Black silicon carbide 0-1/1-3/3-5mm and powder with good quality

Ref Price:
Loading Port:
China main port
Payment Terms:
TT OR LC
Min Order Qty:
25 m.t.
Supply Capability:
2000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Quick Details

Place of Origin:

China (Mainland)

Brand Name:

CNBM

Model Number:

CF180# 240# 320# 800# 1200#

Material:

SIC

Usage:

Lapping, Polishing,Blasting, Refractories

Abrasive Grain Sizes:

46#..1200#...2000#..2500#

color:

black and green

hardness:

9.15 mosh

melting point:

2250

Packaging & Delivery

Packaging Details:bags, cartons
Delivery Detail:15-20 days

Specifications

silicon carbide Size Available: 
F10-F220,F240-F1200 
Other special size could be supplied as required.

1.used for made abrasive products
2.professional manufacture
3.prompt reply-within 24hours
4.prompt delivery-within 15days.
GritSiCF.C.Fe2O3
F12-F9098.50%min0.20%max0.60%max
F100-F15098.00%min0.30%max0.80%max
F180-F22097.00%min0.30%max1.20%max
F230-F40096.00%min0.40%max1.20%max
F500-F80095.00%min0.40%max1.20%max
F1000-F120093.00%min0.50%max1.20%max
P12-P9098.50%min0.20%max0.60%max
P100-P15098.00%min0.30%max0.80%max
P180-P22097.00%min0.30%max1.20%max
P230-P50096.00%min0.40%max1.20%max
P600-P1500095.00%min0.30%max1.20%max
P2000-P250093.00%min0.50%max1.20%max
Black Silicon Carbide is brittle and sharp and has electrical and heat conductivity in some degree.

Aplications :
Black Silicon Carbide is suitable for make grinding wheels, cutting wheels, mounted wheels, oil stone, abrasive media, and also suitable for surface grinding, lapping or polishing. 

The abrasive products made of it are suitable for working on Cast Iron, Non-ferrous Metal, Rock, Leather, Rubber, Wood, Ceramic, etc.

Black Silicon Carbide is also broadly used as high-grade refractory material and metallurgical additive. 

