Product Description:

General Information
CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

Feature
Low thermal conductivity   
Excellent acid and base slagging resistance
High refractoriness    
Excellent thermal shock resistance    
Excellent mechanical strength

Application
CMAX high alumina bricks are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc

 

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,%

1450x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h       0.1-0.4

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

Al2O3 Content , %

48

55

65

75

80

85

82

 

 

Composite Brick with Al2O3 content 55-60%

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Tunnel kiln firing refractory brick by 0 against the good rely on
Modern advanced kiln has high temperature strength and good thermal shock resistance, better environmental protection, is the most economical and efficient kiln. (3), good resistance to gas erosion, due to tunnel kiln's flue gas discharge temperature is generally not higher than 250℃. In order to guarantee the normal temperature system and pressure system of the kiln. Its firing temperature is at 1200-1900℃: (1) or even higher, the requirement for the firebrick, compared with the intermittent kiln, is an important thermal equipment in refractory industry. It is a kind of energy-saving kiln. Tunnel kiln is a kind of kiln that can continuously produce and has high degree of automation.
Q:What types of refractory bricks are divided into?
middle rank。 A refractory is stronger than B refractory, low rank, the other is refractory, the senior is AB. Shale is hollow, it is not refractory, refractory, advanced, refractory B, there are nonfireproof materials in intermediate and low rank. Three types of refractory A
Q:Where the refractory bricks rider bricks that are used for building arch and vault should be put?
Arch and vault shall be built simultaneously from both sides of the arch of the foot to the center of symmetry, when masonry, inverting concentric reducer of arch brick is prohibited; the lock should be driven into the brick arch from the side, if the last rider brick can't be driven from the side, you can process the first 1-2 brick to make the size of the lock and the lock buckle equal, and then drive suitable rider brick from top, and use steel plate to jam-pack the side; dismantling arch tire must be performed after all rider bricks are driven and lock brick arch foot ditch masonry is completed and the final tightening nut for skeleton retractor rear.
Q:Is there any special requirements for the building blocks of the smoke and gas wells, how about the refractory bricks?
There are no special requirements. Not necessarily need refractory bricks, red bricks are ok. The building size of the flue is according to the smoke exhaust rate.
Q:Is the quality of refractory brick influenced if it is soaked by water
No refractory brick is not afraid of water
Q:What is refractory brick? What is refractory clay? ?
Refractory brick is a kind of brick that is fireproof, refractory soil is the soil that is fireproof
Q:What are the reasons for the production of waste in the formation of fireclay bricks?
The reasons for the production of waste when form fireclay bricks: Tile size is unqualified. This is due to the mold installation is not firm, the template transfers when molding; if the amount of material being added fluctuates largely, also can cause the body size changing. Ji Yangon Chi lie charge generation layer containing decyl poke pull and crack. The molding operation does not according to the principle of the light first and the thick later. At the initial pressure, the air doesn't releases, which causes the elastic aftereffect by repressing. Too much mud water, uneven mixture and inequal template all can make the body produce layer crack or crack. Twist. The template is used for too long, the template deforms, so raw brick deforms, the amount of water is too large, brick naturally deforms, causing the body twist. Miss edge and angle. Because of poor plasticity of mud, particles segregate, feeding back corner is not real, the body will appear side missing and angle modulation phenomenon. Bias voltage. Due to the deflection of the die head or the uneveness of mold bottom. Loose。 Due to insufficient feeding amount or insufficient pressure times.
Q:How to use the firebrick to build crucible furnace? How to calculate its furnace's width and depth?
1, classify according to the smelting method : Open-hearth furnace steel: Including carbon and low-alloy steel. According to the different lining material, there are acidic and basic open hearth steel two types. Converter steel: Including carbon and low-alloy steel. According to different positions of blowing oxygen, there are bottom blowing, side blowing and BOF steel three types. Electric furnace steel: Mainly alloy steel. According to the different types of electric furnace and electric arc nail fixed Li modified cool boat to raise spending whale steel, induction furnace...
Q:Why are the refractory bricks near to rotary kiln tyre easy to be short lives?
Q:What is the meaning of special shaped refractory brick material n-2b?
In fact, there are many kinds of refractory bricks, titanium, high alumina refractory brick, after drying. The mineral composition of the clay brick is mainly kaolinite (Al2O3·2SiO2·2H2O) and 6% ~ 7% impurities (K, etc.). Clay refractory bricks are iron oxide sintered by 50% soft clay and 50% hard clay clinker ingredients according to a certain granularity requirements under the high temperature of 1300 ~ 1400 degrees), perlite

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range