Refractory For Furnace Silica Fire Brick

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

silica fire brick
1.Stable Capability,
2.High Quality,
3.Excellent Service,
4.Competitive price

Silica fire Brick

With dense and smooth appearance, uniform corner and edge, pure color and luster and accurate size

1)Silicon oxide is above 95%.

2) Good acid erosion resistance.

3) High softening point with temperature.

4) No shrink in burn repeatedly.

5) Temperature of refractoriness under load is above 1650º C

Stable Capability, High Quality, Excellent Service, Competitive price is the most important advantage of our products

Item

BG-94

BG-95

BG-96A

BG-96B

Chemical composition

SiO2

≥94

≥95

≥96

≥96

Fe2O3

≤1.5

≤1.5

≤0.8

≤0.7

Al2O3+TiO2+R2O

≤1.0

≤0.5

≤0.7

Refractoriness °C

1710

1710

1710

1710

Apparent Porosity%

≤22

≤21

≤22

≤22

Bulk Density g/cm3

≥1.8

≥1.8

≥1.8

≥1.8

True Density,g/cm3

≤2.38

≤2.38

≤2.34

≤2.34

Cold Crushing Strength Mpa

≥24.5

≥29.4

≥35

≥35

0.2Mpa Refractoriness Under Load T0.6 °C

≥1630

≥1650

≥1680

≥1680

Permanent Linear Change On Reheating

(%)1500°CX2h

0~+0.3

0~+0.3

0~+0.3

0~+0.3

20-1000°C Thermal Expansich10-6/°C

1.25

1.25

1.25

1.25

Thermal Conductivity (W/MK) 1000°C

1.74

1.74

1.44

1.44


FACTORY:


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:what's the standard of fireproofing material?
first, the classification of fire resistant levels of buildings, 1, the classification basis of fire resistant levels of buildings, the classification of fire resistant levels of buildings is one of the basic building fire protection technology measures, our national architectural design specification divides fire resistant levels of buildings into first, second, third and fourth class, first class ios the highest and has the most strong fire-resistant capacity, fourth class is the lowest and has the weakest fire-resistant capacity. Fire resistant level of buildings depends on the combustion performance and fire endurance of the components of the buildings. construction components refer to the wall, base, beam, column, floor, stair, suspended ceiling and other basic components of buildings. Combustion performance and fire endurance of building components are shown in table 4-11), the combustion performance of building components are divided into non-combustible component,hard-comnustible component,combustible component,according to their response to the fire. as for building components, non-combustible component includes wall column and base,etc; hard-comnustible component includes hanging bracket, suspended ceiling and internal pipe;combustible component includes doors and windows, suspended ceiling, decoration materials,etc.
Q:Who can introduce the difference between galvanized fireproof coatings and steel structure fireproof materials?
Steel structure with heat galvanization has a process requirement, which is to spray fireproof coatings. Fireproof coatings have different functions and purposes from galvanized process. When the steel surface derusted, it generally needs to brush rich-zinc primer before spraying fireproof coating. Fireproof coating plan itself includes anticorrosion plan, and fireproof coating is just a layer of coating plans, which is an intermediate layer in general. Fireproof coating plan generally includes primer, fireproof coating and finishing paint. Some fireproof coatings can be directly painted on the bare steel elements without primer and finishing paint.
Q:What defect does fused cast refractories have ?
The impact on the quality of glass is mainly the defects that eroded down refractory materials mixed in the glass, thus being prodeced of grass products. Defects are mainly foreign body defects such as sand, knot and wave reinforcement.
Q:Why the refractories should be waterproof and wetproof
It is necessary to like magnesium carbon, waterproof and wetproof is more important. There is a variety of refractory materials, in general, basic is defective, and wherein the binder and additives water will lose their effect, the relationship is not very high aluminum large amount of water determines how much of the performance after the hydration will affect the strength and high temperature performance ;; hydration & quot, just need a little package like magnesium and calcium-based product itself readily react with water to calcium oxide, magnesium, chromium is not all the material goods have waterproof ordinary bulk materials need to add water before use
Q:Is refractory material harmful to human body?
The risk of mineral wool and glass fiber have cancer!
Q:How to do environmental impact assessment for refractory Co., Ltd.
The preparation of a report or statement. During the compilation process, any problems should be actively communicated with the construction side. For example, dust collector selection, environmental protection investment, total emission approval. (especially the total emission, you must let the construction side and communicate with the environmental protection bureau to get the total amount, otherwise you write the EIA does not make any sense.) Generally speaking, the preparation of the report is longer, about forty days; and the preparation of the report table is shorter, about fifteen days.
Q:What are the basic requirements of continuous casting for molten steel? What are the requirements for refractory materials?
The rapid development of the technology of continuous casting refractories so the corresponding development and improvement in variety and quality, continuous development of refractories for the continuous casting billet continuous casting production and quality have a significant impact. Especially, the completion and operation of Baosteel have greatly promoted the technological progress of refractory materials in China, and the refractory materials for continuous casting have made great progress both in variety and in quality.
Q:What is the importance of silicon powder in refractory processing?
it can certainly improve the fire resistance
Q:What are the characteristics of magnesium fireproof plate
Plate glass magnesium fire with high temperatures, flame retardant, sound absorption, shock-proof, pest control, anti-corrosion, non-toxic tasteless non-polluting, can be used directly on the painting, direct veneers, available gas nail directly on the tile, the surface has good coloring , high strength, resistance to bending toughness, nails, saw, can be sticky, easy decoration. It can also be made into thermal insulation materials with a variety of compround composite insulation plate.
Q:Who knows what material is in the center of fireproof rolling curtain?
made of inorganic super fireproof rolling curtain: Glass fiber cloth ceramic fiber cloth (reinforced stainless steel wire) ceramic fiber blanket aluminum foil cloth. Hope my answer will help you.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range