Silica Brick S96 for Coke Oven

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 100000 pc/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Silica Brick S94 for Hot Blast Stove

Calcium Silicate Bricks Price for High Duty Silica Ceramic Kiln

Silica Silicate Mullite Bricks for Industrial Furnace

$Silica Brick - Refractory Silica Insulation Fire Brick$

Silica Brick - Refractory Silica Insulation Fire Brick

$Zero Thermal Expansion Refractory Silica Bricks$

Zero Thermal Expansion Refractory Silica Bricks

Silica Brick for Low Thermal and Chemical Expansion in Steel and Iron Industries

Silica Bricks for Coke Oven and Hot Blast Stove

$Silica Brick - High Quality Refractory Silica Brick$

Silica Brick - High Quality Refractory Silica Brick

General Information of SilicaBrick For Coke Oven

Our corporation produces a comprehensive range of silicabricks, with high silica content, all of these bricks exhibit excellentperformance.

Our Silica bricks are the final result of blendingexcellent tridymite and cristobalite, as the main raw materials withcutting-edge technology, after mixing, drying, forming, in the high temperatureshuttle kiln. There are also little quartz and vitreous within. We ensure youthat the silica bricks made by us possess high quality standard and have gonethrough all the complicated quality control parameters. Their durability andstrength adds life to the structure and they have the capacity of bearing hightemperature.

Feature of Silica Brick For Coke Oven

Resistant to thermal shock, abrasion, chemical attack

High ability for anti-abrasion during work

Superior resistance to acids (including oxidizing)

Resistance to chlorine

Resistance to thermal shock and pressure changes

Low thermal and chemical expansion

Applications of Silica Brick Coke Oven

Silica brick for Coke Oven ismainly used in Coke Oven.‍

Silica Brick For Coke Oven---S96
Physical Properties:
Permanent Linear Change(1500℃×4h)%	%	0.2
Apparent Porosity, %	%	≤24
Cold Crushing Strength	Mpa	30
Refractoriness Under Load (T0.6)	℃	≥1680
Thermal Expansion	%	≤1.3
Density	g/cm³	-
Chemical Analysis:
SiO₂	%	≥95
Fe₂O₃	%	≤0.8
Al₂O₃	%	≤1
Residual Quartz	%	≤1
Note: Technical Data are typical average results from test pieces. The technical data is offered solely for your consideration. And we reserve the right to modify the technical data without any prior notice. Users of our products should make their own tests to determine the suitability of each product for their particular purposes.

Q: The hot blast stove when the temperature did not rise against the brick interface decreased: Different insulation methods can be adopted according to the length of the stop time and the location and equipment of the overhaul. Gold, refractory material factory specializing in the production of various specifications of brick

Q: Why will expand when heated brick: Because the production of raw materials are silica brick, brick with SiO2 content of not less than 95% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system

Q: What is the effect of the content of silicon nitride in silicon nitride bonded silicon carbide brick on the use of electrobath? Thank you: The main damage of silicon carbide side wall brick is stress damage, not chemical erosion. Chemical damage is formed prior to the formation of the groove, and the damage to the chemical erosion is little after the formation of the groove.

Q: What is the main material of silica brickIt's common, the kind we see so often!: Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into phosphorus and quartz. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.

Q: Glass kiln brick for physical and chemical indicators?: Glass kiln with high quality silica brick with silicon oxide content, low melt index, mainly used for glass kiln crown, parapet, wall hanging, small furnace arch superstructure and regenerator.

Q: What role does silica play in refractories?: The production of clay brick refractory clay raw material is natural, its main mineral is kaolinite (formula Al2O3 - 2SiO2 - 2H2O), clay brick containing SiO2 in 45% ~ 65%, belongs to the weak acid refractory materials, have a certain ability to resist acid slag, but easy to be alkaline slag erosion.

Q: The United States of our brick anti-dumping duties?: At present of our brick anti-dumping rate is 73.10%

Q: The chemical composition of silica brick and its physicochemical index?: ????Al2O3 SiO2??????fe2o3??????cao???????r2o93～98?0.5～2.5?；；?0.3～2.5??0.2～2.7；??1～1.5；

Q: The difference between clay refractory bricks and refractory brick in the application.: Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.

Q: Such purpose and scope please give me detailed points thank you: Acid refractory brick is mainly composed of tridymite and cristobalite and quartz and a small amount of residual glass phase.

Send your message to us

*Email

*TEL

*Quantity

*Unit