Product Description:

Product features: use clay brick of hot air stove USES yangquan high-quality clay clinker as main raw materials, through high pressure molding, high temperature sintering, the main mineral composition of mullite phase, the product has excellent high temperature properties and resistance to chemical attack function, widely used in various parts of the middle and small blast furnace lining.
       热风炉用粘土砖

项目
Item

RN-42

RN-40

RN-36

Al2O3, %              不小于
min

42

40

36

Fe2O3,%               不大于
max

-

-

-

耐火度,℃            不低于
Refractoriness        min

1760

1740

1700

荷重软化开始温度,℃  不低于
RUL                   min

1400

1350

1300

重烧线变化,%         1450℃x2h
P.L.C.                1350℃x2h  

0—-0.4

0—-0.3

0—-0.5

显气孔率,%           不大于
A.P.                  max

24

24

26

常温耐压强度,Mpa     不小于
CCS                   min

29.4

24.5

19.6


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Whether fireclay raw materials or clinker are used when masonrying general fireclay brick? What is the difference between raw material and clinker?
Generally, refractory bricks use clay refractory mortar, raw material and clinker are halves
Q:What are the main raw materials of refractory brick and runner brick?
Types of refractory bricks are divided into low-grade and high-grade. generally, siliceous, semi siliceous and high aluminous runner brick brick have higher requirements. If it needs to contact melting in high temperature molten steel directly, then it is high alumina(the main raw material is clinker of bauxite with high alumina, corundum( brown corundum and white corundum), the refractoriness is high, lower than 1580 DEG C temperature, but the actual using temperature reaches 1630 DEG C
Q:The boiler is divided into several categories according to the structure, what characteristics does each have?
package boiler and assemble boiler are divided into vertical boiler and horizontal boiler. Vertical boiler. Assembled boiler adapts to boiler more than 6 tons, the package adapts to boiler less than 10 tons.
Q:What raw materials can be added to fireclay brick to respond to the urgent cold and urgent heat?
The effect of adding andalusite is better
Q:Are refractory bricks necessarily needed to build a kitchen stove?
The kitchen stove is used to cook dinner, so refractory bricks are unnecessarily needed. It depends on the temperature.
Q:What is the difference between the refractory brick and the thermal insulation brick
Refractory bricks are used in the stove, in order to prevent from burnouting the stove under high temperature. Thermal insulation brick is used for preserving heat, is to heat preservation
Q:Can thick steel plate be used instead of the furnace inside the refractory brick?
It depends on the temperature. The steel plate is a kind of heat conduction material which hasn't heat insulation, which should be based on the working environment.
Q:Expansion ratio of light corundum fireproofing brick
And then the appropriate drying, the using temperature 1500~1700 degrees of light corundum brick, the porosity is 70% to 80% Now, use foaming method to produce light corundum brick, 3g/, shaped idiosome with mould dry for 4 days in 60 degree to 70 degree oast, it will demoulding, foaming method and evaporating method produce light corundum brick, the thermal conductivity is 0. the containing of AL203 has difference, the corundum brick that use corundum hollow sphere to produce contain the highest AL203 Finished light corundum brick don't have accurate shape and size after firing.8 1, so products need mechanical or manual cutting after the kiln, finally, firing in 1300 degree and 1550 degree, basically still meters with water forming, just add to burn: 50~60h, because its production methods and the introduction of additives are different, the total sintering time.17W/, light corundum fireproofing brick can be made into density is 0, withstand voltage strength is 4MPa, the containing of A1203 is no more than 99%.
Q:buliding method of refractory bricks in boilers
Q:Why are the refractory bricks near to rotary kiln tyre easy to be short lives?

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range