Magnesite Brick - Graphite Alumina Magnesia

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

High Performance Kiln Refractory Bricks Alumina Magnesia Carbon Brick LMT-8 MG-20
High strength
Corrosion resistance

magnesite or corundum and flake graphite Alumina Magnesia Carbon Brick LMT-8 MG-20

Detailed Product Description

Type Of Magnesia Ferrum Alumina Brick Used For Rotary Kiln
Quick Detail:
♦ High strength
♦ Corrosion resistance
♦ Erosion resistance
♦ Excellent slag resistance
♦ Good thermal shock stability

Description:
This product belongs to new chrome-free basic refractories for large rotary kilns developed by our company. It is produced with high quality synthetic spinel materials and special technical process. The product is characterized by high crushing strength, good thermal shock resistance, good thermal creep, high refractoriness under load, also has the characteristics of direct bonded magnesia-chrome brick (easily adhering the furnace crust), and has solved the problem of environment pollution of sexavalent chrome forming during the use magnesia-chrome brick in cement kiln.
The development and application of Rongshrng company’s pleonaste brick conform to the trend of magnesite-chrome brick withdrawing from the historical stage in the cement industry, meet the demand of chrome-free basic refractories in cement industry under the new environmental-friendly situation.
Application:
It is widely used in all kinds of rotary kiln, the sleeve kiln, shaft kiln and lime kiln, etc

Items		Index
Items		QB/RS-1	QB/RS-2	QB/RS-3
Chemical Composition	MgO, % ≥	88	86	85
	Fe2O3 %	3-5	5-7	3-5
	Al2O3 %	3-5	1.0	1.0
	SiO2 % ≤	1.0	1.0	1.0
Bulk Density(g/cm3)		2.95	2.95	2.95
Apparent Porosity, % ≤		16	16	16
Cold Crushing Strength, MPa ≥		80	80	80
Refractoriness Under Load,℃, [0.2MPa×0.6%] ≥		1700	1650	1680
hermal Shock Resistance, Times, [1100℃, water-cooling]		10	8	10

Q: Brick price?: Refractory brick series sintered magnesia brick, magnesia chrome brick, magnesia brick, magnesia spinel brick, magnesia calcium brick, unburned magnesia chrome brick, magnesia brick, magnesia calcium brick, magnesia brick, and al2o3-mgo-c bricks.

Q: The index of magnesia brick: Room temperature compressive strength≥（MPa）（15－25－）24.5－24.5－24.5－24.5－40－40－40

Q: Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?: The ore quality requirements of MgO = 41%, CaO = 6%, SiO2 = 5%. The resources of magnesite in China are rich. The types of deposits include sedimentary metamorphic deposits, sedimentary hydrothermal metasomatic deposits and weathering leaching deposits.

Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it

Q: Magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying

Q: How to identify the fused magnesia brick and sintered magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying.

Q: Process for producing magnesia chrome brick: The oxide of iron reacts to produce a loose effect caused by the expansion of the spinel. Also, the magnesia chrome brick can be made from the synthetic common sintered material. In addition, there are non burned magnesia chrome bricks, for example, non burned magnesia chrome bricks combined with inorganic magnesium salt solutions. The unfired magnesia chrome brick has the advantages of simple production process, low cost and good thermal stability, but the strength of the high temperature is far less than that of the burnt brick. In the late 50s, a so-called "direct bonding" magnesia chrome brick was developed. The characteristics of this brick raw material is pure, high firing temperature, periclase and spinel phase with high temperature directly, silicate and other low melting point phase for island distribution, therefore, significantly improve the high temperature strength and slag resistance of brick.

Q: How do you differentiate between the two clearly? Where is the key? Thank you: Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius. It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.Fused magnesia brick brick has compact structure, high mechanical strength, low impurity content, mainly used for the storage of large glass kiln

Q: Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.: If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position

Q: Combined with the ordinary clay brick and magnesia brick as an example, the existence of impurities in minerals and refractories production main components of the formed liquid relative what affect the performance.: The main varieties of common magnesia brick, magnesia brick, magnesia brick, magnesia brick high pure grade. Product main mineral phase is periclase, volume has high stability and anti erosion ability. Literature is widely used in steelmaking, non-ferrous metal smelting and other high-temperature industrial furnace.

Send your message to us