Magnesite Refractory AZS41 Brick

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-
Inquire Now Customer Service

Contact us by

(1) WeChat
(2) Whatsapp: +8617190086776

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Fused Casting Zirconia Corundum (AZS) bricks for glass furnace

Fused Casting Zirconia Corundum (AZS) bricks for glass furnace

1.Definition:

It is mainly made of the baddeleyite and corundum material.

2.Raw material: corundum and baddeleyite eutecticum
3.Product technology:Casting technology.
4.Production process:

Made of the zirconite (Industry zirconia ) and industry alumina as the mainly mixed raw material, melting in the electric furnace, casting, annealing, machining, then finished.

5.Highlight:1). Fine thermal conductivity in the normal temperature.

2).Compact structure

3).Strong resistant erosion stability to the glass liquid.

4).Not color to the glass.

6.Properties:

chemical composition

AZS-33

AZS-36

AZS-41

ZrO2

≥33

≥35

≥40

SiO2

≤16.0

≤14

≤13.0

Al2O3

a little

a little

a little

Na2O

≤1.5

≤1.6

≤1.3

Fe2O3+TiO2

≤0.3

≤0.3

≤0.3

Physical Properties

bulk density(g/cm3):

3.5-3.6

3.75

3.90

cold crushing Mpa

350

350

350

thermal expansion coefficient (1000°C)

0.80

0.80

0.80

exudation temp. of glass phase

1400

1400

1400

corrocion resistance  of glass melt(mm/24h)

1.6

1.5

1.3

Density

PT   QX

3.40

3.45

3.55

WS    ZWS

3.60

3.70

3.8

phase composition(%)

baddeleyite

32

35

40

glass phase

21

18

17

α- corundum  

47

47

43

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:High purity magnesia brick masonry mortar for what?
Always! There is no 800 degrees can be sintered chamotte? As long as the dregs and do not break the aluminum content, the magnesia brick stick together can!
Q:Process for producing magnesia chrome brick
The oxide of iron reacts to produce a loose effect caused by the expansion of the spinel. Also, the magnesia chrome brick can be made from the synthetic common sintered material. In addition, there are non burned magnesia chrome bricks, for example, non burned magnesia chrome bricks combined with inorganic magnesium salt solutions. The unfired magnesia chrome brick has the advantages of simple production process, low cost and good thermal stability, but the strength of the high temperature is far less than that of the burnt brick. In the late 50s, a so-called "direct bonding" magnesia chrome brick was developed. The characteristics of this brick raw material is pure, high firing temperature, periclase and spinel phase with high temperature directly, silicate and other low melting point phase for island distribution, therefore, significantly improve the high temperature strength and slag resistance of brick.
Q:How to identify the fused magnesia brick and sintered magnesia brick?
Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying.
Q:Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.
If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position
Q:What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?
In addition to the brine binder burned magnesia brick and sulfite pulp waste liquid, Magnesium Sulfate solution binder is generally around 3%
Q:The index of magnesia brick
indexMGe-20 MGe-16 MGe-12 MMGe-8 DBMK-A DBMK-B DBMK-C MgO≥(%) 40 45 55 60 80 80 80 Cr2O3≤(%) 20 16 12 8 6-8 6-8 6-8 SiO2≤(%) --- --- --- --- 2.0 2.5 3.0
Q:Brick price?
There are various series of unshaped refractory gunning, magnesia ramming material, mending material, coating material, dry lining material, composite refining agent, covering agent, tundish and tundish slag wall, ladle drainage sand and electric furnace taphole filler etc..
Q:With different capacitance magnesia brick brick
Fused magnesia brick brick has compact structure, high mechanical strength,It is mainly used for thermal storage of large glass furnaceHigh temperature area of the room.
Q:Magnesia brick
Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclase. General can be divided into sintered magnesia brick (also called burnt magnesia brick) and chemically bonded magnesia brick (also known as the two major categories of not burned magnesia brick). Purity and high firing temperature of magnesia, due to the direct contact of periclase grains, known as direct bonded magnesite brick; made of fused magnesia bricks called electrically fused magnesite brick.
Q:Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick or clay brick, which type of high temperature refractory brick?
The super high alumina brick in high alumina refractory brick has the highest refractoriness, and the corresponding production cost is higher.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range
客服
live chat