Product Description:

Specification of Calcined Bauxite

Item

Al2O3

(min)

Fe2O3

(max)

TiO2

(max)

SiO2

(max)

KO2+NaO2

(min)

CaO+MgO

(min)

Bulk Density(g/cm3)

70

70%

2.5%

2.9min

75

75%

3.0%

4.0%

8%

0.3%

0.6%

2.7min

80

80%

3.0%

4.0%

8%

0.3%

0.6%

2.8min

85

85%

2%

4.0%

8%

0.3%

0.6%

3.0min

86

86%

2%

4.0%

8%

0.3%

0.6%

3.2min

87

87%

2%

4.0%

7%

0.3%

0.6%

3.2min

88

88%

1.8%

4.0%

7%

0.25%

0.6%

3.25min

90

90%

1.8%

4.0%

7%

0.25%

0.6%

3.25min


Packaging & Shipping

In 1MT jumbo bag or as the buyer request.

We ship the cargo in 20' GP containers,each container loads 25MT/20bags.


Application of Calcined Bauxite

1.aluminium industry


2.precision casting


3 refractory materials


4.aluminum silicate refractory fiber for fiber blanket, refractory brick .


5. refractory cement


Bauxite is an aluminium ore and is the main source of aluminium.


Bauxite is used in cement, chemicals, face makeup, soda cans, dishwashers, siding for houses.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Does anyone know the fire endurance of steel stud partition?
The fire endurance degree is 1 hour. which is in line with the national building material fireproofing test standards. CaSo4.2H2O is molecular gypsum molecular structure formula, containing 20% ​​water, crystal water and free water, when putting on fire, 10% of the surface water will slowly evaporate, remaining10% of crystal water. It is a class A fire retardant material itself. The longest time can be 4 hours.
Q:What refractories have good mechanical property resistance and heat expansion and cold contraction property?
Explain that where you use it for and what requirements you have. Follow-up: I use it in metallurgical furnaces with the features of strong stirring and acidic residue.
Q:Where is refractory used? Thank you!
According to its refractoriness, it can be divided into ordinary refractory (1,580℃ to 1,770℃), high class refractory (1,770℃ to 2,000) and super refractory (above 2,000℃); according to chemical property, it can be divided into acid , neutral and alkali refractories, and including refractory used for special occasion. The current definition of refractory do not only depend on whether the refractoriness is above 1,580℃. At present, refractory is widely used as inorganic nonmetallic material of production equipment lining in metallurgy, petrifaction, cement, ceramics, power, etc. Refractory generally has good thermal shock resistance, chemical attack resistance, low thermal conductivity and coefficient of expansion, widely used in chemical, construction material, mechanical manufacturing, and ceramics, accounting for 50% to 60% in the total output. It can resist high-temperature action. Refractory has many varieties. Refractory materials are widely used in metallurgy; chemical properties divided by acidic refractories. In addition, cement, silicates. Refractoriness refers to that when cones sample made from refractory has no load. Currently, refractory refers to that is widely used in metallurgy, including neutral refractory and basic refractory.
Q:What is high alumina refractory?
It refers to inorganic non-metallic material with refractoriness of higher than 1580℃. Refractoriness refers to the celsius temperature that the cone-shaped refractory sample without load can resist, and under which the sample won't soften and melt down. Refractory material appears together with high temperature technology, and roughly dates from the Middle Bronze age. In the Eastern Han Dynasty (AD25~AD220) of China, fireclay refractories has been used as furnace refractories and saggers for making porcelains. In the early 20th century, refractory material develops toward the direction of high purity, high dense and ultra high temperature products, and meanwhile unshaped refractory and refractory fiber with no need of firing at all and with low energy consumption appear.
Q:I would like to ask a friend that how much is the fire endurance of level A fireproofing glass?
the fire endurance of fire window is: class A window is not less than 1.2 hours, class B window is not less than 0.9 hours, Class C window is not less than 0.6 hour. technical requirements: 1, materials and accessories (1) the window frame is made by a certain strength of steel frame or wooden frame which is sufficient to safeguard the integrity and stability. (2) steel frame and mound layer can select galvanized steel sheet or stainless steel plate. Its selection standards should be in line with the provisions of Article 5.1. in GB12955 "Steel Fireproof Door General Technical Condition" (3) the selection standards of wood frame and mound layer should be consistent with the provisions of Article 5.1.1. in GB14101 "General Technical Conditions of Wooden Fireproof Door" (4 ) the inner filling material of steel and wood frame should be non-combustible material. (5) fireproofing glass can choose the qualified products in fire resistance test and not affecting the fire windows. light transmittance of glass is not less than 75% of identical layers of ordinary plate glass. ( 6) a sealing material between the frame and the fireproofing glass should use the nonflammable material, it can play the role of fireproofing and smoke insulation in the fire disaster. I hope I can help you
