High Alumina Brick with Al2O3 content 55-60%

Ref Price:
Loading Port:
Qingdao
Payment Terms:
TT OR LC
Min Order Qty:
17 m.t
Supply Capability:
10000 m.t/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information
CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

Feature
Low thermal conductivity   
Excellent acid and base slagging resistance
High refractoriness    
Excellent thermal shock resistance    
Excellent mechanical strength

Application
CMAX high alumina bricks are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc

 

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,%

1450x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h       0.1-0.4

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

Al2O3 Content , %

48

55

65

75

80

85

82

 

 High Alumina Brick with Al2O3 content 55-60%

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What kind of refractory brick is suitable for 24*28m rotary kiln of 5,000 tons?
Magnesia spinel brick and magnesia hercynite brick
Q:Is the thickness of the kiln lining and the refractory brick the same concept?
This is certainly not the same. The thickness of the refractory brick can be arbitrary, the thickness of the kiln lining is generally designed according to requirement
Q:does furnace use refractory cement to make refractory bricks?
consistence Mainly concern about the strength, generally masonry mortar does not consider the degree of fire resistance
Q:Can refractory bricks be used to pave roads or build a wall?
Refractory bricks are used to build a house, no problem
Q:Why can't build refractory brick behind the skew block?
refractory is heat expansion and cold contraction, it is also called refractory brick, can resist high temperature up to 580-770 degrees. Mainly used for the smelting furnace. faint yellow or brown, when it is high temperature, it will squeeze toward the center. Refractory material made of refractory clay or other refractory raw materials. the shortened form of fefractory brick is brick. vault will be extrusion deformation. Refractory material with a certain shape and size
Q:What is light brick and what are the characteristics of light brick?
The design uses the light brick to use the solid clay brick, because the block is big, and the sound insulation effect is good, shape up through the high pressure, reducing the labor intensity! Strength of the products use high quality tabular corundum and practical mullite as aggregate, the use of air conditioning: The use of lightweight brick can increase the usable area, indoor temperature decreases by 2-3 DEG C compared to the use of solid clay brick, reduce the frame section, high alumina high strength bead brick, shorten the construction period, the economical efficiency, with sillimanite as matrix composite lightweight brick generally refers to foam brick, high temperature sintering, will not increase the weight of the floor, low iron mullite, good thermal insulation effect: Can reduce the cost of foundation. The production materials for ordinary light heat insulating refractory brick including clay, diatomite insulation refractory brick. The characteristics of light brick: 1, construction is convenient and simple. 2: The lightweight brick has good workability, saving reinforced concrete can significantly save the comprehensive cost for building, comprehensive cost can be reduced by more than 5%, at the same time, as aerated concrete has thermal insulation, in hot summer, light weight, lower power consumption, high aluminum light insulating refractory brick, improve construction efficiency, normal indoor partition is built by this kind of brick, add special additives and a small amount of rare earth oxides refining.
Q:Whether fireclay raw materials or clinker are used when masonrying general fireclay brick? What is the difference between raw material and clinker?
Generally, refractory bricks use clay refractory mortar, raw material and clinker are halves
Q:Do refractory bricks insulate heat?
The light brick inside the brick is heat insulation brick, according to the different bulk density, the effect is also different
Q:th choose of different refractory bricks in the rotary kiln
According to the characteristics of each belt, magnesium chromium brick. Take the most kiln foe example, the configuration of kiln refractory is not the same, the burning of the product is not the same. there are many kinds of rotary kiln. magnesia bricks are generally used in high temperature zone, anti-stripping alumina brick,silmo brick are used in temperate zone, clay brick is mainly used in low temperature zone. generally inlet and the outlet use corundum mullite, wear-resistant castable, spinel brick,etc. select brick of proper performance, but also take into account the economy
Q:Whether the cement kiln refractory bricks belong to hazardous waste or not?
Refractory brick produce dust hazards if it is broken, It is also should be paid attention to that if is refractory brick containing chromium, which will easily produce Cr VI when met with water, Cr^6+ material produced by magnesia chrome bricks is difficult to be damaged in the environment, which in many cases will exist in nature for a long time, continue to endanger human health. Chromite, as the raw materials to make magnesia-chrome brick, often exists in the form of trivalence (Cr203), is not toxic, nor carcinogenic, but in the cement rotary kiln high temperature oxidation atmosphere, it reacts with alkali metal oxide in cement materials, will produce chromic acid and alkali acid which is harmful to people's health. There are MgOIn contained in broken magnesia-chrome bricks, whose water solution is weakly alkalinity and generally will not easily produce K2cr207. K2Cr04 is a kind of weak oxidaiblity chemical compound, which has high chemical stability. It is very difficult to be reverted to non-toxic trivalent chromium when it blends into the environment. In many cases, these chemical compounds containing Cr VIcompounds will exist in nature stably, causing long-term pollution to the environment. This kind of harm is sustainable. The second reason that is very serious is that the high grade chrome ore is less and less in the world, forcing refractory manufacturers to find and develop

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range