Raw Materials for High Alumina Refractory Cement with Low Price

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 0 m.t.

Supply Capability:: 40000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Products	Calcium Aluminate Cement /High Alumina Cement CA-50
Applications	1,As binders calcium aluminates cement are used in concretes and mortars for specialised applications for their properties of resistance to corrosion, abrasion and heat combined with rapid hardening and the ease of controlling grading variations. Calcium aluminate cements are also used in combination with other fine components. Hydraulic binders with new properties are then obtained. In this way, aluminates act as both a complex hydraulic binder and a mineral reagent interacting with the other components in the mix. 2,As reagents, calcium aluminates are found in non-hydraulic systems. This is the case in metallurgical treatments (iron and steel industry, foundry) where specific grades of calcium aluminate are used for their low-temperature melting properties and for trapping molten metal impurities.
Features	1,Very low mixing-water requirement
2,Very high purity
3,High product consistency
4,High cold and sintered strength
5,Very tight specifications of setting times

product	CA50F	A600	A700	A900	CA50R
Chemical Compositionn (%)	SiO2	≤8.0	≤7.8	≤7.5	≤5.5	≤7.0
Al2O3	≥50.0	≥50.0	≥51.0	≥53.5	≥52.0
Fe2O3	≤2.5	≤2.5	≤2.5	≤2.5	≤2.5
R2O	≤0.4	≤0.4	≤0.4	≤0.4	≤0.4
S	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1
Cl	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1
45µm residue (%)	≤20	≤15	≤12	≤8	≤8
Blaine (m2/kg)	≥300	≥300	≥320	≥350	≥350
InitialSetting (min)	≥30	≥45	≥60	≥90	≥30
FinalSetting (h)	≤6	≤6	≤6	≤6	≤6
Flexural strength (MPa)	6h	——	——	——	——	≥3.0
1d	≥5.5	≥6.0	≥6.5	≥8.0	≥7.0
3d	≥6.5	≥7.0	≥7.5	≥10.0	≥8.0
Compressive strength (MPa)	6h	——	——	——	——	≥30
1d	≥40	≥45	≥55	≥72	≥60
3d	≥50	≥55	≥65	≥82	≥70

Packaging & Delivery

Packaging Details:	1,Packaged in multi-ply paper bags on pallet and polyethylene shrink wrapping. For added protection polyester strapping may be applied. 2,big bags may be placed on standard pallets with polyethylene shrink wrapping.
Delivery Detail:	upon to the quantity of order

.jpg

Q: what's the standard of fireproofing material?: Class A1 is divided according to the combustion performance of GB8624-2006 building materials and products. Specific technical index requirements are: 1, the temperature rise ≤30 degrees;mass loss rate ≤50%; combustion duration time is 0; 2, main components, overall products, gross calorific value of external secondary components ≤2.0MJ/kg; any inner secondary component ≤1.4MJ/kg; (there are difference between homogeneous and non-homogeneous). Z802 building materials noninflammability testing furnace has to be used for testing technical indicators mentioned in test 1, using Z805 building materials combustion heat value to test technical indicators mentioned in test device 2.

Q: How much modulus is used as refractories material of sodium silicate.: Storage and use are very convenient, especially for mechanized and the evenly refractory material and the sodium silicatemodulus is generally...2. transportation. The appearance of product is pure white. Instant powdered sodium silicate, also known as instant sodium metasilicate.4 to 3, in powder form, automation. in the range of 3, hydrated sodium silicate

Q: Who knows what is the requirement for fireproofing of interior decoration materials ?: In addition to the underground building, combustion performance level of interior decoration materials inside windowless room , in addition to a class, should advance 1 level based on the original provisions . Library, archives and rooms storing artifacts, ceilings, walls should use class A decoration materials, and the ground should use decoration materials no lower than class B. When high temperature parts of lighting and lighting lamps and lanterns are close to non - grade A decoration materials should be taken, fire prevention measures such as thermal insulation and heat dissipation must be taken. Combustion performance level of materials used for lighting should be no lower than B. Kitchen ceiling, wall and floor should used class a decoration materials.

Q: How many types do refractory bricks have? Where the quality of refractory material is best? What is the model?: Sinosteel Luoyang (Luoyang Refractory Material Plant in the past): High alumina(mainly blast furnace), Gongyi. There are also a series of high-tech materials (silicon carbide, carborundum, etc.) a major producer of high alumina; silicious: Resistant material for steel, glass furnace, cement kiln); magnesia. Divide from uses and divide from chemical texture; silicious(glass furnace): Xinmi, Hennan Province, Lengshui River, coke oven, etc.). As for the models, Yixing and Changxing in Jiangsu Province: Haicheng, Liaoning Province; silicious, I do not understand your intentions; magnesia (nonferrous, steel refining; magnesia: High alumina brick; Dashiqiao area! Please put it in detail.