Q:Who knows the refractoriness of high temperature lightweight firebricks?
pores of high temperature lightweight refractory bricks is made by lightweight aggregate such as combustibles, foaming agent, and hollow sphere production with better thermodynamic stability. Refractoriness reaching 1200 ℃ or more is first grade refractories. fire resistance of building blocks of 100mm thick can reach 225 minutes, 200mm thick brick 480 minutes.
Q:Who knows that among refractory materials, insulation boards from which refractory material industry is superior in quality?
When casting ingot, after high temperature molten steel is poured into ingot mold, molten steel keeps shrinking during cooling, for example, killed steel is shrinking 3% --5%. because of fast heat dissipation of ingot head , some shrinkage holes appear at the head of ingot. Therefore, you should cut shrinkage holes which account for more than 15% of the ingot quality in the head while cutting steel ingot cogging. If effective measures were taken to insulate the head of ingot from heat, then the coagulation time of ingot head would lag behind in the body of the ingot solidification, which will greatly shrinkage holes, improve ingot yield so as to reduce energy consumption of steelmaking. Adiabatic plate can achieve this purpose. China Heng insulation board has the advantages of uplifting adiabaticity and small heat capacity, so that it greatly reduced heat loss of molten steel, And the tundish can be directly put into use without preheating, thereby saving a large amount of preheating fuel. So in the current process of continuous casting, the heat insulation board is the main material of tundish lining.
Q:Technical scheme of refractory for refuse incinerator
Incinerator conditions and requirements for refractory lining1, working conditions: deal with rare earth, furnace body normal use temperature of 800~900 degrees.2, the specific requirement for refractory: refractory has good resistance to acid corrosion, thermal shock performance good stability and good high temperature.
Q:What are the use of fire-resistant material and admixture?
Generally speaking, there are several admixtures: 1. Water reducing agent. It can ensure basic refractory castable flow value and significantly reduce its water mixing amount sodium hexametaphosphate and sodium tripolyphosphate 2. Plasticizer. It can increase plastic refractory mixture and enhance the ability of bentonite clay mud material stress strain 3. Gelling agent. It can make the colloidal solution (or suspending liquid containing solid particles condensed gelling agent 4. Dispergator. It can turn condensation or reunion colloidal particles (particles) into sol or uniform dispersion suspended particles and make the thick colloid free stream sol said scattered coagulant peptizer 5. Coagulant. It can shorten the stereotypes refractories condense sclerosis NaOH Mars between aluminum hydroxide, etc. 6. Retarder. It can delay the stereotypes refractories condense sclerosis between citric acid tartaric acid, etc. 7. Delayed coagulant. It can make setting fire-resistant materials contain binder by set out the condensation hardening effect between calcium aluminate cement, etc. 8. Foaming agent. It can reduce the liquid surface of power to produce uniform stability as rosin soap bubble resin fat saponin and so on. 9. Antifoaming agent. It can make fast setting fire-resistant material mixing or shock in produce bubbles escape alcohol fatty acids, such as 10. Shrink agent can reduce or prevent the refractory materials used to produce contraction type heating said silicon powder stabilizer or volume expansion agent, etc. 11. Preservative. It can keep setting fire-resistant material stored on construction performance change or change oxalic acid citric acid, etc. 12. Inhibitors. It can inhibit stereotypes refractories ingredients contain iron or iron compounds and acidic reaction caused inflation to produce hydrogen bond CrO3 diacetone alcohol, etc. I hope it can help you.
Q:which kind of fire bulkhead is better?
General business fire endurance of two products are 3 hours. Organic fire bulkhead's main ingredient is organic material, which can be used in anti-corrosion and fireproofing cable tray. Inorganic fire bulkhead's main ingredient is inorganic material, which mianly play a role of fireproofing. It's main ingredient is inorganic material, so it can't be used in acidproof and alkali resistant projects. Of course, the price of same amount organic fire bulkhead in general is more expensive than the inorganic fire bulkhead.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range