Ball Mill Chromium Alloyed Grinding Ball made in China with Top Quality and Highest Hardness

Ref Price:
Loading Port:
Qingdao
Payment Terms:
TT or LC
Min Order Qty:
25M.T. m.t.
Supply Capability:
200000M.T./Year m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

1. Feature of Ball Mill Chromium Alloyed Grinding Ball made in China with Top Quality and Highest Hardness

1) In general, grinding steel ball has high hardness: surface hardness to 58-65 HRC, volume hardness of 56-65 HRC 

2) impact toughness high: impact toughness more than 12 J / cm2. 

3) broken rate is low: the actual broken rate is not higher than 0.5%. 

4) loss of grinding forged steel ball round rate is low. 

 

2. Index analysis of Ball Mill Chromium Alloyed Grinding Ball made in China with Top Quality and Highest Hardness

Product

Brand

DIA

hardness

Breakage ratio of ball

Impact fatigue life of ball

Numbers time

Metallographic organization

Special high chrome casting iron ball

Cr26

15-150MM

58

0.5%

6

15000

M+C

Special high chrome casting iron ball

Cr20

15-150MM

58

0.5%

6

15000

M+C

Special high chrome casting iron ball

Cr15

15-150MM

58

0.5%

5

15000

M+C

High chrome casting iron ball

Cr12

15-150MM

58

0.5%

4

15000

M+C

High chrome casting iron ball

Cr8

15-150MM

58

0.5%

3

15000

M+C

Middle chrome casting iron ball

Cr5

15-150MM

47

0.5%

2

12000

P+C

Low chrome casting iron ball

Cr2

15-150MM

45

0.5%

1

12000

P+C

Casting ball

QTB

15-150MM

50

0.5%

-

12000

-

Casting ball

QTM

15-150MM

52

0.5%

-

12000

-

 

3. Chemical Composition of Ball Mill Chromium Alloyed Grinding Ball made in China with Top Quality and Highest Hardness

Product

Brand

Chemical composition(%)

C

Si

Mn

Cr

Mo

Cu

Ni

P

S

Special high chrome casting iron ball

Cr26

2.0-3.3

1.2

0.3-1.5

>23.0-30.0

0-3.0

0-1.2

0-1.5

0.10

0.06

Special high chrome casting iron ball

Cr20

2.0-3.3

1.2

0.3-1.5

>18.0-23.0

0-3.0

0-1.2

0-1.5

0.10

0.06

Special high chrome casting iron ball

Cr15

2.0-3.3

1.2

0.3-1.5

>14.0-18.0

0-3.0

0-1.2

0-1.5

0.10

0.06

High chrome casting iron ball

Cr12

2.0-3.3

1.2

0.3-1.5

>10.0-14.0

0-3.0

0-1.2

0-1.5

0.10

0.06

High chrome casting iron ball

Cr8

2.1-3.3

2.2

0.3-1.5

7.0-10.0

0-1.0

0-0.8

-

0.10

0.06

Middle chrome casting iron ball

Cr5

2.1-3.3

1.5

0.3-1.5

4.0-6.0

0-1.0

0-0.8

-

0.10

0.10

Low chrome casting iron ball

Cr2

2.1-3.6

1.5

0.3-1.5

1.0-3.0

0-1.0

0-0.8

-

0.10

0.10

Casting ball

QTB

3.2-3.8

2.0-3.5

2.0-3.0

-

-

-

-

0.10

0.03

Casting ball

QTM

3.2-3.8

2.0-3.5

2.0-3.0

-

-

-

-

0.10

0.03

 

 

 

