High Aluminium Brick Commonly Used in Hot Blast Furnace

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
10 m.t
Supply Capability:
8000 m.t/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

High Aluminium Brick Commonly Used in Hot Blast Furnace


Firebricks Description
High alumina insulating fire brick is a kind of insulation material adopting organic matter as ignition loss substance in order to increase the porosity of refractory,which has such advantages as high porosity, small volume density,good insulation effect,high mechanical intensity,small thermal conductivity and long service life.For various industrial kilns&furnaces,it is a kind of essential refractory for energy saving and temperature preservation.This series of High Alumina fire resistant brick are made of selected high alumina bauxite, kaolin caly,hollow microsphere as the mian material.By shaping at high pressure and sintering at high temperature.


Firebricks Application
High alumina bricks are commonly used in blast furnace,hot blast furnace,the roof of electric furnace,teeming ladle,rotary kiln,regenerator etc.


Firebricks Features
.Low thermal conductivity
.Excellent acid and base slaging resistance
.High refractoriness
.Excellent thermal shock resistance
.Excellent mechanical strength

Firebricks Specification&Pictures

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness, ℃

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa 

39

44

49

53

55

60

100

Refractories Under Load (0.2Mpa),℃

1420

1470

1500

1520

1500

1520

1550

Reheating Linear Change,% 

1450℃x2h             0.1~-0.4

1500℃x2h             0.1~-0.4

1500℃x2h             0.1~-0.4

1500℃x2h         0.1~-0.4

1550℃x2h             -0.5~+0.5

1550℃x2h             -0.5~+0.5

1550℃x2h             -0.5~+0.5

Al2O3 Content , %

48

55

65

75

80

85





High Aluminium Brick Commonly Used in Hot Blast Furnace

High Aluminium Brick Commonly Used in Hot Blast Furnace

FAQ

Q1  What’s the transport method?

A1  FCL delivery goods with wooden pallet or wooden case by sea; If LCL delivery, must with wooden case; Sometimes need open top, flat rack or bulk cargo.

Q2  What’s the required payment term?

A2  Generally 30% TT as the prepayment, 70% TT before delivery. If need, 100% Irrevocable Letter of Credit or negotiation.

Q3  Which country are our products exported to?

A3  Apart from entire Chinese market, the US, Russia, Japan, Korea, Australia and some Southeast Asian Nations.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are the alloy wear resistance materials?
According to the composition of Beijing Naimo metal materials company will wear resistant metal materials is divided into the following five categories: one: high manganese steel series: high manganese steel (ZGMn13),
Q:What are the high aluminum bricks made of?
It's OK to use corundum bricks and alumina hollow ball bricks to build a furnace,
Q:What is the difference between fireclay bricks and high alumina refractory bricks?
First of all, there is a difference in the material, one is clay, and one is high aluminum.Also known as clay brick brick, is a man-made small bulk building, clay brick clay (including shale, coal gangue powder) as the main raw material, through mud processing, molding, drying and roasting, solid and hollow.
Q:Refractory brick, high alumina brick, magnesia chrome brick or magnesia brick, clay brick, which type of high temperature refractory brick?
High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it
Q:Introduction of high alumina brick
High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.
Q:The difference between light high alumina brick and heavy aluminum brick
Lightweight high alumina brick, also called high alumina insulation brick. Alumina content of 48% or more, mainly from mullite and glass phase or corundum composition of lightweight refractory. Volume density 0.4 - 1.35g/cm3. Porosity 66% - 73%, compressive strength 1 - 8MPa. Better thermal shock resistance. Usually, a high alumina clinker is added with a small amount of clay. After grinding, it is poured and shaped in the form of slurry by gas generation or foam method, and it is fired at 1300 - 1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.
Q:Which is faster for heat transfer between corundum bricks or high alumina bricks?
75 high aluminum and 43 clay bricks, 75 single weight 4.5kg or more. 43 3.65kg or so, the use of temperature 75, high aluminum in about 1520, 43 of brick 1430 or so, the color of 75 pan white, 43 of the Loess color. In short, the difference is great.
Q:Are there any differences between insulating bricks and refractory bricks?
As the name suggests, the main role of insulating brick is used to preserve heat and reduce the loss of heat. Such as: Molai S; and the firebrick is mainly used to withstand flame burn. Bricks usually do not contact fire directly, while refractory bricks usually contact the flame directly.
Q:How to distinguish the good or bad of the high aluminum brick?
The general high alumina bricks used in the steel, steelmaking, hot blast furnace, electric furnace, blast furnace, reverberatory furnace, rotary kiln lining of industrial furnace in China, mainly composed of a bauxite; sillimanite minerals (including kyanite, andalusite, sillimanite etc.); synthetic material, such as alumina synthesis of mullite, corundum, etc.. High aluminum brick has good quality, high refractoriness, long life and other characteristics, is the main use of refractory brick kiln products, commonly used units can not distinguish the quality and grade of high aluminum brick right in the procurement time, caused by the high prices to buy low grade products, thereby reducing the furnace life therefore, Zhengzhou's Sindh yuan refractory material factory in here is simple to introduce how to identify the quality when purchasing brick high alumina brick.Color: in the purchase of high alumina brick, first of all to see the color, high quality aluminum brick surface smooth, yellow color white, four sides smooth, no broken angle, no cracksWeight: the weight of a block of bricks to be called, according to the standard weight level, high aluminum brick weight of 4.5 kg. Two grade high alumina brick weighs 4.2 kg, three high aluminum brick weighs 3.9 kg, the same level, the same parameters can reach this standard can be regarded as high-quality high aluminum bricks, the opposite is not up to the weight that the quality is good, if there is a crack, four angle uneven, off angle phenomenon, then substandard products, some of the above points to help to the purchaser
Q:Density of high alumina bricks
Alumina content of 48% or more, mainly from mullite and glass phase or corundum composition of lightweight refractory. The volume density is 0.4 ~ 1.35g/cm3. The porosity is 66% ~ 73%, and the compressive strength is 1 ~ 8MPa. Better thermal shock resistance.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range