Q:How do graphitized electrodes differentiate between high power and low power?

In electrolysis industry, using graphite anode plate as the anode has a history of more than 100 years, the metal anode is in recent decades, the research and application of metal anode in China late last century, only in 70s the technology related to the research and experiment of metal anode, anode on electrolysis industry, mainly through the silver (2%) (0.5%): low silver lead silver alloy, lead and silver tin antimony alloy, lead calcium alloy and lead silver alloy adding nucleating agents and several stages.

Q:What is the difference between pyridine type nitrogen and graphite type nitrogen?

In fact, this problem is very simple, the carbon graphite is six square lattice ordered, natural graphite and artificial graphite is divided into two kinds: the classification of natural graphite flake graphite and graphite is earthy, basically it is not forming soil shaped graphite graphite, are rough machining, the battery core and do more. The use ratio of flake graphite.

Q:How much does a graphite electrode cost about a ton?

According to purity and quality, the price is 1-6 tons / tonDo not calculate the processing cost

Q:Why should supercapacitors use graphite as electrode material?

There are some similarities between the supercapacitor and the lithium-ion battery technology...... Typing and super capacitor is divided into three kinds: organic (carbon based, including now speculation is very powerful, Shi Moxi) principle is potential polarization of electrolyte, electrolyte and the positive and negative ion conductive material on the electron positron forming an electric double layer, high porous carbon materials.

Q:Graphitized coke, graphite, broken, mixed up, how to export?

The graphite powder is soft, black and gray, greasy and polluting paper. Hardness is 1~2, along the vertical direction with the increase of impurities, its hardness can be increased to 3~5. The specific gravity is 1.9 ~ 2.3. Under isolated oxygen conditions, the melting point is above 3000 degrees Celsius and is one of the most refractory minerals. At room temperature, the chemical properties of stone toner are relatively stable, insoluble in water, dilute acid, dilute alkali and organic solvents. The material has high temperature resistance and conductivity, and can be used as refractory materials, conductive materials, wear-resistant and lubricating materials.

Q:What are pyrolytic graphite electrodes used for?

(1) the processing speed is faster: normally, the mechanical processing speed of graphite can be 2~5 times faster than copper, while the discharge processing speed is 2~3 times faster than copper;More material is not easily deformed: obvious advantages in the processing of thin electrodes; copper softening point at about 1000 degrees, easily deformed by heat; graphite sublimation temperature is 3650 degrees; the thermal expansion coefficient of copper is only 1/30.

Q:Graphite electrode in milling machine processing, dust is especially big, boot 5 minutes, workshop can not open the figure, what is the solution?

This is to use the dust collector, the graphite itself is a semiconductor, can not be electrostatic dust removal

Q:What does graphite electrode GSK mean?

Graphite board material is GSK, GSK refers to model specifications

Q:How can I electroplate iron? I would like to use graphite as an electrode. Iron is plated on graphite with iron solution, so it can be processed into iron parts. I wonder if it can be done

Iron plating can be, with 2 valence iron, but on the graphite joint force is good, it is difficult to say, electroplating is bad, peeling is also common. Relatively speaking, iron parts on nickel plating is relatively simple, also more applicable

Q:Do electroplating experiments, graphite as an electrode, graphite how to pre process to ensure that the coating will not fall, resulting in increased color of the solution

Both of these will be a little bit absorbed, when plating, the anode and anode inside the syrup will run on the negative pole,