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Casting pieces of plastic processing requirements can not fall off the skin,
Steel parts are not familiar. But after spraying, the powder should be divorced from the adhesive force is too low, try to provide the surface roughness of the casting
Q:How much is the casting allowance in the design of the casting machine and the drawing?
Casting parts do not need to provide drawings of casting blank, the casting factory according to your drawings in the required surface will be sufficient allowance, and the rest of the size according to the mechanical design manual and the casting manual can be found.
Q:What's the effect of casting copper?
In general cast iron, the mass fraction of copper below 3% - 3.5% can increase the hardness; but when the cast iron has a tendency to chill, or when there is a hard point of free carbides, the addition of copper decreases the hardness.Copper can be used to improve the wear resistance, abrasion resistance, and shock absorption of cast iron, so it is often used in the manufacture of sliding friction iron castings, such as drilling machine spindle, automobile and tractor, valve tappet, etc.. But in white cast iron or chilled cast iron, adding copper does not make any improvement in its abrasion resistance.Copper for certain heat resistant cast iron and austenitic cast iron can increase the heat resistance and corrosion resistance, copper - chromium composite alloy to prevent oxidation under high temperature in the atmosphere from the skin effect is particularly effective, heat resistance and corrosion resistance of austenitic cast iron containing many mass fraction of 4% ~ 7% copper.
Q:What should I pay attention to when designing a casting structure?
The basic structure of unit 3 in the design of metal casting casting and its parameters are selected, usually should also pay attention to: (1) because of the metal type heat quickly, so the metal type casting minimum wall thickness should be bigger than the sand casting casting casting; (2) the inner wall of the internal ribs and the thickness of a should be connected the outer wall thickness of 0.6 to 0.7, or as the inner wall (rib) cold slowly, cracks in the wall at the junction in the casting shrinkage; (3) to prevent generating white grey cast iron, in addition to taking measures in the process, must make the wall thickness is not too thin (some information that cast fillet at the corner of the wall thickness of 15mm or more, with metal casting casting must be in the corner, for Aluminum Alloy, metal casting magnesium alloy castings shall not be less than 3 ~ 4m; (4) because of the metal type and the core that, for To facilitate the extraction of castings and casting out type, slope casting should be suitably large than sand casting metal casting, the general should be 30% ~ 50%, it should be pointed out that in addition to the height of the slope of casting size and alloy type, wall, is also related to the casting surface position, where the cooling and contraction of the metal type the surface of casting surface can be designed from the tendency of small inclination, while casting shrinkage tend to be pressed on the surface of metal casting type should be given greater inclination.
Q:How to get rid of casting sand inside casting parts?
Are you saying that in the sand casting cavity? We use the manual blast, he is like a pipe will be automatic shot out of the grit, into the casting cavity, to remove the internal cavity in the purpose of casting sand!
Q:Casting parts in rocker arm drilling, reaming, roughness, block.
Radial drilling machine can achieve boring, reaming function, but as much as you want, according to your requirements and material to determine!
Q:The casting sand is going on
3, prevention measures(1) to improve the strength of sand mold (core), especially surface strength, high temperature strength, refractoriness, compact, better coating, good core coating and parting surface coating.(2) mould and box can prevent damage;(3) the core should have clearance.
Q:What is the reason for 304 stainless steel precision casting parts to be changed?
304 stainless steel is easier to change than ordinary steel. Because the 304 heat conductivity is lower than that of the low doped steel, the temperature is even more uneven, and 20% of the non ferrous elements also make the distribution of internal and external elements more uneven, hard and soft inside. Each of these two produces greater internal stresses, resulting in a variant.
Q:What is the difference between casting and stamping parts?
Cold stamping is generally no longer done by cutting, or only a small amount of cutting is required. The precision and surface state of hot stamping parts are lower than those of cold stamping parts, but they are better than those of castings and forgings, and the amount of cutting is less.Stamping is mainly based on process classification, can be divided into separation process and forming process two major categories.
Q:What are the factors affecting the machining process of the casting material and structure?
Medium carbon steel begins, and the casting can not be punched and tapped directlyStainless steel, ordinary grade (Fe based alloy element content, less) can not do heat treatment. But processing small holes or tapping to heat treatment (solution. In practice, the annealing treatment can also be). There are a lot of stainless steel matrix is not to say, for example, nickel, cobalt and tungsten. And so on.
CMD is one of the largest manufacturers and professional exporters of forged grinding balls and cast grinding balls in China, with an annual output of 50,000 tons. Now, there are 180 employees in our company, with an area of 20,000 square meters. Our products are mainly exported to more than 20 countries in the world, such as Africa, South America, Asia, and Australia. 

1. Manufacturer Overview

Location Shandong, China
Year Established 1983
Annual Output Value Above US$100 Million
Main Markets South Asia, South Asia, Central America, Western Europe, Eastern Asia, Mid East, Oceania, Africa
Company Certifications ISO9001;IS014001 Certificate

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port Qingdao Port
Export Percentage
No.of Employees in Trade Department 3-5 People
Language Spoken: English;Chinese;Japanese;Korean
b)Factory Information  
Factory Size: Above 20,000 square meters
No. of Production Lines 8
Contract Manufacturing Grinding steel balls;Grinding steel cylpebs;Grinding media;Grinding meida ball