Aluminum Circle Plate for Utensile Cookware

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
2 m.t.
Supply Capability:
6000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Item specifice:

Grade: 1000 Series,3000 Series Surface Treatment: Mill Finish Shape: Round,Flat
Temper: O-H112,Half Hard,Soft Application: Kitchen Use Technique: DC/CC
Thickness: 0.3mm-4mm Width: 200mm-950mm Packaging: wood pallets

Product Description:

Aluminum Circle Plate for Utensile Cookware 


Packaging & Delivery

Packaging Details:25kg/carton-boxes(35*32*19CM) &Fumigation wooden-pallets (110*110*15cm)
20GP can loading 22 Ton,total 21 pallets,20 CBM.
Delivery Detail:within 25 days

Specifications

1).Excellent Surface Quality for lighting reflectors.
2).Excellent deep drawing and spinning quality.
3).Anodizing Quality

 Aluminium circle/Aluminium discs/disks for cooking utensils Cookware

  • Aluminum disc Surface Finish: Bright & smooth surface, without flow lines, slightly oiled to avoid White rusting.Smooth,Brightly ,No Zone of Fracture ,No Scratched ,No oil Sludge

  • We enjoy a good reputation among our customers for our aluminum circle with high quality and competitive price, win high appreciation from our clients with the excellent workman-ship and professional ability. The quality matches with ISO 9001 quality management system.

  • It is equipped with 5 hot tandem rolling line, 4 cold mill production lines, 4 annealing surface machines and a complete finishing equipment.



  • Specification:

  • Alloy

    Temper

    Specification

    Thickness

    Diameter

    1070,1050,3003,1100

    O,H12,H14,H16

    0.5-5.0mm

    100-1200mm

  • Aluminum disc chemical Properties(WT.%)

  • Alloy

    Si

    Fe

    Cu

    Mn

    Mg

    Cr

    Ni

    Zn

    Ca

    V

    Ti

    Other

    Min.A1

    1050

    0.25

    0.4

    0.05

    0.05

    0.05

    -

    -

    0.05

    -

    0.05

    0.03

    0.03

    99.5

    1070

    0.25

    0.25

    0.04

    0.03

    0.03

    -

    -

    0.04

    -

    0.05

    0.03

    0.03

    99.7

    3003

    0.6

    0.7

    0.05-0.2  

    1.0-1.5 

    -

    -

    -

    0.1

    -

    -

    -

    0.15

    96.95-96.75 



Aluminum Circle Plate for Utensile Cookware


Aluminum Circle Plate for Utensile Cookware

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:how to avoid oxidation of aluminum sheet after wire drawing?
leave it alone after wire drawing!aluminum sheet will formulate a layer of dense oxide film. So you don't need to worry about it! Don't often polish the aluminum wire, or they will be more and more slimsy, the oxide film is used for avoiding reoxidation.
Q:after putting aluminum sheet into the area between magnet and iron products, could magnet attract iron again?
magnet can attract iron if the aluminum sheet isn't too thick. Because aluminum can't cut off magnetic line of force, unless aluminum sheet's thickness surpass the range of magnetic attraction.
Q:How to press multilayer aluminum sheets (aluminum sheet's thickness: 0.2mm) together and keep them inseperate after pressing?
resistance welding usually overlays two pieces together and presses them, heating them to melting state through current, you can try multiple sheets.
Q:how to connect copper pipe and aluminum sheet?
welding!
Q:why does 10% sulfuric acid not react with aluminum sheet?
10% sulfuric acid has a high concentration and will be passivated and formulate a layer of oxide film after reacting with aluminum,and the reaction will stop after seperating sulfuric acid and aluminum. there is a layer of Al2O3 oxide film on the surface of aluminum, so it's hard for sulfuric acid to break the oxide film and react with aluminum.
Q:Could two pieces of aluminum sheets be welded together?
or you can use file to rub back and forth, and it needs lots of practices or you can't weld the sheets.because aluminum sheet cann't be tightly welded to tin, it's hard to weld two pieces of aluminum sheets by common welding methods.it's hard, the aluminum sheets are oxidized soon after polished by abrasive paper.and you need to cover the new polished area with soldering paste and learn some operating skills.owing to aluminum sheets' high oxidized speed, you need to wipe the aluminum sheets with soldering paste and soldering tin and rub them with large power soldering iron, then the aluminum sheets will be tightly welded to tin.so two pieces of aluminum sheets could be welded together.
Q:which kind of enterprises are aluminium sheet circles used in?
user use cold squezz method to transform the aluminum sheet circle into various standard capacitor shell, aluminium collapsible tube shell, which are broadly used in electron industry, daily chemical industry, medicine, education and automobile products,electrical appliance, heat preservation, machine manufacturing, automobile,spaceflight,military industry,mould, construction, printing and other industries.
Q:how to separate the aluminum sheet in plastic?
Put them into clean water if both of them won’t react with water, and aluminum sheet will sink into the bottle, then fish up them separately.
Q:is aluminum foil spacer poisonous after heating?
It’s a kind of thermoprint material made by pressing the aluminum into sheet, and owing to its similar thermoprint effect to silver foil, so it’s called fake silver foil. Aluminum has soft texture, good ductility, and is silver white, if we use sodium silicate to paste the sheet after pressing on the offset paper, making aluminum foil, the foil can be printed. But aluminum foil is easy to be oxidized and darkens, rubbing and touching will make it darken, so it doesn’t suit for the thermoprint of books’ cover that needs to be preserved for a long time.
Q:how to make aluminum products bright? How to polish or clean the products punch formed by 0.3mm aluminum sheet?
you can try to grind it with magnetic grinder.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range