Product Description:

High Alumina Refractory Brick For Blast Furnace 


Specifications

Fire brick 
1.ISO 9001 approved, 
2.With high quality and competitive price, 
3.Standard and special shape.

Fire-clay refractory brick.
1. N-1
AL2O3 (%)>42
Refractoriness >1750
Refractoriness under load KD>1400
Permanent linear change onreheating
1500*2h
1450*2h
1400*2h:+0.1; -0.4 
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>29.4

2. N-2a
AL2O3 (%)>40
Refractoriness >1730
Refractoriness under load KD>1350
Permanent linear change onreheating
1500*2h
1450*2h
1400*2h:+0.1; -0.5 
Apparent Porosity(%)<24
Cold crushing strength (Mpa)>24.5

High-alumina refractory brick
1. LZ-75
AL2O3 (%)>75
Refractoriness>1790
Refractoriness under load KD>1520
Permanent linear change onreheating
1500*2h:+0.1; -0.4 
1450*2h
1400*2h
Apparent Porosity(%)<23
Cold crushing strength (Mpa)>53.9

2. LZ-65
AL2O3 (%)>65
Refractoriness >1790
Refractoriness under load KD>1500
Permanent linear change onreheating
1500*2h:+0.1; -0.4 
1450*2h
1400*2h
Apparent Porosity(%)<23
Cold crushing strength (Mpa)>49

3.LZ-55
AL2O3 (%)>55
Refractoriness >1770
Refractoriness under load KD>1470
Permanent linear change onreheating
1500*2h:+0.1; -0.4
1450*2h
1400*2h 
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>44.1

4.LZ-48
AL2O3 (%)>48
Refractoriness >1750
Refractoriness under load KD>1420
Permanent linear change onreheating
1500*2h
1450*2h:+0.1; -0.4
1400*2h 
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>39.2


High Alumina Refractory Brick For Blast Furnace



Fire clay brick SK-32


Item

Standard

AI2O3(%)

30

Fe2O3 (%)

3.5

Refractoriness (SK)

32

Refractoriness under load,

0.2MPa, Ta, (°C)

1300

Porosity (%)

22-26

Bulk density (g/cm³)

2.05

Cold crushing strength (MPa)

25

Thermal expansion at 1000°C (%)

0.6



Fire clay brick SK-34


Item

Standard

AI2O3(%)

38

Fe2O3 (%)

2.5

Refractoriness (SK)

34

Refractoriness under load,

0.2MPa, Ta, (°C)

1350

Porosity (%)

19-23

Bulk density (g/cm³)

2.10-2.15

Cold crushing strength (MPa)

25

Thermal expansion at 1000°C (%)

0.6



Fire clay brick SK-36


Item

Standard

AI2O3(%)

50

Fe2O3 (%)

2

Refractoriness (SK)

36

Refractoriness under load,

0.2MPa, Ta, (°C)

1450

Porosity (%)

20-24

Bulk density (g/cm³)

2.30-2.40

Cold crushing strength (MPa)

45

Thermal expansion at 1000°C (%)

0.3

 

High Alumina Refractory Brick For Blast Furnace

High Alumina Refractory Brick For Blast Furnace

Features:

1. Low thermal conductivity, good thermal insulation performance.

2. Long service life, easy operation, could be shaped freely

3. Product specification: standard form, normal standard, shaped and special shaped bricks.

4. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.



Application:

 

Refracory brick plant can be in direct contact with the flame,this insulating brick can be used as linings or as thermal preservation layers in various industrial furnaces and kilns in metallurgical industry, ceramic industry, chemical industry, machinery industry.

 

such as blast furnace, hot blast stoves ,electric arc furnace, cement kiln,melting furnace, ignition furnace, flue, refining equipment, heating equipment and piping, regeneration device, gas furnace, soaking furnace, annealing furnace, heat reaction chamber and other thermal industrial equipment.

High Alumina Refractory Brick For Blast Furnace




FAQ



1. Do you provide samples?


   Yes, samples are free. Guarantee samples quality same as mass production quality.


2. What's the MOQ of trial order?

 

   No limit,We can offer the best suggestions and solutions according to your condition.

 

3. Can we visit your company?

 

  Of course,welcome at any time,seeing is believing.

 

4. Do you accept OEM?

 

   Yes, we can do OEM.

 

5. What are the payment terms?

 

   Usually T/T, D/A, D/P, L/C, Western Union ,others could be discussed .

 

6. How long is delivery time?

The delivery time will be determined according to the quantity of the order.

 

7. How are your products’ quality?

 

More than 20 years of production experience. The products will be strictly inspected before shipment, so the quality could be guaranteed.