Black silicon carbide 0-1/1-3/3-5mm and powder with good quality


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How to choose thermal insulation materials for flood heating?
How to choose the appropriate thermal insulation materials: 1, Thermal insulation material shall have a small thermal conductivity, good thermal insulation properties. Besides, that also depends on whether the specific temperature changes of in the insulation materials' working environment can ensure the material has good thermal insulation. 2, when purchasing, we must be make sure it is light, and loose enough. These heat insulating material can not only afford bracket, and can also increase the heat transfer performance of the heat insulation material. prevet water penetration. Waterproof function should be soild, even if it accidentally absorbs water, its thermal insulation function must be guaranteed. 3, None of the organic material should applied to production of insulation materials, Thermal insulation material containing organic matter may get rotten, mildewed, and cause other destructive . At the same time they should not contain flammable substances, in order to avoid the fire. I hope my answer can help you
Q:What kind of material is refractory fiber?
Refractory fiber, also known as ceramic fiber, is a fibrous thermal insulation refractory. It has the characteristics of ordinary fibers, such as softness, flexibility, having a certain tensile strength. And it can be further processed into a variety of products such as paper, wire, rope, tape, blankets and felts. Besides, it has high temperature resistance and corrosion resistance which ordinary fibers don't have. As a fire retardant and thermal insulated material, it has been widely used in metallurgy, chemical, machinery, building materials, shipbuilding, aviation, aerospace and other industrial sectors.
Q:Can anyone tell me what is a high alumina refractory?
High alumina refractories: High-alumina refractory products have high refractoriness, compressive strength and refractoriness under load, which are used for building the high-temperature parts of various large blast furnaces, such steelmaking furnace, airheater, electric furnace, rotary kiln and other thermal equipment.
Q:How many kinds of refractory materials are there in the EI?
I suggest that you contribute articles to foreign SCI journals for the odds are better, and generally the articles that fill the bill will not be rejected. The traditional refractory materials can contribute to EI journal. If being rejected by EI journal, you can also contribute to Russia's journal Industrial Ceramics and Refractories. I didn't contribute to the Journal of Wuhan University of Science and Technology, the receiving cycle is almost 3 to 4 months. Though the impact factor is low, domestic EI journal is not so good, it is still SCI journal. This is my own experience, please take my advice. The best journals are the Journal of the American Ceramic Society and the Journal of the European Ceramic Society, I heard that they are not bad. But the best domestic EI refractory material journal is the Journal of The Chinese Ceramic Society. It is very long, but if it belongs to your university, it is another pair of shoes. Journals now all want to have materials about functional ceramics, and they don't want Chinese articles, if your English is not well enough, you can choose Ceramics International and Japan Ceramics but they have strict manuscripts reviewing standards.
Q:What is the concept of lightweight refractory material?
Lightweight refractory material has high porosity, mechanical strength and erosion resistance. Compared with normal refractory bricks, it is a kind of refractory material with large volume shrinkage in high temperature, low thermal conductivity and small bulk density. It is used as thermal insulation material in industrial furnace and other thermal equipments. It has poor wear resistancel.
Q:What kind of material is good for cabinet fireproof board
Cabinet fireproof plate can be classified into fiber cement fireproof board, metal fire proof board, mineral wool fireproof board, perlite fireproof board, all sorts of fire prevention board. Fiber cement fireproof board is a kind of ornament plate using siliceous or calcareous as main materials and combined with a certain proportion of fibre material; metal fireproof board is a kind of decorative plate made of aluminum plate, stainless steel plate, color steel plate and other metal materials as the main raw material and added by certain flame retardant materials. Mineral wool fireproof board is a decorative plate made of mineral wool and glass wool; perlite fireproof board is hollow fire proof plate made of low alkalinity cement as the main raw material, and supplemented by certain perlite with fireproof function as filling. Fiber cement fireproof board is a kind of new material increasingly gets popular with superior heat insulation, sound insulation performance, belonging to the A1 level fire materials 1, Suzhou total surplus purification A-grade fireproof rock wool colored steel rock wool board range of applications: Partition ceiling material: Rock wool reference price: On a square 58.00/2 meters, Huarui thermal insulation fireproof materials aluminum silicate refractory aluminium silicate A-grade fireproof heat insulation aluminium silicate plate temperature: 1000 core material: Reference price for aluminum silicate fiber cotton: $3500.00\ ton
Q:What are the fire resistance ratings of the glass partition?
The glass partition system is composed entirely of metal structures, glass, color plate and other materials which also has fire resistance capacity. When the inner structure of the system is steel structure, the fire resistance of which is 30 mins, 60mins or even longer. The fireproof glass is a special glass which is able to maintain its integrity and insulation in a fire resistance test. According to fire resistance performance, it can be divided into three categories: Class A: The fireproof glass which meets demands of fire integrity and fire insulation at the same time. This glass has advantages of excellent transmittance, fire-proofing(smoke resistance, fire insulation, and blocking heat radiation), sound insulation and impact resistance. It can be applied to architectural ornaments, fire resistant timber doorsets with steel structure, windows, upper beam, partition walls, daylighting roofs, ceiling screens, perspective floor and other building components which need transparency and fireproofing. Class B: The fireproof glass which meets demands of fire integrity and thermal radiation intensity at the same time. This glass is mostly composite fireproof glass which has advantages of transmittance, fireproofing, and smoke resistance. Class C: The fireproof glass which only meets demand of fire integrity. This glass has advantages of transmittance, fireproofing, smoke resistance and high intensity. It can be applied to fireproof glass partition walls, fire windows and with no requirements on outdoor curtain walls, etc. The fireproof glass can be classified as composite fireproof glass and single chip fire-proof glass in terms of structure.
Q:What is the most reasonable drying heating curve of magnesia refractories? Products of less than 0.5T
o
Q:What kind of refractory material should be used for common boiler?
Build by using clay refractory mortar. Common clay brick is used as combustion layer. Xindeyuan Refractory Material, red brick is used as external wall. Light clay brick is used as thermal insulation layer, thank you.
Q:Is the linear change on reheating the same as heating permanent linear change of refractory material?
“+”represents expansion. the afterexpansion and aftercontraction after cooled to be at room temperature. The change may significantly damage the masonry of thermal kiln. There are regulations on the linear change on reheating of common refractory material in the national standard. Some physical chemical changes may continue. It is defined as the change from being heated to the specified temperature of refractory material sample. Heat preserving for a while till afte cooling to be at room temperature, then the residual will expand or contract in its length, heat preservation for a while, organization vitrification, the irreversible changes of its length refers to heating the firing refractory to be at high temperature, so as to make the volume of refractory materials expand or contract, due to the influence of uneven temperature or lack of time, otherwise it will cause the deformation of the refractory ball and make this indicator within standard even reach smaller value, so firing control must be strengthened in product production. But it is should not be too high. For refractory materials with same chemical composition, the linear change on reheating is produced in the heating process. Properly increasing sintering temperature and prolonging the holding time is an effective process measures, make its firing inadequate. When subjected to high temperature, it can reduce the thermal shock resistance. Minus sign "-" represents contraction. The permanent line rate refers to heating the fire refractory ball to the specified temperature. Linear change on reheating, also known as residual linear change, is an important indicator to assess the quality of refractory in the long time use. To control the permanent line rate within the standard or reach the minimum value.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range