate having good fire-resisitance quality. Flame will never burn continuously on it. It does not catch on fire when temperature reach 800 ℃, and will not be lit up at 1200 ℃. The plate, having high-quality keel partition system, is rated as the highest non-combustible level A1 with fire resistance being above 3 hours. It absorbs a lot of heat when fire is burning, delaying rise of ambient temperature. Waterproof and moisture proof: Glass magnesium plate functions steadily whenever weather is dry and cold or humid and damp, not influenced by condensed water drop and moist air. Even air dried after soaked in water for a few days, no deformation, it will not go out of shape, turn soft, or absorb moisture After testing, the board has no water permeability. Light weight and seismic resistance: Low overall plate density of 0.8-1.2g/cm3 reduces the building's load, and the weight of building interior wall by over 60%, and increases the use area by 5-8%. Its lightweight is conducive to anti-seismic, can effectively reduce main cost of foundation and structure. Superior strength: Magnesite has special 5.1.8 phase covered fiberglass cloth and good toughness of plant fiber. Altough glass magnesium fireproof plate is light, it has tight structure, good stability, wood-like toughness, outstanding performance in impact resistance, compressive strength, tensile strength equal rigidity and toughness, with flexural strength up to 322kgf\cm2 (vertical) and 216kgf\cm2 (level of) as well as impact strength of 25MPa.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range