Silica Brick for Industrial Kilns System 1

Silica Brick for Industrial Kilns

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

1. Profession manufacturer with 25 years experience
2. Silica refractory brick
3. High quality and low price

Silica Brick Description

High quality silica a brick is made of silicon raw material, the content of SiO2 is above 95%. And the content of Al2O3 is below 1.0%. Our factory produces various kinds of refractory products. The products can be made according with the customers' requirement.

Silica Brick Advantage:
1) Silicon oxide is above 95%.
2) Good acid erosion resistance.
3) High softening point with temperature.
4) No shrink in burn repeatedly.
5) Temperature of refractoriness under load is above 1650º C
Stable Capability, High Quality, Excellent Service, Competitive price is the most important advantage of our products.

Application of silica brick:

They are widely used for hot blast furnace, coke oven, and glass furnace. The products can be made according to customers' requirement.

Silica Bricks specification:

Item	Coke Oven Silica Brick	Glass Furnace Silica Brick		Hot Blast Stove Silica Brick
Item	JJG-94	JBG-95	JBG-96	JRG-95
SiO₂ %	94.5	≥95	≥96	95
Fe₂O₃ %	1.5	≤1.0	≤1.0	1.3
CaO %	2.5	2.2	2.2	2.2
Refractoriness °C	1790	1790	1790	1790
Refractoriness under load T1,°C	1650	1650	1660	1650
Apparent porosity %	22(24)	22(24)	22(24)	22(24)
Cold crushing strength Mpa	40(35)	35(30)	35(30)	35(30)
True Density g/cm³	2.33	2.32	2.33	2.34
Thermal Expansion %	1000°C 1.28(1.30)	1000°C ≤1.25	1000°C ≤1.25	1000°C 1.26
Residual Quartz %	1.0	1.0	1.0	1.0

$Silica Refractory Brick For Industry Kilns$

Q: The specific content is what gb/t2608-2012 brick: The provisions of the brick classification, technical requirements, test methods,

Q: The introduction of silica brick: The characteristics of silica brick:Brick belongs to refractory materials, with strong resistance to acid slag or acid solution erosion ability, high load softening temperature are excellent properties of silica brick, usually 1640-1680 C.The use of silica brick:Mainly used for masonry brick oven carbonization chamber, a combustion chamber and a partition wall, glass furnace and kiln roof, pool wall, high temperature hot blast furnace, glass furnace, load-bearing pool wall, hot blast stove, baking furnace of carbon bearing part of high temperature furnaces etc.. Rongsheng with refractory

Q: How much is the highest melting point of silicon?: Acidic silica brick refractories, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. More than 94% silica content.

Q: Which material is good for furnace refractory?: Basic refractories in Magnesium Oxide and calcium oxide as the main ingredient, commonly used is brick. Magnesium Oxide 80% to more than 85% containing magnesia brick, has good resistance to alkaline slag and slag, refractory clay brick and brick high ratio. Mainly used in open hearth furnace, oxygen converter, electric furnace, non-ferrous metal smelting equipment and high temperature equipment.

Q: What role does silica play in refractories?: The production of clay brick refractory clay raw material is natural, its main mineral is kaolinite (formula Al2O3 - 2SiO2 - 2H2O), clay brick containing SiO2 in 45% ~ 65%, belongs to the weak acid refractory materials, have a certain ability to resist acid slag, but easy to be alkaline slag erosion.

Q: The brick is mainly used in the place?: Also used for high temperature bearing part of hot blast stove and acid open hearth furnace.

Q: Can iron oxide be used as refractory material?: Iron oxide can not be used as refractory material, but it can be used as refractory additive. Iron oxide can be used as pigment

Q: Common bond brick?: When adding ingredients, the amount of lime added shall be converted to CaO, and the amount of addition varies depending on the product, usually fluctuating at 1.5~2.5%. For example, the production of coke oven silica brick, the dosage of CaO is 2.0~3.0%; the production of electric furnace top brick, the dosage of CaO is 1.4~1.75%.

Q: What are the main constituents of refractory bricks?: (a) containing refractory brick brick, refers to more than SiO293%, is the main varieties of acid resistant brick. It is mainly used for coke oven building, also used in furnaces all kinds of glass, ceramic and carbon calciner, refractory brick arches and other load-bearing parts, is also used in high temperature bearing part of hot blast stove, but should not be used in thermal equipment below 600 DEG C and the temperature fluctuation in the.

Q: The difference between clay refractory bricks and refractory brick in the application.: Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.