Refactory Silica Brick for Hot Blast Stove

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
15 m.t.
Supply Capability:
30000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information
CMAX silica brick is a kind of acid refractory product which is mainly made of tridymite and cristobalite, and a small amount of quartz and vitreous. CMAX Silica bricks are made from high quality quartz tail sand, lime and mineralizing agent through the process of crashing, screening, mixing, pressing, drying and sintering.

 
Application

Coke oven

Hot blast stoves

Glass furnace

Features
High refractoriness under load
High mechanical strength
Excellent thermal shock resistance
Corrosion resistance.

Low thermal and chemical expansion


Technical Data

  ITEM

For Hot-Blast Stoves

                   For Glass Furnace

  S-94

S-95

  S-95B

  G-94

  G-95A

  G-95B

  G-96A

  G-96B

  SiO2, %

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 96

  ≥ 96

  Fe2O3, %

  ≤ 1.5

  ≤ 0.5

  ≤ 1

  ≤ 1.5

  ≤ 1.2

  ≤ 1.2

  ≤ 0.8

  ≤ 1

  Residual Quartz, %

  ≤ 1

  ≤ 1

  ≤ 1

  ≤ 1

  Apparent Porosity

  ≤ 23

  ≤ 23(24)

  ≤ 21(23)

  ≤ 24

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  True Density, g/cm 3

≤ 2.35

  ≤ 2.34

  ≤ 2.33

  ≤ 2.35

  ≤ 2.35

  ≤ 2.34

  ≤ 2.34

  Cold Crushing Strength, Mpa

  ≥ 29.4

  ≥ 30(27)

  ≥ 30(20)

  ≥ 30

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  Refractoriness Under Load, º C

  ≥ 1650

  ≥ 1600

≥ 1630 

  ≥ 1660

  ≥ 1650

  ≥ 1680

  ≥ 1670

  Permanent Linear Change, %

  1500º CX4h, ± 0.2

  1450º CX2h, ± 0.5

Refactory Silica Brick for Hot Blast Stove

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are the materials for refractory materials? What are their names?
The main raw material is the main body of refractory. Auxiliary raw materials can be divided into binders and additives. The role of bonding agent is to make the refractory body in the production and use process has enough strength. There are commonly used lignin, phenolic resin, asphalt, cement, water glass, phosphoric acid and phosphate, sulfate, some main raw material itself has the effect of binder, such as clay; additive is to improve the production of refractory materials and construction technology, or strengthen the refractory material of some properties, such as stabilizer, water reducing agent, inhibitor, plasticizer, foaming agent, dispersing agent, bulking agent, antioxidant.
Q:The brick is mainly used in the place?
Open hearth furnace regenerator and a sediment chamber, soaking furnace, glass furnace refractory materials and ceramic brick kiln, kiln vault and other load-bearing parts.
Q:What is acid refractory?
Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.
Q:Why is the new trend of the high thermal conductivity of silica brick
The use of high thermal conductivity of silica brick, reducing coke fuel consumption, reduce emissions of pollutants such as NOx, with considerable economic benefits and social benefits, is the future direction of the new technology of using coke oven refractory.
Q:Can not use it two brick
The softening temperature is up to 1640~1670 DEG C, and the volume is stable at high temperature for a long time.
Q:The introduction of silica brick
Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature.
Q:The difference between clay refractory bricks and refractory brick in the application.
Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.
Q:Can iron oxide be used as refractory material?
Is widely used in this area. Mentioned refractory material of high school textbooks generally refers to three two aluminum oxide (alumina), alumina is also used as a refractory material, refractory crucible, porcelain, artificial gemstones.
Q:The introduction of silica brick?
An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.
Q:Semisilica brick, clay brick, high alumina brick and what is the difference?
The share of A12O3 and SiO2 is different

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range