Magnesite Magnesia Calcium Brick

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Magnesite Bricks for Nonferrous Metal Industry

Magnesite Brick for Induction Furnace Magnesia Spinel Bricks

Magnesite Brick - Firebricks, Fire Resistant Brick

Cement Kiln Magnesite Bricks

Industrial Kiln Magnesite Bricks

Industrial Furnace Magnesite Bricks

Magnesite Brick for Steel Tundish Magnesite Carbon Brick

Magnesite Brick for Permanent Linings of EAF and Steel Converters

Product Description

Features:

1. Low thermal conductivity, good thermal insulation performance.

2. Long service life, easy operation, could be shaped freely

3. Product specification: standard form, normal standard, shaped and special shaped bricks.

4. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.

Applications:

1. Carbon bake furnaces in the aluminum industry

2. Preheat zones and cyclones of rotary cement kilns

3. Insulation for glass tanks

4. Fireplace and pizza ovens

5. Coke ovens

6. Blast furnaces

7. Reheating furnaces

8. Suspended roofs

9. Lime kilns

10. Chimney

Specifications:

Technical data

Item	AL-30	AL-34	AL-38	AL-45	AL-55
AL2O3 % (min)	30	34	38	45	55
Fe2O3% (max)	3	3	2.8	2.8	2.6
Refractoriness	1670°C	1710°C	1750°C	1770°C	1770°C
Refractoriness under load, 0.2MPa, (°C)	1250	1300	1350	1450	1470
Apparent porosity (%)	22-26	22-26	20-24	20-22	20
Bulk density (g/cm³)	1.9-2.1	1.95-2.1	2.1-2.2	2.15-2.22	2.2-2.35
Cold crushing strength (MPa)	20	25	30	35	40
Thermal expansion at 1000°C (%)	0.8	0.6	0.6	0.5	0.4

Q: What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?: Different grades of burned magnesia brick is mainly made of magnesia binder with different taste, there is not a big difference. However, the physical and chemical properties of binders should be controlled well!

Q: Brick price?: Refractory brick series sintered magnesia brick, magnesia chrome brick, magnesia brick, magnesia spinel brick, magnesia calcium brick, unburned magnesia chrome brick, magnesia brick, magnesia calcium brick, magnesia brick, and al2o3-mgo-c bricks.

Q: The index of magnesia brick: indexMGe-20 MGe-16 MGe-12 MMGe-8 DBMK-A DBMK-B DBMK-C MgO≥（%） 40 45 55 60 80 80 80 Cr2O3≤（%） 20 16 12 8 6-8 6-8 6-8 SiO2≤（%） --- --- --- --- 2.0 2.5 3.0

Q: Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?: The ore quality requirements of MgO = 41%, CaO = 6%, SiO2 = 5%. The resources of magnesite in China are rich. The types of deposits include sedimentary metamorphic deposits, sedimentary hydrothermal metasomatic deposits and weathering leaching deposits.

Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it

Q: With different capacitance magnesia brick brick: Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius.

Q: Magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying

Q: How to identify the fused magnesia brick and sintered magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying.

Q: Process for producing magnesia chrome brick: The fine powder compacts after calcination produced by magnesia - chrome ore grinding method, brick with magnesia coarse particles, are effective measures to eliminate the effect of loose. Compared with the common magnesia chrome brick, the magnesia chrome brick made by this method has lower porosity, higher compressive strength, higher softening temperature and higher flexural strength. Compacts with chrome magnesite powder, magnesia chrome brick by synthetic magnesia chrome sand made of high-temperature calcination, slag resistance and high temperature strength are better than other magnesite chrome brick.

Q: Combined with the ordinary clay brick and magnesia brick as an example, the existence of impurities in minerals and refractories production main components of the formed liquid relative what affect the performance.: Also known as clay brick brick, is a man-made small bulk building, clay brick clay (including shale, coal gangue powder) as the main raw material, through mud processing, molding, drying and roasting, solid and hollow.

Send your message to us

*Email

*TEL

*Quantity

*Unit