Silicon Wear-resistant Magnesite Refractory

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

1.High crushing strength
2.High hot strength
3.Good thermal shock resistance
4.Strong anti-stripping resistance

Characteristic:

  • High crushing strength

  • High hot strength

  • Good continuously forming protective layer during service

  • Good wear resistance,

Trademark

AZM-1 550

AZM-1650

AZM-1680

Item

Index

Index

Index

Chemical composition(%)

SiC+SiO2

≥35

≥30

≥32

Al2O3

≥60

≥65

≥65

Volume density(g/cm3)

≥2.55

≥2.65

≥2.70

Apparent porosity(%)

≤20

≤19

≤19

Cold crushing strength(Mpa)

≥80

≥90

≥100

Refractoriness under load(T0.6,°C)

≥1550

≥1650

≥1680

Thermal shock resistance,time(1100°C,water-cooling)

≥10

≥15

≥20

1) Good performance to thermal shock, corrosion, erosion and abrasion resistance.
2) High refractoriness and excellent mechanical strength.
3) Both intermittently and continuously working mode are acceptable, reducing lining cracks.
4) Longer and stable life cycle to reach high efficiency.
5) Suit for all kinds of metal types, reduce residue and porosity of the products.
6) Labor and cost saving by convenient installation and maintenance

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What kind of material is good for cabinet fireproof board
What kind of material is good for cabinet fireproof board What are the advantages and disadvantages of using it? How much is the price? A about how much does one piece cost?
Q:What's the A class fireproof and thermal inuslation matertial for external wall?
It is roughly divided into thermal insulation mortar, phenolic foam board, rock wool board, foamed cement board, etc. Insulation mortar is quite good for its simple construction, convenience and low cost, but its production is too simple to make fake products easily. If you want to use the material, it is suggested to find a large plant with complete procedures such as provincal records of production and use, city records, test report above provincial levels, national fire inspection report, design drawings sheets of Department of Construction, etc. If there is lack of any one, it is unsafe. Hope my answer is helpful for you.
Q:What brands are the best in the A-level refractory materials?
1 International (It is a well-known brand in the field of global boats and protective coatings, the products are famous for its safety, strength and smoothness, Akzo Nobel (China) Investment Co., Ltd.) 2 LANLING (It is a high-tech enterprise, and a large provider of industrial coatings, started in 1980, as well as a famous brand of Jiangsu Province, Jiangsu Lanling Chemical Group Co., Ltd.) 3 Champion (It is a high-tech enterprise who is involved in developing a number of industry standards, it is a industry-leading brand brand of Jiangsu Province Jiangsu champion coating Technology Group Limited) 4 BBMG Coating (It is a large coating enterprise and a leading brand of fire-resistant coating who draft up the fireproof coating industry standards, Beijing BBMG Coating limited liability company) I hope my answer can help you .
Q:How to distinguish the fire rating of rubber and plastic thermal insulation material?
It is divided into level A, B1, B2 and B3. According to the current "burning behavior of building materials classification method", Level A insulation material is a non-combustible material, which belongs to YT. However, from the point of view of the current market , level A insulation material are very few, only glass wool, rock wool board, foam glass and vitrified micro bead. However, compared with level A insulation material, the more welcomed by the market is the organic insulation material. This is characterized as thermal insulation material, which is divided into three levels: level B1 is flame retardant, level B2 is flammable and level B3 is flammable. The level B1 nonflammable thermal insulation material is determined according to the fire endurance of the material. And different parts of the material are divided differently! Such as the common EPS / XPS insulation boards through special treatment of adding flame retardant. . Level B2 combustible insulation material is commonly the EPS expanded polystyrene foam insulation board and XPS board, that is, the ordinary plate. This material has low ignition point, and releases large amounts of harmful gases in the combustion process . Level B3 flammable insulation material is commonly the thermal insulation material taking polystyrene foam as the main material. Since this material is highly flammable, it has been out of the external wall thermal insulation materials. As for the civil construction insulation materials, China's current popular building insulation materials in the market are mainly made of three organic foams: EPS (molded polystyrene board), XPS (extruded polystyrene board) and PU (polyurethane).
