Specifications

Refractory Cement
high alumia refractory
1.Quick hardening and early strengthening
2.Good quality with competitive price

High Alumina Refractory Cement

Product Description

Applications

1.Used as building refractory cement.

2.Furnaces lining material of metallurgy industry, heat treatment furnace.

3.Furnace lining material of incineration of garbage, recirculating fluidized bed furnace.

4.Furnaces lining material of chemical industry and construction industry.

Typical Features:

1.Low thermal conductivity, excellent thermal insulation, low liner shrinkage.

2.Good integrity with furnace lining, long service life, easy operation, could be shaped freely.

3.Allow direct contact of fire, suitable for various atmosphere.

4.High strength and good thermal shock resistance.

Specifications:

Item		Unit	75% Alumina Index	40% Alumina Index
Al₂O₃		%	≥75	≥40
CaO		%	≥2.5
Bulk density	110°C×24h	g/cm³	≥2.65	≥2.3
Bulk density	1100°C×3h	g/cm³	≥2.65	≥2.3
Crushing strength	110°C×24h	Mpa	≥45	≥40
Crushing strength	1500°C×3h	Mpa	≥70	≥60
Rupture strength	110°C×24h	Mpa	≥6	≥6
Rupture strength	1500°C×3h	Mpa	≥10	≥8
Linear change rate at 1100°C		%	-0.1~-0.5	±0.5
Highest Application Temperature		°C	1500	1350

FACTORY:

$High Alumina Refractory Cement$

Q: What kind of fireproof material is used for steel structure?: Fireproof material means the coating is with thickness 3 mm (including 3 mm) or less, good decorative effect, capable of expanding foam, fire endurance of generally within 2 h of steel structure fire at high temperatures. fire-resistant coating for steel structure is generally solvent-based systems, with strong bond strength, water resistance, weatherproof, good flowing property, decorative; it slowly expanded at high temperature to a dense layer of fire insulation, which has a strong refractory shock, delaying the rise of steel, protecting steel components. ultra-thin?intumescent?fireproof coatings?for steel?structure can be used by spraying, brushing or rolling, generally using construction steel with fire endurance within 2 h. new type of ultra-thin fireproof coatings for steel structure has a fire endurance of 2 hours or more, mainly using binding agents of polymethacrylate or epoxy resin and amino?resin and chlorinated?paraffin, which are of special structure, added with fire retardant system such as high degrees of polymerization, phosphoric?acid, dipentaerythritol, adding titanium dioxide, wollastonite and other inorganic refractory materials, solvent oil 200 # solvent composite. All kinds of light steel structure, grid and other use of this type of fire-resistant coating conduct fire protection. As such the fire retardant paint coating is ultra-thin, greatly reducing the amount of thin steel structure fire retardant coating, thereby decreasing the total cost of the project. The steel is protected and the fire is prevented.

Q: Which kind of external wall fire barrier zone material is better?: I recommended foam cement and particulate thermal insulation composite waterproof material, which is fire isolation area product, which uses surface of vertical?plate arranged fiber technology to make the compressive?strength in the vertical direction up to above 80KPa. At the same time, under the conditions of both exterior heat insulation and effects of humiture in the long-term, it can still maintain the non-aging performance of various aspects, and safety (reliability), fire resistance and excellent durability.

Q: What is the interior fireproof thermal insulation material?: polystyrene foam board, glass fiber spraying, polyurethane foam, thermal insulation system of inorganic wall. Use "DY" inorganic active thermal insulation material, have small thermal conductivity, large heat storage coefficient, better strength and achieve better thermal insulation and energy-saving effect when used in wall . Wall should definitely not crack and hollow because of high temperature in summer. It doesn't crack and shed because it is influenced by stress during heat expansion and cold contraction in cold winter.

Q: What thickness is needed of the ultra-thin fireproof paint with a fireproof time of 2.5 hours?: Fireproof of steel components can adopt outsourcing concrete (or laying bricks method), fireproof coatings, fire prevention board coated and composite structure. Anti-firing plate can be divided into the fire protection lamella thickness plate and thin plate. Fire protection lamella thickness plate is of 20 ~ 50 mm. There are mainly calcium silicate and decayed stone of fire prevention board fire board, main varieties KB board, CF board; Fire sheet thickness is between 6 to 15 mm and the main varieties have short fiber reinforced cement pressure plate, fiber reinforced ordinary calcium silicate board and glass cloth reinforced inorganic plate. I hope you can be satisfied.

Q: What does refractory mean?: Acid refractory material usually refers to refractories with SiO2 content greater than 93%. Its main characteristic is that it can resist acid slag corrosion at high temperature, but it is easy to react with alkaline slag.

Q: What is the difference between the fire?rating and the fire resistant level of the fire-fighting equipment?: Hello there. Fire rating and fire-fighting rating are the misnomer to the building fire resistant level. The building fire risk is measured by fire resistant level. The article 3.2.1 and 5.1.7 of "Architectural design code for fire protection" have made provision respectively on the fire resistant level of plant (the storeroom) and civil construction. Article 3.0.2 of "Code for fire protection design of tall buildings" has made provisions on the fire resistant level of tall buildings. As for the warehouse building "category malonate", it refers to one of the fire risk of goods storage, which is divided into A, B, C, D, E, and each category is refined depending on the nature of different substances. "Malonate class" specified in article 3.1.3 of "building design for fire protection" refers to the flammable solid.

Q: What is refractory cement?: Refractory cement is also known as aluminate cement, whose major mineral are monocalcium aluminate (CaO · Al2O3, abbreviated CA) and other aluminate as well as a small amount of dicalcium silicate (2CaO · SiO2), etc. The advantage is that it is easy to use, able to harden if mixed with added water without other binding agent usually. Refractory aggregate and powder can be added into it. If you use refractory cement purely, it will produce a lot of cracks after high temperature.

Q: What's the fire resistance rating of the exterior fire?retardant?coating?: Exterior thick fire-resistant coating for steel structure can reach the first level of fire resistance, thin fire-resistant coating for steel structure can be fire-resistant for three hours, and ultra-thin fire-resistant coating for steel structure can just be within the second level of fire resistance.

Q: What can red stone refractory do?: In severe cases, the resistance to high temperature without softening down the Celsius temperature. Refractory materials are widely used in metallurgy, chemical, petroleum, machinery manufacturing, silicate, power and other industrial fields, the largest amount of metallurgical industry, accounting for 50% ~ 60% of the total output. Chinese use less impurity clay in more than 4000 years ago, firing pottery, and have been able to cast bronze. In the Eastern Han Dynasty (AD 25 ~ 220) have been used to make clay refractory kiln firing porcelain material and sagger. At the beginning of twentieth Century, the development of refractories to high purity, high density and ultra high temperature products, while developing completely without firing, small consumption of unshaped refractory materials and high refractory fiber (160 for industrial furnace refractories above 0 DEG C). The former, such as alumina refractory concrete, is often used in large chemical plants, ammonia synthesis plant, two - stage reformer furnace wall, the effect is good. Since 50s, the rapid development of atomic energy and space technology, the development of new energy technology, requires the use of special refractory material of high temperature resistance, corrosion resistance, thermal shock resistance, erosion has excellent properties, such as melting point above 2000 DEG C, oxide refractory compounds and high temperature composite refractory materials.