Factory Directly 85% Al2O3 1-3mm Calcined Bauxite

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
25 m.t.
Supply Capability:
12000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Factory Directly 85% Al2O3 1-3mm Calcined Bauxite

Specifications

We can supply Calcined bauxite,Mullite low cement castable,Corundum low cement castable,mullite Ramming Mix etc.

Application:  they are widely used in various kinds of kiln lining.Such as boiler, blast furnace hot blast stove, heating furnace, ceramic kiln, etc

 

Specifications of Calcined bauxite

Grade

AL2O3

SIO2

FE2O3

TIO2

K2O+Na2O

CaO+MgO

Bulk density

HX75

75min

≤17

≤3.0

≤4.0

≤0.3

≤0.5

≥2.70

HX80

80min

≤12

≤3.0

≤4.0

≤0.3

≤0.5

≥2.80

HX85

85min

≤8

≤2

≤4.0

≤0.3

≤0.5

≥3.00

HX86

86min

≤7

≤2

≤4.0

≤0.3

≤0.5

≥3.10

HX87

87min

≤6

≤2

≤4.0

≤0.3

≤0.5

≥3.20

HX88

88min

≤5

≤1.8

≤4.0

≤0.25

≤0.5

≥3.25

HX90

90min

≤3

≤1.8

≤4.0

≤0.25

≤0.5

 ≥3.3

Moisture(max)

0.50%

 

Usage of Calcined bauxite

1.Aluminium industry.
2.Precision casting.
3.Refractory industry.
4.Silicic acid aluminium firefibre
5.Mixed with magnesium oxide,it can be an nice bonding agent,especially for pouring entire steel          teeming ladle lining
6.Manufacture bauxite cement,grinding abrasives.ceracmic industry,and chemical industry for making    aluminium compounds

 

Pictures

Factory Directly 85% Al2O3 1-3mm Calcined BauxiteFactory Directly 85% Al2O3 1-3mm Calcined Bauxite

Factory Directly 85% Al2O3 1-3mm Calcined BauxiteFactory Directly 85% Al2O3 1-3mm Calcined Bauxite




Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What's the feature of construction external wall fireproof and thermal inuslation matertial?
It has properties of low heat conductivity coefficient, low density, high flexibility, fireproof and waterproof. Its heat conductivity coefficient at normal temperature is 0.018W / (K · m) . The thermal insulation property is three to eight times that of the traditional materials. And it is completely waterproof. [2] Thermal insulation lining has properties of low heat conductivity coefficient, low density, high flexibility, fireproof and waterproof. Light, generally about10-96kg / m3, 20kg / m3 or less is felt, 24-48kg / m3 is middle-hard plate, 48-96kg / m3 is hard plate, wherein 48kg / m³ can be used as ceiling, with softening point being 500 ° C , thermal insulation 300 ° C. It is widely used in the United States, k =0.9. Calcium silicate thermal insulation product is developed in 1970s in China. With high compressive strength, low heat conductivity coefficient, recycle and easily construction, it is widely used in the power system. In China, small workshop production were the most common, then four production lines were gradually introduced from America, including instant fiber forming, dry method punched felt, which are advanced and quality, temperature endurance up to 800-1250 ° C.
Q:What things and cement mixed can act as refractory?
This has a lot. I suggest you can check monolithic refractories.
Q:Why do magnesium oxide refractory bricks can be made into refractories?
Because the magnesium oxide, commonly known as magnesia, which is a basic oxide, with the common property of alkali oxides and belongs to the cementitious material . It is white or light yellow powder, odorless, tasteless, non-toxic and a typical of alkaline earth metal oxide, whose chemical formula is MgO. It is white powder, with melting point of 2852 ℃, boiling point of 3600 ℃ and relative density of 3.58 (25 ℃). The magnesium oxide that is soluble in acid and ammonium hydroxide solution has high insulation properity. After high temperature of above 1000 ℃ burning, it will transform into crystals, and when rising above 1500 ℃ , it will turn into dead-burned magnesium oxide (also known as the magnesia) or sintered magnesia. So the performance of magnesium oxide refractory bricks is good, and the fire resistance of it is very strong.
Q:what needs to be noted when choosing and using blast furnace fireproof materials?
Hello,: three parts of the blast furnace lining in general are easily corroded. The first one is furnace bosh,second is the middle part of the furnace, The third is lower part of the furnace stack. if These parts are damaged, then we need an overhaul. Bosh, because damage to the middle part of the furnace and the furnace bosh are generally due to alkali metal and fusant erosion. the main reason for the lower furnace part damage is molten iron, slag. In view of this situation, mullite bricks, corundum bricks, silicon carbide bricks are used for reparation. make repairments as soon as possible if any problems occur in case of incidents.
Q:What are the models of bauxite with high alumina?
China Ferrous Metal Industry Corporation released the industry standard of bauxite (YS / T78-94) in 1994. According to this standard, bauxite can be divided to sedimentary diaspore, stacked type diaspore and lateritic gibbsite. According to the chemical composition, it can be divided into nine trade marks as LK12-70, LK8-65, LK5- 60, LK3-53, LK15-60, LK11-55, LK8-50, LK7-50 and LK3-40. In addition to the provisions of chemical composition of bauxite, the standard also requires that the water of sedimentary diaspore shall not exceed 7% and water of stacked type diaspore and lateritic gibbsite shall not exceed 8%. Moreover, particle size of bauxite should be not greater than 150mm. Bauxite shall not be mixed with clay, limestone and other debris.
Q:The classification of fire-resistant material
Refractory material cna be divided into common and special fire proofing material. Common fire proofing material can be sub-divided in to acid fire proofing material, neutral fire proofing material. and alkaline fire proofing material according to chemical properties. Special fire proofing material can be divided into high temperature oxide refractory, refractory compounds and high temperature composite materials according to the composition. In addition, it also can be divided into common refractory products (1580 ~ 1770 ℃), high-grade refractory products (1770 ~ 1770 ℃) and super refractory products (above 2000 ℃) according to the strength . According to the shape, it can be divided into block (standard brick, special-shaped brick, etc.), special shape (crucible, sagger, pipe, etc.), fibrous (aluminum silicate, zirconia and boron carbide, etc.) and irregular shape (refractory clay, refractory castable, ramming material and so on). According to sintering process, it can be divided into sintered product, fused cast product and melting jetting product.
Q:What's the fire endurance of fire windows?
Fire endurance of fire windows: A class fire window: no less than 1.2h; B class fire window: no less than 0.9h; C class fire window: no less than 0.6h. Technical requirements: 1. Materials and fittings: (1) Window frame should adopt the steel frame or wood frame with certain strength so as to guarantee the integrality and stability of the fitting; (2) Steel frame and mound layer can choose the galvanized steel sheet or stainless steel sheet. Its selection standard is in line with provisions of Article 5.1 in GB12955 "General Technical Requirements on Steel Fire Doors"; (3) Selection standard of wood frame and mound layer should be consistent with the provisions of Article 5.1.1 in GB14101 "General Technical Requirements on Wood Fire Doors"; (4) Filler material inside the steel frame and wood frame should be incombustible material; (5) Fireproof glass can choose the qualified product with no influence on the fire resistance test of the fire window, and its light transmittance should be no less than 75% of that of the ordinary sheet glass with the same layers; (6) Sealing material between the frame and the fireproof glass should use flame retardant material which can play the role of fire prevention and smoke control in the case of fire. (7) Hardware fittings should be approved supporting products which is detection qualified.
Q:Which are fire proofing thermal insulation materials?
Fire proofing thermal insulation materials include: fire proofing heat insulating brick, fire proofing thermal baffle, fire proofing thermal insulation paper, fire proofing thermal insulation felt, fire proofing blocking, fire proofing fiber bulker, castable refractory, etc. In addition, there are also auxiliary products such as fire proofing cement gum, high temperature binder.
Q:hat kind of fire retardant materials are there
There are many flame retardant plastics, which are modified on the basis of raw materials, such as flame-resistant ABS, flame-resistant HIPS, flame-resistant PP, flame-resistant PE, flame-resistant the PET, flame-resistant PBT, flame-resistant PC, flame-resistant PC/ABS alloy. Now there are mainly halogen flame retardant, though there are a lot of researches about halogen free flame retardant, the product stability and flame retardant effect remain to be improved. Testing methods of flame retardant materials are mainly: horizontal and vertical combustion, oxygen index method, NBS smoke box , thermal analysis, cone calorimeter, etc.
Q:The primary problem, does the gas permeable brick is fired refractory bricks(refractory) ?
gas permeable brick have two types:built-in type and external mounted type. the built-in gas permeable brick and the external mounted gas permeable brick are usually made by fire burning, and small part of bricks are made by the low temperature heat.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range