Product Description:

Specifications

1. Good construction performance
2. High strength stability
3. High temperature resistance
4. Good resistance to abrasion

Refractory Castable Features:

1.Good construction performance.

2.High strength, good bulk stability.

3.Good insulation, high temperature resistance, good thermal shock resistance.

4.Good slag resistance, good resistance to abrasion.

5.Good corrosion resistance.Scouring resistance

Refractory Castable Application:

1.Used as lining turning kiln, hot converter lining heat treatment furnace.

2.Furnaces of metallurgy industry, chemical industry and construction industry.

3.Circulation part of furnaces.

Physical and chemical index:

Item

Properties

DLG-80

DLG-70

DLG-60

DLG-50

    Al2O3%

≥80

≥70

≥60

≥50

 CaO%

≥2.5

≥2.5

≥2.5

≥2.5

Bulk density,g/cm3

110°C×24h Drying after

≥2.75

≥2.60

≥2.50

≥2.40

1500°C×3h After burn with fire

≥2.70

≥2.60

≥2.40

≥2.40

Compression strength

110°C×24h Drying after

≥45

≥45

≥40

≥40

MPa

1500°C×3h After burn with fire

≥75

≥70

≥60

≥60

The flexural strength

110°C×24h Drying after

≥7

≥6

≥6

≥6

MPa

1500°C×3h After burn with fire

≥10

≥10

≥8

≥8

Line rate %

110°C×24h Drying after

≤-0.1

≤-0.1

≤-0.1

≤-0.1

1500°C×3h After burn with fire

≤-0.5

≤-0.5

≤-0.5

≤-0.5

  Highest using temperature

1600

1500

1450

1400


FACTORY:


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Are there any differences between insulation and refractory materials ?
Refractory materials can resist more than 1200 degrees, some of which are not insulation materials, such as firebricks, which can directly contact with heat source, has little insulation effect. Ceramic fiber, high silica, etc. are all refractory materials which can insulate. Insulation materials with poor performance usually is lower than 800 degrees, which have large thermal resistance, and low thermal conductivity, high porosity. Thus they reduce the thermal loss. To put it simply, insulation materials store most of the heat and only let a small part of heat lose through the air, thus the heat has been isolated. Glass fiber, rock wool, flexible material for thermal insulation, etc.
Q:What is the upper temperature limit for refractory materials?
Different materials are different. In the professional field, there is a triangulation cone softening point experiment as a reference for using the upper temperature limit.
Q:Who know about the knowledge of acid refractory material? Please explain in detail.
Abrasion resistance of fire resistance material depends on the material group and structural material. The abrasion resistance of dense single crystal materials depends on the hardness of mineral crystal. The higher the hardness, the more resistance the material is to abrasion. non mineral crystals with fine grain material has a high wear resistance. The abrasion resistance of materials is related to bulk density or porosity. Aluminium refractory material can resist a temperature as high as 700~900 degree within the elastic range. The higher the temperature, the lower the resistance. Abrasion resistance will be increased with elastic modulus as temperature increase. In many cases, refractory material will often cause a lot of harm due to mechanical abrasion.
Q:What needs to be noted when choosing and using blast furnace fireproof materials? Who knows?
there are different temperatures in various parts of the blast furnace, thus using different types of refractory.
Q:What a blast furnace refractories generally?
Common refractories often use silica brick, semi-silica brick, fireclay brick, high alumina brick, magnesia brick, etc. special materials often used are AZS brick, corundum brick, directly bonded magnesia-chrome brick, carborundum brick, silicon nitride bonded silicon carbide bricks, nitrides, silicides, sulfides, borides, carbides and other non-oxide refractory materials; calcium oxide, chromium oxide, aluminum oxide, magnesium oxide, beryllium oxide refractory insulating refractory frequently used. material diatomite products, asbestos products, insulation boards. monolithic refractories have fettling frequently used, refractory ramming mixes, refractory castable, fire-resistant plastic, refractory clay, refractory gunning refractory projection material, refractory coatings, lightweight refractory castable, stemming etc.
Q:The classification of clay according to refractoriness, and what is the plasticity and plasticity index of clay?
Q:What is the function of refractory material?
Refractory is a basic material in the field of high temperature technology. Generally, the refractory is used as structural material or lining to resist high temperature in various thermal equipment and high temperature container. In the iron and steel industry and metallurgy industry, coke ovens are mainly composed of refractory materials. Various refractories that meet the requirements are essential in blast furnace for ironmaking, hot stove, all kinds of steel-making furnaces, soaking furnace and heating furnace. Not only the die casting for molten steel needs lots of refractory materials, but also the continuous casting needs some high-quality refractory materials. Without high-quality refractory materials, external refining is also not impossible to achieve. Statistics show that the steel industry is the sector that needs the most refractory. Pyrometallurgy and thermal processing of ferrous metal also needs refractories. All high-temperature furnaces or lining in construction materials industry or other high temperature industries that produce silicate products such as glass industry, cement industry, and ceramics industry must be constructed with refractory materials. All kinds of roasting funaces, sintering funaces, heating furnaces, boilers, flues, chimneys and protective layers in chemical, power and machinery manufacturing industry need refractories. In short, when some kind of structures, devices, equipments or vessels are used under high temperature, they all should utilize refractory to resist the high temperature because those materials will deform, soften and fuse or will be eroded, scoured or broken due to the physical, chemical, mechanical effects, which may stop the operation, affect the production, contaminate processed objects and impact the quality of products.
Q:What is the requirement of refractory concrete for raw materials? What is the main principle of commercial mixing station?
There are many kinds of raw materials used, three, two aluminum oxide is one of the most commonly used raw materials, as well as alumina, hollow ball, Magnesium Oxide, zircon, etc., or the specific design temperature and the use of parts.
Q:Who knows what fire heat preservation material are there?
It can be realized through inorganic insulation materials, such as glass wool, rock wool, foam glass etc.. The phenolic foam materials inside organic foam material is more special. Phenolic foam does not only have a good thermal insulation performance, but also can be combined with steel and other materials, to achieve a class A fire retardant level. Class A thermal insulation include: Rock (ore) cotton, foam glass, inorganic thermal insulation mortar, etc.. 1 thermal insulation materials with class A combustion performance Phenol, powder polystyrene particles etc.. Fire insulation materials of fire barrier zone can use class A material with class A combustion performance in rock (ore) cotton, foam glass, inorganic thermal insulation mortar. Hope my answer will help you.
Q:What's the difference of fire-resistant material's density, specific gravity and bulk specific gravity?
glass

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range