High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
3000 pc
Supply Capability:
50000 pc/month
Inquire Now Customer Service

Contact us by

(1) WeChat
(2) Whatsapp: +8617190086776

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces


 The phosphate bonded high aluminum bricks are with high strength, low bulk density, low thermal, conductivity, high thermal shock resistance and the anti-spalling is good. Widely used in cement kiln,hot blast stove/furnace,EAF(electric arc furnace),coke oven door...WeCNBM are manufacturing various ceramic fiber productsfireclay brickscorundum bricks,insulation bricksmagnesia bricks,silica brick. chrome and zirconia brick...





High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces

High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces


ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,%

1450x2h           

  0.1~-0.4

1500x2h             0.1~-0.4

1500x2h             0.1~-0.4

1500x2h       0.1~-0.4

1550x2h             -0.5~+0.5

1550x2h             -0.5~+0.5

1550x2h             -0.5~+0.5

Al2O3 Content , %

48

55

65

75

80



 


High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces

High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces


Our services:


1.Adhering to the business philosophy "Mutual Trust, Mutual Benefit, Mutual Profit, Faith Oriented".


2.According to your requirements to produce your order and OEM/ODM service is available.


3.Products are inspected through SGS and BV etc and accord with the international standard.


4.Your inquiry related to our products or prices will be replied in a timely manner.



Application:

 

Refracory brick plant can be in direct contact with the flame,this insulating brick can be used as linings or as thermal preservation layers in various industrial furnaces and kilns in metallurgical industry, ceramic industry, chemical industry, machinery industry.

 

such as blast furnace, hot blast stoves ,electric arc furnace, cement kiln,melting furnace, ignition furnace, flue, refining equipment, heating equipment and piping, regeneration device, gas furnace, soaking furnace, annealing furnace, heat reaction chamber and other thermal industrial equipment.

High Alumina Fire Clay Corundum Refractory Bricks for Various Industrial Furnaces




FAQ



1. Do you provide samples?


   Yes, samples are free. Guarantee samples quality same as mass production quality.


2. What's the MOQ of trial order?

 

   No limit,We can offer the best suggestions and solutions according to your condition.

 

3. Can we visit your company?

 

  Of course,welcome at any time,seeing is believing.

 

4. Do you accept OEM?

 

   Yes, we can do OEM.

 

5. What are the payment terms?

 

   Usually T/T, D/A, D/P, L/C, Western Union ,others could be discussed .

 

6. How long is delivery time?

The delivery time will be determined according to the quantity of the order.

 

7. How are your products’ quality?

 

More than 20 years of production experience. The products will be strictly inspected before shipment, so the quality could be guaranteed.


8. How to slove the quality problems?

 

If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.

 

9. What is the service life of your bricks?

The service life of different bricks is unlike.It also depends on your using condition and method.

 

10. How about your company's certification?

 

ISO9001 and Test Report,also we could apply other necessary certification.

 

11.  How about your price?


Quality will be guaranteed. Competitive prices based on same quality.




Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are the reasons for the decline in the performance of high alumina bricks when we use high alumina refractory bricks?
Quality requirements for aluminium bricks of different grade. 2, high aluminum powder and high alumina aggregate and other materials of reasonable proportion, to reach the production requirements.
Q:Density of high alumina bricks
High alumina brick by aluminum content is divided into four grades, three grade high alumina bricks content of not less than fifty-five percent, two grade high alumina bricks content of not less than 65, a high aluminum brick content of not less than 75, super high aluminium brick content above 85. As for the high aluminum brick shape, in addition to the standard high alumina brick, high alumina brick and general type, also called special high alumina brick, if the shape is very irregular it is usually called the specific type of high alumina brick, in short, to customized according to the specific use of kiln.
Q:What is the high temperature limit of refractory bricks and refractory soil?
Refractory bricks are stone powder and clay paste. They are fired in a kiln of 1300 degrees. The upper limit is 1500 degrees above normal pressureRefractory bricks - refractory materials of a specified shape and size.
Q:How does the physicochemical index change when the high alumina brick is used at high temperature?
If the range of softening temperature exceeds the load, the constants of other physical and chemical indexes will also increase or decrease.
Q:The difference between aluminium refractory and magnesia refractory
Therefore, the difference between the two is a neutral, one is alkaline, the original product is different naturally.
Q:The difference between light high alumina brick and heavy aluminum brick
Lightweight high alumina brick, also called high alumina insulation brick. Alumina content of 48% or more, mainly from mullite and glass phase or corundum composition of lightweight refractory. Volume density 0.4 - 1.35g/cm3. Porosity 66% - 73%, compressive strength 1 - 8MPa. Better thermal shock resistance. Usually, a high alumina clinker is added with a small amount of clay. After grinding, it is poured and shaped in the form of slurry by gas generation or foam method, and it is fired at 1300 - 1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.
Q:Application characteristics of high alumina brick
Reheating line change. If the firing temperature of high alumina brick products is enough and the firing time is enough, the volume is stable, the change of the reheating line is small; on the contrary, the residual shrinkage of clay brick products is caused by recrystallization.
Q:What is the heat preservation material used in a laboratory furnace?
Thermal insulation cotton is a high-purity clay clinker, alumina powder, silica powder, chromium sand and other raw materials in the industrial furnace melting at high temperature, forming fluid. Then, compressed air is used to blow or use the wire throwing machine to turn the yarn into a fiber shape. After the cotton collector is collected, the cotton is formed into a heat preservation cotton.The high alumina brick is usually made of high alumina clinker with small amount of clay. After grinding, the high alumina brick is poured and shaped in the form of slurry by the way of gas generation or foam, and it is burnt at 1300~1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.
Q:How to reduce the harm caused by two times mullite in high alumina refractory material
Prolong the sintering time and adjust the aluminum content of the high alumina brick.
Q:What are the high aluminum bricks made of?
It's OK to use corundum bricks and alumina hollow ball bricks to build a furnace,

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range
客服
live chat