Product Description:
Specifications
1) Density (ends/cm): 3 x 3
2) Breaking strength (N): 2700 x 2500
3) Good quality
4) White color
5)plain weave
Specification:
1) Density (ends/cm): 3 x 3 (warp x weft)
2) Breaking strength (N): 2700 x 2500 (warp x weft)
3) Weight: 600±60g/m2
4) Width: 1000mm
- Q:nan
- It is a kind of boron silicate glass with corrosion protection. It also can used as chemical filter. As a reinforcing material of glass fiber, it has the following characteristics. It is alleged that it also has the potential as glass fiber reinforced materials with 86000MPa elastic modulus. It is upgraded alkali free glass fiber for the requirements of environmental protection. It belongs to a sodium calcium silicate glass containing boron or no-boron and high alkali glass fiber (over 13% sodium oxidation, the absorption of impact energy is very good, but it is very important). After processing, glass fiber can be divided into non-alkali glass fiber ( 0% ~ 2% sodium oxidation). Quartz sand belongs to sodium calcium silicate glass with good heat resistance. (1) with high tensile strength, it can be fused into a small glass beads under high temperature and also can used for the production of reinforced materials. (3) the elastic limit is large and the tensile strength is high. (7) good machinability, it is mainly used for enhancing the properity of cement. It also can be used for enhancing asphalt roofing. Its main component are silica and it is a typical sodium silicate glass so as to reduce environmental pollution. It also be widely used for the production of glass fiber. (11) It is not easy to burn with high strength. Its disadvantage is that it is easy to be eroded by inorganic acid. Its strength is greatly increased with high flexibility. Glass fiber is mainly used for electrical insulating materials, manufacture of reinforced plastic or reinforced rubber, electrical insulating materials and heat or thermal insulation materials and so on.
- Q:nan
- No, it doesn't. The glass wool is produced by the centrifugal glass and it is irregular and discontinuous and fiber diameter is indefinite. The glass fiber is produced by platinum bushing and wire drawing machine with roving diameter is more than 9 micron, spun yarn is less than 9 micron and ultra fiber diameter is about 4 micron.
- Q:nan
- No, it doesn't.
- Q:nan
- Resins require low viscosity and are easy to operate manually. (2) pay attention to the overlap of the layer of raw materials, resin and unsaturated polyester. Enhance the materials by resin impregnation with roller or brusher, and then the corrosion resistance mandrel is made in the production made by the composite material. (3) advantages 1) As the advantages of straight fiber with reasonable line laying, as the inner lining, it could prevent wrinkles, so mould cost is high. Although the composite products are usually single shell. Twistless roving is used to priduce tube tank. (4) Disadvantages (1) It belongs to the labour intensive production. The filament winding angle and fiber arrangement density are designed according to the secondary active liquid thermosetting(subject to gel condensation) and two layers of fiber reinforced materials (reinforcing material surface mat.) The roving arranged in the creel, composite material and uniform direction; 2) the glass content can not be too high; 4) resin and reinforced material can be combined freely, mold depreciation is low, carbon fiber, phenolic resin, unsaturated polyester; 5) can be used to strengthen reinforced local enhancement.
- Q:nan
- Various kinds of products are formed finally which is called yarn number (t). The content of chrysotile is the most abundant. The diameter of glass fiber monofilament is from a few microns to twenty micron. 2 or more primary yarns are formed into added twist yarns by folded twist which is widely used. Glass fiber twist or twistless roving are formed into spun yarn with different specifications and usage. There mainly are alkali free. Composite line is formed by two or more fold twist. Glass fiber is a kind of inorganic nonmetal material with excellent performance. It uses glass ball or waste glass as raw materials and is formed by high temperature melting. It mainly is used for producing glass?fiber products. It has no degree of twist and it is spray forming reinforced material and insulation,electric insulation and heat or thermal insulation material which is also called double twist yarn. It mainly is used for hand lay-up glass?reinforced?plastics and is known as detwisting yarn in glass fiber industry. The meaning of metric system number. This yarn is called primary twist yarn which is bundling filaments combined by impregnating compound, namely 24tex. It is mainly used for testing the thickness of the original silk, laminate and winding. The metric system number is recommmended by the international organization for standardization(line destiny). 3 metric system number: The fineness degree of the yarn is expressed by the yarn quality of the unit length, which is equivalent to a hair. The smaller the number is, the thicker the yarn is. Monofilament is equal to 20tex. There are many kinds of asbestos whcih is widely used and usually is called monofilament. The former is a fixed length, the latter is a fixed weight.
- Q:nan
- 240 epoxy resin is used to produce glass fiber cloth by high temperature and pressure. It features with heat resistance and moisture resistivity. It is often used as components and parts for electrical appliance and electron with its model is 3240. It has high mechanical properties under medium temperature. Heat resistant grade is F (155 degrees). It is suitable for machinery with stable electrical performance at high temperature.
- Q:nan
- The materials for strengthen are Medium, vinyl type and flame retardant, vinyl resin. There are many types of materials like phthalate, benzene, alkali free glass fiber roving, knitted mat etc.: polyester resin
- Q:nan
- Q:nan
- A fiber as main ingredient in nonwoven adhesive bonded materials.
Needle punched nonwoven materials, Spunlaced Nonwovens Materials, spunlaid nonwovens method, fiber mesh constitute the main body of nonwoven materials, fiber in Nonwovens in these accounted for more than half or even one hundred percent. Fiber as a component of nonwovens fiber tangles in acupuncture Nonwovens Materials, Spunlaced Nonwovens Material and no yarn stitch bonding nonwoven material, part of fiber like buddle structure and coil web fibers to reinforce the fiber web. Three, fiber as the adhesive components of Nonwovens in most thermal bonded nonwovens, hot melt fiber into web in thermal bonding when all or part of melting, forming a hot melt adhesive composition in Web reinforcement.
- Q:nan
- The unsaturated resin is used as the subtrate material. it have many advantages such as sound insulation and so on. Glass?reinforced?plastics is also called glass fiber reinforced material with lightweight property. Glass?reinforced?plastics doors and windows use glass fiber twistless roving and fabric as reinforcement material. It is a new type of composite material developed abroad in early twentieth Century and can add other mineral filler.
Company respected "steadfast, perseverance, responsibility" spirit of enterprise, and with integrity, win-win and create a business philosophy, to create a good environment of enterprise, with new management mode, perfect technology, and thoughtful service, excellent quality for survival, we always adhere to customer first service to customers, insist on their service to impress customers.
1. Manufacturer Overview |
| Location |
Shanghai,China |
| Year Established |
2006 |
| Annual Output Value |
Above US$20 Million |
| Main Markets |
Mid East；Western Europe；North America：South American |
| Company Certifications |
|
2. Manufacturer Certificates |
| a) Certification Name |
|
| Range |
|
| Reference |
|
| Validity Period |
|
3. Manufacturer Capability |
| a)Trade Capacity |
|
| Nearest Port |
Shanghai |
| Export Percentage |
70% |
| No.of Employees in Trade Department |
200 People |
| Language Spoken: |
English；Chinese |
| b)Factory Information |
|
| Factory Size: |
Above 400,000 square meters |
| No. of Production Lines |
Above 15 |
| Contract Manufacturing |
Average |
| Product Price Range |
OEM Service Offered；Design Service Offered |