Q:What's the maximum temperature that the refractory ceramic fiber cloth can endure?
It depends on the composition of the ceramic material. If its composition is alumina and it is used by civilians, its normal use temperature is 1200℃; if its composition is alumina but it is for millitary use, it can endure the highest temperature of 2200℃.
Q:I wanna ask that magnesium oxide is refractory?
Yes, Magnesia belongs to ionic crystals, the oin of magnesium has two charge, oxygen and magnesium ions are relatively small radius, these two factors make a lot of magnesium oxide lattice energy, high melting point is up to 2800 degrees Celsius. Because the magnesium oxide is stable and not react with water, it is widely used as a refractory material.
Q:What's the difference between refractory metal raceway and fireproof raceway?
Refractory metal is used to lay and control cables, while trunking is used to lay wires and communication cables; refractory metal is bigger (200*100-600*200), while trunking is smaller; refractory metal has bigger turning radius, while trunking mostly turns a right angle; refractory metal has larger span, while trunking has smaller span; their fixation and installation ways are also different.
Q:What refractories are used in various parts of the blast furnace.
Blast furnace from top to bottom has the throat, hearth staves, waist, bosh, hearth and furnace bottom. the specific structure is as follows: The throat is the first to be affected by the impact and abrasion, generally use high-density alumina bricks. the upper and central portion of temperature furnace is only 400 ~ 800 ℃, the area with high alumina bricks and silicate bricks. The lower part of furnace is subject to erosion and dust erosion alkali metal vapor due to high temperatures, it is required in such case to use high quality clay brick,high alumina brick,carborundum brick,corundum brick that is slag resistance and alkali resistance, temperature resustant and wearproof. Furnace bosh temperature reached 1400 ~ 1600 ℃, serverly eroded by slag,vapor, flush. so we use carborundum brick and reaction-bonded silicon carbide brick. Bosh temperature reaching1600 ~ 1650 ℃, using alumina brick, corundum brick or silicon carbide brick. the temperature of Hearth near the upper portion of the outlet zone at 1700 ~ 2000 ℃, use of silicate bricks and corundum castable graphite filler, silicon carbide bricks. In 1450 Silly twitch bottom temperature sealing die of hunger slander bet phoenix astringent preserved Grade ~ 1500 ℃, use of graphite bricks and microporous carbon bricks, now use more corundum brick, corundum mullite brick and synthetic mullite brick. x26lt;P class x3d "share-btn"x26gt;
Q:what's the varieties of fire-proof sealing material?
ATD-AB, organic fire-proof caulking, fire retardant bag, fire retardant net, fire retardant ring, fire barrier wrap, fireproofing sealing strip, flexibility fireproofing coiled material, fireproof glue, etc., fireproofing sealing materials currently on the market can be divided into two types, one is the traditional type: flexible organic caulking, WXY-II, fire retardant bag, fire bulkhead, cable refractory coating; there are some new materials used in large-scale projects: fireproofing coating board system (fireproofing coating board, intumescent fireproof sealing tape, elastic fireproof sealant, Waterborne Fire-retardant Coating), fire retardant module system (fire retardant module, sealing gum, cable refractory coating), fireproofing plaster system (fireproofing plaster, sealing gum, cable refractory coating).
Q:What kind of flexible fireproof material is really good?
The best one is grade A fireproof material. A-class fire flexible material adopts clay, stone, sand, cement blocks and other inorganic powder and modifier and product density is 2327 kg/m3. Upon examination, the combustion performance of this product is in accordance with the grade A specified requirements and additional classification meets A s2, d0, t0 level requirements. According to GB 8624-2006, the combustion performance of product reach A2 - s2, d0, t0 level.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range