Product Description:

Type:We can supply High Alumina Bricks, Fireclay Bricks, Low Porosity Fireclay Bricks, Mullite Bricks, Corundum Bricks, AZS Bricks, Magnesite Bricks, Zircon Bricks,insulating Bricks etc.

Advantage:Our High alumina brick has high cold crushing strength,high refractoriness under load, high thermal stability,good creep resistance and thermal shock resistance,It is alternative product for high aluminum bricks, used in the professional of the key parts of the furnaces.

Application: Andalusite bricks are mainly used in the cooling wall of blast furnace, chemical and ceramic industry, the door of coke oven, or as the lining and checker of hot blast furnaces.

Specification:

                                                                     High alumina brick

Index           Product

LZ-48

LZ-55

LZ-65

LZ-70

LZ-75

LZ-80

LZ-85

Al2O3 %

≥48

≥55

≥65

≥70

≥75

≥80

≥85

Fe2O3 %

≤2.5

≤2.5

≤2.0

≤2.0

≤2.0

≤2.0

≤1.8

Refractoriness °C

1760

1760

1770

1770

1770

1790

1790

Apparent porosity %

≤23

≤23

≤23

≤23

≤23

≤22

≤22

Bulk density g/cm3

2.30

2.35

2.40

2.40

2.45

2.68

2.75

Refractoriness under load 0.2MPa°C

1420

1470

1500

1510

1520

1530

1550

Cold crushing strength MPa

45

45

50

60

60

70

70

Permanent linear change %

1500°C×2h

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:The cloth blowing is not uniform on the lime kiln refractory brick is damaged it
Lining 1 yuan to prevent direct damage to the Sindh kiln high temperature flame or air, to protect the kiln carcass; 2, to prevent harmful substances (CO, SO2) erosion of the kiln body; 3, to prevent corrosion, material flow on the kiln body; 4, reduce the kiln temperature, kiln body to prevent oxidation 5, has the function of corrosion; thermal insulation; 6, to improve the coating performance.
Q:How can the refractory brick blast furnace be pulverized and pulverized enough not to be taken away by the wind?
Top burning type hot blast stoveIt means that the burner is installed on the top of the hot blast furnace of the iron making equipment, and it does not need a special combustion chamber in the vault space. It is also called a non combustion chamber type hot blast stove.
Q:Difference between low creep high alumina brick and ordinary high alumina brick
Low creep and high alumina brick is based on the theory of "three stones". The combination of bauxite and clay as the main raw material, adding kyanite, andalusite and sillimanite, commonly known as the "three stone" control, physicochemical index and size composition, using alumina mullite corundum + + raw materials such as technical scheme. In the production process, first to detect and control indexes of raw materials, crushing, grinding, sieving process, according to the distribution ratio of ingredients, the size and moisture control of mud mixing after to meet the requirements of forming and molding machine, the use of qualified abrasives, blow molding control number, size and flash at the same time, the detection efficiency of semi-finished products and meet the requirements. Production process: high temperature calcination of high-grade alumina, adding small creep rate of high temperature materials, by high-pressure molding and high temperature firing. It has the characteristics of high strength, low creep rate and high use temperature. Widely used in high temperature furnace, hot air furnace hearth lining, brick and so on.
Q:What is spalling resistant high alumina brick?
Using bauxite as main raw materials, the introduction of a small amount of ZrO2 (ZrO2 is due to phase transition, between monoclinic and tetragonal type can improve the thermal stability of the products), adding a certain amount of binder and additives, the particle size distribution control mud, forming and sintering of refractory products produced, called anti stripping high alumina brick.
Q:Which is faster for heat transfer between corundum bricks or high alumina bricks?
There must be a difference. They vary in color from the amount of aluminum, the weight, the temperature, and the color.
Q:What is the standard classification of high alumina bricks or high alumina bricks?
Refractory brick is non-metallic materials can be classified according to a kind of inorganic material, high aluminum brick, clay brick, magnesia brick, corundum brick, mullite bricks, silicon carbide materials such as brick, high alumina brick is used as a relatively wide range of products in accordance with the refractory brick high alumina refractory materials by high aluminum brick is generally divided into Al2O3 content three: I - II - >75% Al2O3 content; the content of Al2O3 is 60 ~ 75%; III - Al2O3 content from 48 to 60%.
Q:What are the specifications for bricks?
Thecompressive node as a new type of building energy-saving wall materials, which can be used for masonry walls, but also has good thermal properties, in line with the construction of the building module, reduce the loss in the process of construction, improve work efficiency; the hole rate reached more than 35%, can reduce the weight of the wall, save the foundation engineering cost. Compared with common sintered porous brick, it has the characteristics of heat preservation, heat insulation, light weight, high strength and high construction efficiency. The product is made of shale as raw material. It is produced by high vacuum extrusion molding machine and one yard firing process
Q:How to make refractory bricks and boiler wall adhesion more firm?
Suggest that you use fire brick to increase the length of brick or pull the amount of turn, and use high temperature mortar masonry
Q:What causes breakage of refractory bricks?
Refractory brick is a non metal mineral products can be used in the high temperature of 1550 DEG C under belongs to a class of inorganic, used in high-temperature furnace lining materials as protection kiln, which causes damage, usually have these points.Furnace temperature is not clear, there is no corresponding choice of refractory bricks.Physical impact, abrasion and erosion cause damageChemical factors, especially chemical industry, should be made of refractory bricks, which should be resistant to penetration and erosionIV: products from the factory when the factory did not pass the quality inspection standards
Q:What is fireproof concrete?
According to the different properties of fire resisting and heat resisting concrete, they can be divided into silicate, aluminate, phosphate, sulfate, chloride, sol and organic substance, fireproof and heat-resisting concrete, etc.. The following are mainly used silicate, aluminate, phosphate, sulfate fire, heat-resistant concrete.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range