CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

Specifications

1. High temperature
3. with economical prices
4. Various models and size
5.acid and alkaline resistant

Specifications

1.Apparent porosity max 24%
2.Bulk density min 2.30 g/cm3
3.CCS min 40MPa
4.0.2Mpa (RUL)min 1400
5.Fe2O3 max 1.8 %

Index

LZ-75

LZ-65

LZ-55

LZ-48

LZ-80

LZ-85

Refractoriness SK

38

37

37

36

39

40

Refractoriness under load 0.2Mpa °C

≥1520

≥1500

≥1470

≥1420

≥1530

≥1550

permanent linear change %

1500°Cx2h

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

1450°Cx2h

+0.1~-0.4

Apparent porosity %

≤23

≤23

≤23

≤22

≤23

≤23

Cold crushing strength Mpa

≥53.9

≥49.0

≥44.1

≥39.2

≥55

≥55

Chemical composition

Al2O3 %

≥75

≥65

≥55

≥48

≥80

≥85

Fe2O3 %


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is the apparent porosity of high alumina brick?
In the production of high alumina bricks in addition to the entity, there are many different sizes and shapes of different pores, pores can be divided into three categories: one side closed the other side and the outside world is called open pores, closed in the product not communicated with the outside is called closed pores, penetrating through pores called the few products.
Q:Introduction of high alumina brick
High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.
Q:What are the requirements for Rubble backfill height?
Backfill should be filled with large stones, big face, small face upward, the decoration is stable, and then use small stones leveling, the gap between the stones can be swept into the slag, gravel, so that the gap filled.
Q:High alumina brick 80 with which high aluminum cement?
Which kind should be chosen should be determined according to the conditions of use, life expectancy and cost control. By the way, the quality of masonry is also very influential.
Q:What is the price of the first grade high alumina brick?
Many factories in Xinmi have high alumina bricks, but they must choose a regular factory. Kuwait refractory level high aluminum brick price at around 1600, the quality of double stable supply
Q:What is the difference between corundum and high alumina??
The main components of high alumina brick are high alumina bauxite, mullite and partial corundum sand.
Q:Are there any differences between insulating bricks and refractory bricks?
As the name suggests, the main role of insulating brick is used to preserve heat and reduce the loss of heat. Such as: Molai S; and the firebrick is mainly used to withstand flame burn. Bricks usually do not contact fire directly, while refractory bricks usually contact the flame directly.
Q:The difference between ordinary and diatomite brick refractory brick
To say the difference, the material is the biggest difference. There are diatomite brick density, compressive strength of small brick kiln belongs to the outer thermal insulation, and heavy refractory brick kilns for multi village in direct contact with the flame, high temperature resistance, good compressive strength, but no insulation. Hope to help you.
Q:Aluminum content 38. silicon content 55 What refractory bricks?
High alumina brick:The mineral composition of the high alumina brick is determined by the bauxite used. The mineral composition of the clinker is usually mullite, corundum and glass. The theoretical composition of mullite is Al2O371.8%, SiO2 28.2%, and its melting decomposition temperature is 1840 DEG C. With acicular crystal, network cross structure, high temperature state showed better strength. Corundum in the form of alpha -Al2O3, melting point of 2050 degrees, hardness of Mohs 9, showing a granular and columnar crystal, has good chemical stability, acid, alkaline slag have a certain resistance. Based on the composition of mullite minerals, the phase composition of high alumina brick can be judged according to the content of Al2O3. When the bricks are below Al2O3 71.8%, the base of the composition is mullite and SiO2, such as grade LZ-48 bricks. Because it contains a large number of SiO2 formed in the liquid phase under high temperature is 20% ~ 30%; brick in Al2O3 more than 71.8%, the excess Al2O3 formed corundum crystal under high temperature, while generating 2 high temperature phase, eutectic temperature rise by the low content of Al2O3 brick 1595 C to 1840 C, such as grade LZ-75 brick. In fact, it is impossible to produce a complete phase equilibrium in the process of production, but the glass phase is very small, and there is no more than 10% in the partial gap of the Yu Jing phase
Q:Corundum, high alumina and fireclay refractory difference is what
Corundum is unknown. The high alumina brick has higher aluminum content than the clay brick, and the temperature resistance is higher than 300 degrees. It is more durable and durable than the clay brick. The production process of high alumina brick is better than that of clay brick. For example, the weight of good clay brick is 3.7kg, and that of high alumina is 4.2kg. Good density. But the price of high aluminum is too high: ordinary clay brick (standard brick example) in 1.1--2.5 yuan / block, high aluminum to 4.5 yuan / block, or even more expensive. The extra high aluminum has reached 5000 tons. Say straight white point is: under the same conditions, clay brick for a period of one year, then the high aluminum for more than three years.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range