High Quality Silicon Carbide Fines Silica Refractory Brick

Ref Price:
Loading Port:
China main port
Payment Terms:
TT OR LC
Min Order Qty:
100 kg
Supply Capability:
2000000 kg/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

High Quality Silicon Carbide Fines Silica Refractory Brick

 

CMAX Silica bricks are made from high quality quartz tail sand, lime and mineralizing agent through the process of crashing, screening,mixing, pressing, drying and sintering. zircon brick is characterized by good thermal stability and resistance to corrosion and erosion of glass liquid. They are used for high temperature equipment in the glass furnace, molten steel ladle and continual casting water month.

Silica bricks for hot stoves feature sharp dimension,low expansion,little residual quartz, low true density.low creep rate,good thermal shock resistance upon 600°C and high refractoriness under load, It mainly used at high temperature area include arch and upside of hot stove and upside of checker.What’s more, we are main supplier of Morgan . 

 

Product Applications:

Silica Brick are ideal for use in the below applications 

Furnaces of metallurgy industry, heat treatment furnace
Furnaces of chemical industry and construction industry.
Furnace of incineration of garbage, recirculating fluidized bed furnace
Standard sizing: 230 x 114 x 65 mm others up to the clientKiln car building                      

For ladle  

 

Product Advantages:

With dense and smooth appearance, uniform corner and edge, pure color and luster and accurate size.

Silicon oxide is above 95%. 

Good acid erosion resistance. 

High softening point with temperature. 

No shrink in burn repeatedly. 

Temperature of refractoriness under load is above 1650º C 

Stable Capability, High Quality, Excellent Service, Competitive price is the most important advantage of our products.

 

Main Product Features:

Low bulk density, low thermal conductivity, good thermal insulation performance.

Refractory category allow direct contact of fire, suitable ofr various atmosphere

Good integrity with furnace lining, long service life, easy operation, could be shaped freely

Product specification: standard form, normal standard, shaped and special shaped bricks.

Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used. 

 

Product Specifications:

 

ITEM

For Hot-Blast Stoves

For Glass Furnace

S-94

S-95A

S-95B

G-94

G-95A

G95-B

G-96A

G-96B

SiO2, %

≥94

≥95

≥95

≥94

≥95

≥95

≥96

≥96

Fe2O3, %

≤1.5

≤0.5

≤1

≤1.5

≤1.2

≤1.2

≤0.8

≤1

Residual Quartz, %

≤1

≤1

≤1

≤1





Apparent Porosity

≤23

≤23(24)

≤21(23)

≤24

≤22(24)

≤22(24)

≤22(24)

≤22(24)

True Density, g/cm3

≤2.35


≤2.34

≤2.33

≤2.35

≤2.35

≤2.34

≤2.34

Cold Crushing Strength, Mpa

≥29.4

≥30(27)

≥30(20)

≥30

≥30(35)

≥30(35)

≥30(35)

≥30(35)

Refractoriness Under Load, ℃


≥1650

≥1600

≥1630

≥1660

≥1650

≥1680

≥1670

Permanent Linear Change, %



1500℃X4h, ±0.2

1450℃X2h, ±0.5





 

FAQ:

Q1: Are you a manufacture or trader?

A: Factory+trade (mainly for manufacturing, also do some business of related products).

Q2: What's the MOQ of trial order?

A: No limit,We can offer the best suggestions and solutions according to your requirements.

Q3: After an order is confirmed,when to deliver?

A: According to your order quantity, normally, 15-25 days after deposit received.

Q4: Is your company accept customization?

A: We have our own factories and excellent technical team, and we accept OEM service.

Q5: What certificates do you have?

A: ISO9001 and Test Report, also we can do other necessary certification according to your requirements.

Q6: Can you offer samples?

A: Of course,samples are total free! Freight should be paid by buyers.

 

Product Picture 

 High Quality Silicon Carbide Fines Silica Refractory Brick

Produce Processing 

High Quality Silicon Carbide Fines Silica Refractory Brick

 High Quality Silicon Carbide Fines Silica Refractory Brick

 

 

 




Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:The specific content is what gb/t2608-2012 brick
Quality assessment procedures, packaging, marking, transport, storage, and quality certificates. Suitable for siliceous refractory bricks.
Q:The introduction of silica brick
Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature.
Q:Brick
An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.
Q:The introduction of silica brick?
The characteristics of silica brick:Brick belongs to refractory materials, with strong resistance to acid slag or acid solution erosion ability, high load softening temperature are excellent properties of silica brick, usually 1640-1680 C.The use of silica brick:Mainly used for masonry brick oven carbonization chamber, a combustion chamber and a partition wall, glass furnace and kiln roof, pool wall, high temperature hot blast furnace, glass furnace, load-bearing pool wall, hot blast stove, baking furnace of carbon bearing part of high temperature furnaces etc.. Rongsheng with refractory
Q:The hot blast stove when the temperature did not rise against the brick interface decreased
Different insulation methods can be adopted according to the length of the stop time and the location and equipment of the overhaul. Gold, refractory material factory specializing in the production of various specifications of brick
Q:Such purpose and scope please give me detailed points thank you because I am learning stage
Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on. The properties and process of silica crystal with SiO2 transformation is closely related, therefore, the proportion of it is one of the important quality indexes of silica brick. General requirements below 2.38, high quality silica brick should be less than 2.35. The true density is small, reflecting a large number of scale quartz and square quartz in the brick, the residual quartz is small, so the residual line expansion is small, and the strength is decreased in useThe raw materials for the manufacture of silica brick. The higher the SiO2 content of silica raw material, the higher the refractoriness. The most harmful impurities are Al2O3, K2O, Na2O and so on. They seriously reduce the refractoriness of refractory products. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer (e.g. millscale, lime) and binder (such as molasses, sulfite pulp waste liquid), after mixing, molding, drying, sintering and other processes in the system.
Q:Semisilica brick, clay brick, high alumina brick and what is the difference?
The share of A12O3 and SiO2 is different
Q:The difference between clay refractory bricks and refractory brick in the application??
Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.
Q:The formula in the refractory brick, and firing curve, who knows?
Add 1.8-2.2% of the total weight of the main raw material, and then add lime milk, rolling for 10-15 minutes, and finally add pulp, rolling for 10-15 minutes, out of the mill, forming billet.
Q:What role does silica play in refractories?
The natural mineral of silica is called quartz. In refractories, silica and siliceous refractory materials contain more silica. Silica is acidic at high temperature, and siliceous refractory can resist acid slag corrosion

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range