Q:What is the effect of coke moisture on the blast furnace?

1, a large number of high coke moisture (when the rain open storage of coke in blast furnace smelting coke), if not timely load back down, will cause a relatively large impact on the furnace, coke is better then no timely adjusting load will cause heat phenomenon.

Q:Do not understand why some of the indicators of coke is the cause of the full analysis of phosphorus or foundry use of this time?It is best to use the foundry requirements? Thank you

Foundry coke is used in cupola melting iron will fuel. Because the blast furnace cupola and metallurgical industry is different, only melting effect, without reduction reaction, the furnace is not so dephosphorization, the phosphorus in coke, some will come back to this in the metallurgical molten iron, called "Rephosphorized", this is decided by the principle of thermodynamics and kinetics. To make the original low phosphorus iron phosphorus increased harmful phosphorus. Therefore, the general foundry to buy Coke require low phosphorus coke. Some foundry with part of lime and dolomite in dephosphorization of iron in cupola, in the process, can relax the requirements for coke. However, this is suitable for large-scale, continuous production of iron.

Q:I see that there are metallurgical coke and coke on the Internet, what is the difference between them (I hope to be able to say in detail) and a level of two points, how is this going on?.. Where is the quality of coke in China? Hunan good coke plant which? Although the problem is a little bit more, I hope that insiders can give some useful information. Extremely grateful.

I see that there are metallurgical coke and coke on the Internet, what is the difference between them (I hope to be able to say in detail) and a level of two points, how is this going on?.. Where is the quality of coke in China? Hunan good coke plant which? Although the problem is a little bit more, I hope that insiders can give some useful information. Extremely grateful.

Q:In the coke analysis index, M40% and M25% respectively mean what?

(2) mainly used in: Coal Science and Technology (first level), coal processing and utilization (level two), coal chemistry and coal quality analysis (level three)

Q:The chemical composition of coke is m10.m25

Quality index of cokeThe quality index of coke coke [] is a solid product of high temperature carbonization, the main ingredient is carbon, is the pore structure has a crack and irregular (or pore porous). The crack number directly affects the coke strength and crushing strength, the index of general degree (refer to how to crack crack length unit the volume of coke in the measure.) to measure the pore structure of the main indicators for the porosity (coke pore volume only percentage of the total volume) that it affects the coke reactivity and strength

Q:Coke can be used to do what carbon black can be used to do?

2 carbon black is produced by compounds of carbon and carbon, the main hydrocarbon combustion, the combustion is not sufficient, can not be converted into carbon dioxide, is carbon monoxide, so as small particles of carbon particles, which is carbon black; carbon black can be used as filling agent of rubber mixture, preferably for tires.

Q:What is the concept, relationship and difference between coke and coke? The main difference and contact, thank you

6, the horizontal type coke oven drying machine(7) gas purification circulating water.... supporting technology(8) dry cooling technology of interlayer water-cooled steam.(9) microcomputer precise dosing system

Q:What chemical plant used to coke

Under the condition of isolated air, the bituminous coal is heated to 950-1050 DEG C, and finally, the coke is made by drying, pyrolysis, melting, bonding, solidification and shrinkage

Q:What does the M40% and M25% mean in the analysis of coke?

(2) mainly used in: Coal Science and Technology (first level), coal processing and utilization (level two), coal chemistry and coal quality analysis (level three)

Q:What are the national standards for grade two coke?

Volatile content is not greater than 1.80; crushing strength: M40:76.1 - 80, M25:88.1 - 92; wear resistance: M10: not more than 8.5;