Magnesite chrome bricks in magnesium oxide (MgO style) and chromium trioxide (Cr2O3) as main component, and periclase spinel as main mineral components of refractory products.This kind of bricks of high refractoriness, high temperature strength, strong alkaline slag erosion resistance, good thermal stability, also has certain adaptability for acid slag.The main raw material of manufacturing magnesite-chrome brick is sintered magnesite and chromite.Magnesia raw material purity as high as possible, chromite chemical composition requirement is: the Cr2O3:30 ~ 45%, CaO: 1.0 ~ 1.5% or less.

Production technology of calcined magnesite chrome bricks in line with magnesia brick.In order to eliminate the bricks in burning process because of MgO style and Cr2O3, Al2O3, or
Directly combined magnesite chrome brick
Directly combined magnesite chrome brick
Iron oxide reaction caused by the expansion of the spinel as of loose effect, also can use common sintering synthetic materials made from magnesite chrome brick.In addition, there is not burned magnesite chrome brick, for example, combined with inorganic magnesium salt solution is not burned

magnesite chrome brick.Don't burned magnesite chrome brick production technology is simple, low cost, heat stability, but the high temperature strength far less burnt brick.The late '50 s, develop a socalled "direct combination" magnesite chrome brick.The characteristics of this kind of brick is

pure raw materials, sintering temperature is high, the periclase, spinel, such as direct combination between high temperature phase, such as low silicate phase for the island shape distribution, therefore, significantly improve the high temperature strength and slag resistance of the brick.
With chrome ore - magnesia compact grinding calcined after fine powder, and magnesia bricks made of coarse particle with method, is an

effective measure to eliminate the effect of loose.Magnesite chrome brick made of using this method, compared with common magnesia chrome brick, brick of low porosity, compressive strength, high refractoriness under load and the bending strength.With chrome ore - magnesite powder compact, high-temperature synthesis of calcined magnesite chrome magnesia-chrome brick made of sand, slag resistance and high temperature strength are better than other magnesite chrome brick.
In addition, there is electricity solitary furnace molten magnesite chrome material directly casting and fused magnesite chrome brick

(see figure of microstructure, see image), electricity melt magnesium chrome material according to the production of brick melt granule recombination magnesite chrome brick, etc.