High-Aluminum Refractory Brick

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Chat Online

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Item	Fireclay brick	High Alumina Brick
SK32	SK34	SK35	SK36	SK37	SK38
Al₂O₃ (%) ≥	38	42	48	55	65	75
Refractoriness (^oC) ≥	1670	1730	1750	1770	1790	1790
Refractoriness under Load, ^oC,0.2MPa ≥	1250	1300	1420	1470	1500	1520
Linear Change(%), ^oC×2h	1350	1350	1450	1500	1500	1500
-0.5~0	-0.5~0	-0.4~+0.1	-0.4~+0.1	-0.4~+0.1	-0.4~+0.1
Porosity (%)≤	26	26	22	22	23	23
Cold Crushing Strength, MPa≥	15	20	39.2	44.1	49	53.9

Features:

Strong volume stability in high temperatures
Good thermal shock resistance, wear resistance and erosion-resistance

Applications:

Transitional zone and preheating zone of cement rotary kilnand other thermotechnical equipment which requires thermal shock resistance.

Q:How much is the bending temperature aluminum silicon carbide brick for torpedo car: High alumina brick is made of superfine alumina, fused corundum and fused mullite as main refractory materials.

Q:High alumina brick 80 with which high aluminum cement?: Which kind should be chosen should be determined according to the conditions of use, life expectancy and cost control. By the way, the quality of masonry is also very influential.

Q:How to distinguish the good or bad of the high aluminum brick?: The general high alumina bricks used in the steel, steelmaking, hot blast furnace, electric furnace, blast furnace, reverberatory furnace, rotary kiln lining of industrial furnace in China, mainly composed of a bauxite; sillimanite minerals (including kyanite, andalusite, sillimanite etc.); synthetic material, such as alumina synthesis of mullite, corundum, etc.. High aluminum brick has good quality, high refractoriness, long life and other characteristics, is the main use of refractory brick kiln products, commonly used units can not distinguish the quality and grade of high aluminum brick right in the procurement time, caused by the high prices to buy low grade products, thereby reducing the furnace life therefore, Zhengzhou's Sindh yuan refractory material factory in here is simple to introduce how to identify the quality when purchasing brick high alumina brick.Color: in the purchase of high alumina brick, first of all to see the color, high quality aluminum brick surface smooth, yellow color white, four sides smooth, no broken angle, no cracksWeight: the weight of a block of bricks to be called, according to the standard weight level, high aluminum brick weight of 4.5 kg. Two grade high alumina brick weighs 4.2 kg, three high aluminum brick weighs 3.9 kg, the same level, the same parameters can reach this standard can be regarded as high-quality high aluminum bricks, the opposite is not up to the weight that the quality is good, if there is a crack, four angle uneven, off angle phenomenon, then substandard products, some of the above points to help to the purchaser

Q:What are the requirements for refractory materials in heat treatment furnace?: The structural strength of high temperature is evaluated by loading softening point. Load softening point is that under certain pressure (2 kg/ cm 2 = 0.2MPa) under the condition of heating rate to heating, measured the sample deformation (deformation for the original sample 0.6%) temperature. This temperature is called the softening point of the refractory. Sample size is Phi 36 x 50mm.

Q:Difference between low creep high alumina brick and ordinary high alumina brick: The emphasis is on the physical and chemical indexes of low creep and high alumina bricks. The physical and chemical indexes of the high alumina bricks are different, too. They are DRL-1550And LZ-75 perform GB GB/T2988-2012

Q:How much is one ton of high alumina refractory brick?: Three high aluminum refractory brick Zhengzhou Kuwait is generally around 800. 32 years of experience, good.

Q:Which thermal shock stability of clay brick and high alumina brick is good?: The product has the advantages of high temperature, little creep, strong corrosion resistance and good thermal shock resistance, and is suitable for large and medium-sized hot blast stoves.Thermal shock stability is much better than clay brick.

Q:The difference between clay bricks and clay bricks: According to the hole rate: solid brick (no hole or hole rate less than 25% bricks), porous brick (hole rate is equal to or greater than 25%), the size of the hole is small and the number of bricks, usually used in load-bearing parts, higher strength level. Hollow brick (hole rate equal to or greater than 40%, large pore size and small amount of brick, commonly used in non load parts, low strength grade).Solid bricks and porous bricks are mostly used for load-bearing structural walls. Hollow bricks are mostly used in non load bearing structures.

Q:What are the grades of high alumina bricks?: High alumina brick according to the aluminum content is generally divided into: super high alumina brick, a high aluminum brick, two high alumina brick, three high alumina brick

Q:What is the heat preservation material used in a laboratory furnace?: Silicon carbide (SiC) is made from quartz sand, petroleum coke (or coal tar), sawdust (green salt produced when adding green silicon carbide) and other raw materials by smelting with resistance furnace at high temperature. Silicon carbide also rare minerals in nature, Mo sangshi. Silicon carbide, also known as carbon silica. Silicon carbide is the most widely used and the most economical kind of refractory materials in C, N, B and other non oxide refractory materials. It can be called "carborundum sand" or "refractory sand".

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range