Types of Glass Fusing Kiln Refractory Bricks Silica Brick

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
10 m.t.
Supply Capability:
10000000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Physial properties and chemiacal composition:   

Item

BG-94

BG-95

BG-96A

BG-96B

Chemical composition

SiO2

≥94

≥95

≥96

≥96

Fe2O3

≤1.5

≤1.5

≤0.8

≤0.7

Al2O3+TiO2+R2O


≤1.0

≤0.5

≤0.7

Refractoriness °C

1710

1710

1710

1710

Apparent Porosity%

≤22

≤21

≤22

≤22

Bulk Density g/cm3

≥1.8

≥1.8

≥1.8

≥1.8

True Density,g/cm3

≤2.38

≤2.38

≤2.34

≤2.34

Cold Crushing Strength Mpa

≥24.5

≥29.4

≥35

≥35

0.2Mpa Refractoriness Under Load T0.6 °C

≥1630

≥1650

≥1680

≥1680

Permanent Linear Change On Reheating

(%)1500°CX2h

0~+0.3

0~+0.3

0~+0.3

0~+0.3

20-1000°C Thermal Expansich10-6/°C

1.25

1.25

1.25

1.25

Thermal Conductivity (W/MK) 1000°C

1.74

1.74

1.44

1.44

 

Types of Glass Fusing Kiln Refractory Bricks Silica Brick


FAQ

Q1: How do you control the products quality?

A1: With strict quality control system throughout the materials selection and production process, our refractory and ceramic fiber products quality is effectively controlled to meet customer requirements.

From the raw materials selecting, our quality control begin. The quality certificates of raw materials are required and each batch will be tested before using. During production, the quality control are conducted by workers and then each piece will be sorted and examined by quality supervis

Q4: What is the minimum quantity?

A4: There is no minimum order quantity. Depending on the item and processing, there may be a minimum production required, however we can offer a quotation based only on the quantity you need.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What role does silica play in refractories?
The natural mineral of silica is called quartz. In refractories, silica and siliceous refractory materials contain more silica. Silica is acidic at high temperature, and siliceous refractory can resist acid slag corrosion
Q:The high thermal conductivity of silica brick and traditional brick what is the difference?
Tridymite content high thermal conductivity silica brick is 70%, tridymite content of traditional brick is 60%, tridymite content high thermal conductivity of silica brick than tridymite high content of 10% traditional brick,
Q:Which material is good for furnace refractory?
Basic refractories in Magnesium Oxide and calcium oxide as the main ingredient, commonly used is brick. Magnesium Oxide 80% to more than 85% containing magnesia brick, has good resistance to alkaline slag and slag, refractory clay brick and brick high ratio. Mainly used in open hearth furnace, oxygen converter, electric furnace, non-ferrous metal smelting equipment and high temperature equipment.
Q:What are the materials for refractory materials? What are their names?
Classification of chemical components of refractory materialsAccording to the chemical characteristics of refractory raw materials can be divided into acidic refractory materials, such as silica, zircon etc.; neutral refractory raw material, such as corundum, bauxite, mullite (acidic) (acidic), Ge (alkaline) iron and graphite; alkaline refractory materials, such as magnesite, dolomite, magnesium sand calcium sand.
Q:The production of brick, the ingredients of why join the waste brick
Preparation of silica brick pug, a certain amount of waste silica brick used to add ingredients, for the purpose of expansion and stress reduction products when firing, reduce cracks, improve the rate of finished products.
Q:Why in the production of the brick to detect the volume density
Density is the property of material, different density of materials, density of the same kind of material is not up to standard, affecting performance.
Q:The difference between clay refractory bricks and refractory brick in the application.
Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.
Q:The United States of our brick anti-dumping duties?
At present of our brick anti-dumping rate is 73.10%
Q:The difference between clay refractory bricks and refractory brick in the application??
Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.
Q:How to improve the thermal conductivity of the coke silicabrick rate?
The content of SiO2 is 98.23% crystalline silica as raw material, with sulfite pulp liquid as binder, millscale and lime as mineralizer, by Jin Hongshi (TiO2) as additive, can improve the rate of thermal conductivity of silica brick for coke oven. When the rutile content is 1.5%, the coefficient of thermal conductivity of silica brick for coke oven is 2.66W/ (m.k).

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range