Q:Do not understand why some of the indicators of coke is the cause of the full analysis of phosphorus or foundry use of this time?It is best to use the foundry requirements? Thank you

Phosphorus increased the brittleness of cast iron, the use of metal damage. Therefore, the requirements of the foundry phosphorus is the lower the better. Because of the large cupola furnace in the furnace is acidic, can not effectively dephosphorization, so the foundry coke in the phosphorus requirements as low as possible, and require the supplier to provide a quality guarantee form.

Q:I see that there are metallurgical coke and coke on the Internet, what is the difference between them (I hope to be able to say in detail) and a level of two points, how is this going on?.. Where is the quality of coke in China? Hunan good coke plant which? Although the problem is a little bit more, I hope that insiders can give some useful information. Extremely grateful.

Coke is a special and molten iron cupola coke. Coke is the main fuel cupola molten iron. Its role is to melt the burden and make the hot metal overheating, the support column to maintain good ventilation. Therefore, the foundry coke should have large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough

Q:What are the indicators of first grade coke and the two grade coke?

The mechanical strength of the mechanical strength of ash sulfur%% volatile(crush strength M40) (abrasion strength M10)

Q:What is the reasonable standard of volatile content of coke

The sulfur content in coke: sulfur is a harmful impurity of iron smelting, which reduce the quality of pig iron. The sulfur content in the pig iron is more than 0.07%.

Q:Coke in the whole process of steelmaking in the end is what to do, just to provide heat or carbon and other substances into steel or iron?In the study of coal classification inside, one is divided into coking coal, coking coal and coke as main, and then you see is steel or iron coke must material. What is not clear. In the end, out of coal mining is mainly used to burn energy extraction, or said that coal like oil can be converted into other products, which is a coke can convert?

Coke is not used for blast furnace ironmakingThe use of blast furnace burden include iron ore (natural ore, sinter and pellets), solvent (limestone or dolomite), and coke, charge from top order batch into the furnace. Coke in the blast furnace ironmaking can be summarized as follows:(1) provide the heat: coke in the coke oven in front of the raceway in the intense combustion, combustion heat generated in the blast furnace smelting process is the main heat source(2) reduction: high temperature gas generated in coke combustion in the raceway, passed to the material in the process of heat rising, the endothermic reaction and coke formation, CO and H2, then CO and iron oxide in iron ore reduction reaction is transformed into metallic iron.

Q:The chemical composition of coke m10.m25 refers to?

M10 refers to the wear resistance of coke, M25 refers to the crushing strength is the mechanical strength. Mainly the cold strength of coke. Coke is also the most important indicator is the hot state, CRI thermal reaction and CSR reaction intensity. In blast furnace production, both cold and thermal strength are important.

Q:Some experimental results summarized the following two facts: the coke can not be used to restore aluminum mine, but it can be used for the reduction of copper and iron; no containing copper sulfate solution with tin, thus the activity sequence C, Al, Cu, Fe of the four elements is ______.

There is no containing copper sulfate solution with tin. Because the copper iron can be displaced from the salt solution in their description, copper and iron;To sum up, we can know that C, Al, Cu, Fe four elements of the order of activity is Al > C > Fe > Cu;The answer is: Al > C > Fe > Cu.

Q:What are the quality indicators of coke

Different uses of different coke porosity index requirements, the general requirements of metallurgical coke porosity in the 40 ~ 45%, 35 ~ 40% in coke, coke export demand in about 30%. Coke crack degree and the porosity level, and the coking coal has a direct relationship, such as coal based coke refining, crack, high porosity, low strength; with coal as the foundation of the coal refining coke crack less, low porosity and high strength. The strength of coke is usually represented by two indices of crushing strength and abrasion resistance. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10 value method, commonly used in our country the German migon drum test. Evaluation of the quality of coke, 1 of sulfur in coke: sulfur is a harmful impurity of iron smelting, which reduce the quality of pig iron. The sulfur content in the pig iron is more than 0.07%. 11% of the sulfur from the blast furnace charge into the furnace comes from the ore, and the other comes from the limestone; the other is from the coke, so the coke is the main source of sulfur in the charge of the 82.5% of the charge. Sulfur content in coke directly affects the production of blast furnace. When the sulfur content in coke is greater than 1.6%, sulfur increased 0.1%, the amount of coke increased 1.8%, limestone amount increased 3.7%, 0.3% increase in amount of ore blast furnace output to reduce the sulfur content under 1.5 - 2.0%. metallurgical coke is not greater than 1%, the use of large and medium-sized metallurgical coke content in blast furnace is less than 0.4 - 0.7%

Q:What is the density of coke?

There is also a parameter is also available for your reference: coke porosity of 35% ~ 55%The above parameter is a general range, according to the need to choose to determine.

Q:Can the sulfur content of coke affect the casting process of nodular cast iron at 0.65?

The high sulfur content of nodular cast iron, the most significant impact on the casting is caused by poor balling,