8. How to slove the quality problems?

 

If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.

 

9. What is the service life of your bricks?

The service life of different bricks is unlike.It also depends on your using condition and method.

 

10. How about your company's certification?

 

ISO9001 and Test Report,also we could apply other necessary certification.

 

11.  How about your price?


Quality will be guaranteed. Competitive prices based on same quality.



Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Is glass wool inorganic thermal insulation material?
The characteristics of glass wool, glass wool is the molten glass fibrosis, the formation of cotton like material, chemical composition of glass, is a kind of inorganic fibers. With good forming, small volume density, thermal conductivity, both thermal insulation, sound-absorbing performance, corrosion resistance, chemical stability.
Q:The difference between aluminium refractory and magnesia refractory
Magnesia refractory belongs to alkaline refractory materials refers to refractory products such as magnesia magnesia brick magnesium iron spinel magnesium aluminum spinel magnesia ramming materials and other products of raw materials is the main crystal phase is periclase magnesia products
Q:How much is the bending temperature aluminum silicon carbide brick for torpedo car
The product has the advantages of high temperature, little creep, strong corrosion resistance and good thermal shock resistance, and is suitable for large and medium-sized hot blast stoves.
Q:How are the high alumina bricks fired?
Light and high alumina bricks are usually fired in a weak oxidizing atmosphere. In light and high alumina bricks firing, they are often rich in impurities such as R2O, RO, Fe2O3 and so on. They react with Al2O3 and SiO2 at high temperature to produce liquid phase. In the Al2O3 - SiO2 - R2O system, the growth rate of liquid phase increases with the increase of temperature at high temperature. So, because the increase of sintering temperature brings a lot of liquid phase, the decrease of liquid viscosity will lead to the deformation of brick and the decline of brick high temperature function. Therefore, the lower sintering temperature and longer holding time should be adopted in the sintering process dominated by liquid phase sintering. The production practice shows that the same firing temperature can be used for the high grade aluminum bricks. When fired in an inverted flame kiln, it is usually 1430 degrees centigrade and insulated by 40H. The high alumina bricks such as Ill are 1390~1420 degrees centigrade. When the tunnel kiln is fired, they are 1550 and 1450~1500 degrees centigrade respectively. High alumina brick is usually made of weak oxidizing atmosphere.
Q:What kind of material is the general metal case?
We usually discuss the electromagnetic radiation of computer enclosures, mainly RF radiation, followed by MF leakage.Switch signal of RF radiation from computer high-speed leakage, such as one of the energy radiation is CPU frequency, graphics, display output line, keyboard, is the source of the operating characteristics of the computer leaked out, is also the main part of computer security.For the absorption of radio frequency radiation, the best is the use of copper materials, the use of other metals can also, thickness enough on the line.The most vulgar description is that people can sit in the case is a good thing.
Q:High alumina brick 80 with which high aluminum cement?
In order to maintain a reasonable comprehensive lining, should adopt high quality aluminum refractory mud, such as Sichuan resistance card phosphate refractory mud, refractory clay, high alumina refractory mud PA-80 LN-75, if you use the card volume of Sichuan resistant refractory clay masonry, the effect is better.
Q:What is spalling resistant high alumina brick?
Using bauxite as main raw materials, the introduction of a small amount of ZrO2 (ZrO2 is due to phase transition, between monoclinic and tetragonal type can improve the thermal stability of the products), adding a certain amount of binder and additives, the particle size distribution control mud, forming and sintering of refractory products produced, called anti stripping high alumina brick.
Q:What are the specifications for bricks?
Thecompressive node as a new type of building energy-saving wall materials, which can be used for masonry walls, but also has good thermal properties, in line with the construction of the building module, reduce the loss in the process of construction, improve work efficiency; the hole rate reached more than 35%, can reduce the weight of the wall, save the foundation engineering cost. Compared with common sintered porous brick, it has the characteristics of heat preservation, heat insulation, light weight, high strength and high construction efficiency. The product is made of shale as raw material. It is produced by high vacuum extrusion molding machine and one yard firing process
Q:How many cubic bricks does a high alumina brick have?
Different content of aluminum, different proportion, weight is not the same. General grade T3 standard brick, 4.3~4.5kg, aluminium content 75. T3 size 230*114*65mm.
Q:What is the content of free silica in the refractory bricks of high alumina bricks?
In the meantime, the free silica content of silicon brick is as high as 90% above. Therefore, the most serious damage is silicon brick, followed by clay brick, high alumina brick, magnesia brick and so on.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range