Top Quality Forged Grinding Balls For Cement and Mine

Ref Price:
Loading Port:
Shanghai Port
Payment Terms:
TT or LC
Min Order Qty:
25M.T. m.t.
Supply Capability:
200000M.T./Year m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specification of Top Quality Forged Grinding Balls For Cement and Mine

No.

Diameter

(mm)

Weight of each

(kg)

Pcs/ton

1

Ø20

0.0322

31056

2

Ø25

0.063

15873

3

Ø30

0.11

9091

4

Ø40

0.257

3891

5

Ø50

0.50

2000

6

Ø60

0.867

1153

7

Ø70

1.37

729

8

Ø80

2.05

487

9

Ø90

2.90

345

10

Ø100

4.00

250

11

Ø110

5.30

188

12

Ø120

6.80

147

13

Ø125

7.75

129

14

Ø130

8.74

114

 

The Product Description of Top Quality Forged Grinding Balls For Cement and Mine

Model

Mechanical properties

Microstructure

HRC

Times of falling (5m)

Low Chromium

≥45

8000

P+C

Medium Chromium

≥55

10000

P+C

High Chromium

≥60

10000

M+C

 

Chemical Composition of Top Quality Forged Grinding Balls For Cement and Mine

Model

Chemical Composition

C

Si

Mn

Cr

P

S

Low Chromium

2.3-3.4

≤1.5

0.7-1.5

1.3-2.7

≤0.1

≤0.1

Medium Chromium

2.2-2.8

0.5-1.0

0.7-1.0

11.0-15.0

≤0.1

≤0.1

High Chromium

2.4-3.2

0.5-0.8

0.7-1.2

15.0-18.0

≤0.1

≤0.1

 

10-15days after the contract

Container Bag: Dia20mm-Dia150mm 1000Kgs/Container Bag (GWt:1002Kgs)
Steel Drums: Dia20mm-Dia80mm 900Kgs/Drum (GW: 915Kgs)
 
Dia90mm-Dia150mm 850Kgs/Drum (GW: 865Kgs)

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Where is the precision casting factory?
The National Precision Casting Factory is generally distributed in Shandong, Ji'nan, Jiangsu, Wuxi, Changzhou, Zhejiang, Guangdong, Panyu, Dongguan.The above are only the main distribution, many of Shandong are made supercharger, and Guangdong to jewelry industry based.
Q:Younger brother is to do casting valve, precision casting parts, the valve internal sand serious, but the appearance is very standard, this is why, for God answers, thank you!
Increase the refractoriness and looseness of core sand
Q:How about casting parts for a year?
There are various casting stresses after casting, which can be divided into two kinds: thermal stress and shrinkage stress. In a long time placed in the atmosphere, called aging treatment.Aging treatment is an effective measure to eliminate casting stress. Aging is divided into natural aging, thermal aging and resonance aging.1, the so-called natural aging, the casting is placed in the open field for more than half a year, so that the internal stress relief.
Q:What reason is the bronze statue choking fire?
The casting process in boiling phenomenon, is the setting of the exhaust hole positioner position or number is not reasonable, the air cavity can not be discharged, overwhelmed by a material inlet, reflux, change mould, sincerely help you look forward to adopt,
Q:Is the cast steel a casting part?
Cast steel is one of the casting parts that you call. The material is made of carbon steel or alloy steel, stainless steel, etc. the method is cast
Q:How to solve casting defect casting?
Different defects, different solutions, some shortcomings, the current domestic level can not be resolved
Q:What kind of casting process is used for cast iron parts? And what are the cast steel parts adopted?
Corundum sand: the main mineral composition is corundum alpha -Al2O3, used for investment casting, ceramic mold casting shell materials. The olivine sand: the main mineral composition of olivine (MgFe) 2SiO4, used in cast iron, non-ferrous alloy castings and high manganese steel casting molding sand and the core sand. Silica resources in nature resources, but suitable for casting with high SiO2 content of natural silica sand is not too much. Since 1951, China has carried out a general survey of the casting sand resources in the territory, but mainly limited to the main traffic lines and major industrial cities. Survey results show that Chinese can be used for natural silica sand casting is very rich in resources, a wide range of distribution. Inner Mongolia Zhelimumeng, natural silica sand reserves amounted to hundreds of millions of tons, the particle shape close to the circular, the content of SiO2 is about 90%. Fujian, Jinjiang Dongshan sea sand, the content of SiO2 is 94 to 98%, with a low volume of mud, are good natural silica sand. Are Duchang, Yongxiu Jiangxi County Xingzi, a large number of Quaternary lacustrine deposition of silica sand, the content of SiO2 is about 90%, low iron content, alkaline oxide less, uniform size, is a good lake sand. Guangzhou, Hunan and other places have abundant easily broken weathered sandstone, processing artificial silica sand, the content of SiO2 in more than 96%, can be used for the production of steel castings. Jiangsu Nanjing red sand, sandy mud pure, moderate, strong permeability, good viscosity, high silica content, less water, fine particles, pulls out the casting is smooth, stable quality, can be made of cast iron and non-ferrous metal parts of the sand and core sand
Q:How can the casting be quenched and tempered?
Another is the result of pre heat treatment (quenching or annealing) after quenching and tempering treatment, suitable for ZG35SiMNMo, ZG35CrMo and so on. Please tell the casting process is your product and material and then set tempered.: shutup:
Q:What are the design considerations for casting parts?
(3) to prevent generating white grey cast iron, in addition to taking measures from the process, must make the wall thickness is not too thin (some sources indicate that the corner wall thickness above 15mm, metal type casting must be in the corner, for Aluminum Alloy, magnesium alloy casting casting casting Create fillet should not be less than 3-4m, for casting round cast iron, copper alloy mould casting can see table 1.1-32 selection; (5) because of the metal and the core without let, for the convenience of the casting is taken out and the draw out type, slope casting casting should be suitably large than sand casting metal casting. General 30%-50%, it should be pointed out that in addition to the height of the slope of casting size and alloy type, wall, is also related to the casting surface position, where the cooling and contraction and metal surface of casting surface can be designed from the tendency of small inclination, while casting shrinkage tend to be pressed on the surface of metal castings the type should be given greater inclination, all kinds of metal type alloy casting casting casting.
Q:What are the general technical requirements for casting parts?
According to the national standard GB/T 9438, there are 8 aspects: 1. chemical composition; 2. delivery status; 3. mechanical properties; 4. dimensional tolerances; 5. weight tolerances; 6. appearance quality; 7. internal quality; 8. casting salvage.
Grinding Prince was established in February, 2004 with an area of 24,400 square meters. Our company is an outstanding private enterprise specializing in the production of wear-resistant, corrosion-resistant, and heat-resistant alloy iron and steel castings. Currently, our production capacity of various types of wear-resistant casting balls and heat-resistant steel castings is 10,000 tons.

1. Manufacturer Overview

Location Anshan City, Liaoning Province,China
Year Established 2002
Annual Output Value US$1 Million - US$2.5 Million
Main Markets Domestic Market; South America; Eastern Asia; South Asia; Mid East
Company Certifications ISO9001;IS014001 Certificate

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port Shanghai Port;Dalian Port;Tianjin Port;Yingkou Port
Export Percentage
No.of Employees in Trade Department 6 - 10 People
Language Spoken: English; Chinese; Spanish
b)Factory Information  
Factory Size: 24,400 square meters
No. of Production Lines Above 10
Contract Manufacturing grinding ball,grinding media,casting ball,casting grinding ball
Product Price Range Average