1.High refractoriness:2000 ,
2.excellent anti-oxidation,
3.high strength,50 Mpa
4.perfect thermal Stability

Magnesia carbon Brick for converter melt line

Manufacture:

1.Use the high-purity graphite as bone materials;

2. Make the phenolic resin as the binder, add variety of additives

3. To form by high-pressure and then dry under high temperature.

Product features:

1. High refractoriness, excellent anti-oxidation, high strength, perfect thermal

Stability;

2. Resist the erosion and spall, high abrasion- resistance strength ,

3. Difficult to oxidation and hydration,

4. can be used for long time.

Product application:

Used for the melt line of the converter .

Index:

Grade		MgO (%)	C (%)	Ap (%)	B D(g/cm3)	C CS(MPa)	Hot temperature bending strength(MPa)≥1400°C 30mm
RGMT-14	A	≥78	≥ 14	≤4	≥2.95	≥40	≥12
	B	≥77	≥14	≤5	≥2.94	≥40	≥8
	C	≥77	≥14	≤5	≥2.92	≥35	≥6

Q:Application of electric high temperature regulating valve?: Magnesia brick has good resistance to alkaline slag and slag, refractory clay brick and brick high ratio. Mainly used in open hearth furnace, oxygen converter, electric furnace, non-ferrous metal smelting equipment and glass industry as well as some high temperature equipment. Magnesia chrome brick more resistant to alkaline slag, and thermal shock stability are much higher than the more widely used, magnesia, magnesia chrome bricks in iron and steel smelting and non-ferrous metal smelting industry has almost replaced the brick, chrome oxide containing (Cr2O3) can be spread, the magnesium chromium brick can easily sticking kiln the skin, so in the past 30 years, has been used with refractory preferred cement kiln, magnesia chrome brick in Cr2O3 water after the reaction of trivalent chromium into six chromium can cause the pollution on the water, facing gradually out of the cement industry market trends. Magnesia and magnesia alumina brick using alumina as raw materials, a magnesia brick compared to thermal shock resistance and high temperature creep performance, use parts and magnesia brick is almost the same. Dolomite brick and magnesia calcium brick performance is almost the same, dolomite brick using dolomite as raw material, calcium magnesium brick with synthetic calcium magnesium sand as raw materials, calcium oxide content in 15-30%, the other is the main component of Magnesium Oxide, with the function of purifying molten steel, usually only used for special steel smelting, the production process of magnesia calcium brick complex water and water steam, easy decomposition, not easy to save transportation, do preventive work must be used in the process of. Magnesia spinel brick is a kind of new products, mainly for the zone and transition zone of cement rotary kiln, will be the main products of the cement industry to replace magnesia chrome brick.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range