Q: what are the requirements of fireproofing material?: answer: 1 fireproof materials are used in construction, in various forms and it has played an absolute role in modern fireproofing, common fireproofing materials include fireproof?panel, fire door, fireproofing glass, fire?retardant?coating, fireproof bag,etc. 2, fireproof?panel is the most common texture in the market. There are two common types: One is the high pressure decorating refractory slab, it's advantages are fireproofing,moisture-proof, wear-resistant, oil resistant, easy to clean, and it has various colors; another one is glass magnesium fireproof board, external layer is decoration materials, and inner layer is mineral magnesium fireproofing material, and it can endure 1500 degrees high temperature but has bad decoration. Installing fireproof suspended?ceiling in outlet channel of construction, stairwell and corridor can ensure safe evacuation of people and protect people from attacking of fire spreading in the disaster. 3, the production process of fire and moth proof wood: firstly, put general wooden materials into solution with calcium, aluminum and other cations, then soak it into solution with phosphate radical, silicate and other anions. Thus, the two ions will be carried out chemical reaction in the wood, forming a ceramic-like material, and intimately fill the voids of cells, so that the wood has the fireproofing and mothproof properties.

Q: What are the characteristics of the carbon composite refractories?: The features of carbon composite refractories: 1. It is with an aggressive high thermal shock resistance 2. Good resistance to molten steel and slag

Q: What are the specific steps of stirring the steel ladle castable?: Steps are as follows. 1 Compulsory mixer is used to stir the castable and bags, rope and other debris can not mix in the castable when stirred. 2, Castable should be unpacked on the scene. Stirred volume depends on the capacity of the mixer. Castable should be accurately measured and put into a blender. 3 The process of first dry mixing and then wet mixing is adopted. After the castable is added to the mixer, it is dryly mixed for 2 minutes, add about 5.2 to 5.5 percent of water and continue to add water while stirring. Water that is 80% of the total should be added, and then decide whether to continue to add or not depending on the consistence (noting that the water must be clean water and sewage can not be used). Then it is wetly mixed for 4 minutes and stirred for not less than 6 minutes at one time, until castable is even. In general, the bottom is slightly dry and the wall of the ladle is slightly dilute (the amount of water is only for reference). 4, The amount of water and mixing time should be controlled strictly when stirred to ensure that the needs of the consistency are met. If castable is too thin, it will seriously affect the quality of the material. The stirred volume, stirring time and water that is added should be consistent and they can not suddenly be thick or suddenly be thin. If the consistency does not meet the requirements, the castable should be put back to the mixer and stirred with appropriate water or dry materials. 5, It should be stirred evenly and casting should finish in 20 minutes, in order to avoid sclerosis, affecting structural strength of ladle lining 6, After each completion of construction, varieties of castable should be changed and the mixer should be cleaned 7, Stirring can stop in halfway. If the mixer breaks down and it can be repaired in a short time, some of the materials have to be removed before the machine is opened. If the machine can be repaired on time, castable refractory should all be removed.

Q: What do refractory materials include?: What refractories are included? Refractories include AZS brick, corundum brick, direct-bonded?magnesia-chrome, carborundum brick, silicon nitride bonded silicon carbide brick, non-oxide refractory materials such as nitride, silicides, sulfides, borides and carbides, oxidation calcium, chromium oxide, aluminum oxide, magnesium oxide and beryllium oxide.

Q: Who knows the texture of fire-proof wooden door material?: Steel door, wooden door or steel wooden door can be inset fireproof laminboard, such as rock wool, perlite. Perlite (fireproof doors filling material, fireproof doors raw material) using for fireproof door core is mainly used for the filling material of fireproof doors and security doors. Fire protection, thermal insulation, good sound insulation effects, and higher performance than aluminum?silicate?wool and rock wool. The combustion performance of perlite using for fireproof door core reaches class A non-combustion, which is new type of fireproof doors filling material with characteristics of low cost, good fireproof performance and excellent environmental protection performance. The advantages of fireproof door core perlite as fireproof door filling material: 1, Good fireproof performance, so it has a function of fire prevention. Environmental protection: all materials are environmentally friendly products. Pollution-free: the product is composed of glass fiber reinforced materials and inorganic binder. 2, with characteristics of non-flammable, non-explosive, water-resistant, oil-resistant, chemical erosion resistant, non-toxic and good mechanical strength, etc. The product can be used for mechanic processing like sawing, drilling, gouging, etc. High fire resistance, in the simulated combustion tests, it doesn't deform when the flame temperature reaching 800 degrees, has good fire retardant and fire-resistant properties. 3, product material is cheap, suitable for all kinds of fireproof materials. Perlite fireproof board is made by pressing the expanded perlite powder and high temperature fireproof adhesive through mould, suitable for the filling material of fireproof wooden door and fireproof steel door, which is the substitute products of aluminum?silicate?wool and rock wool. 4, has advantages of light volume-weight, high refractoriness, strong compressive strength, small thermal conductivity, non-flammable, non-toxic, tasteless, non-pollution, etc.

Q: Could you tell me the fire-resisting time of class B fire proof door?: The fire-resisting time of class B fire proof door is 1h and thickness of door can't be lower than 45mm.

Send your message to us

*Email

*TEL

*Quantity

*Unit